Enhanced field emission from ZnO nanorods via thermal annealing in oxygen

Applied Physics Letters

Volumn 88, Issue 3, 2006, Pages 1-3

  Zhao, Q ^a   Xu, X Y ^a   Song, X F ^a   Zhang, X Z ^a   Yu, D P ^a   Li, C P ^b   Guo, L ^b  

^a PEKING UNIVERSITY   (China)

^b BEIHANG UNIVERSITY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

AMMONIA; ANNEALING; CRYSTALS; ELECTRON SOURCES; HEAT TREATMENT; NANOSTRUCTURED MATERIALS; OXYGEN; PHOTOLUMINESCENCE; RAMAN SPECTROSCOPY;

CRYSTAL QUALITY; OXYGEN VACANCY; POSTTHERMAL ANNEALING; ZNO NANORODS;

FIELD EMISSION DISPLAYS;

EID: 31144432165     PISSN: 00036951     EISSN: None     Source Type: Journal    
DOI: 10.1063/1.2166483     Document Type: Article

References (20)

1. Y. Li, G. W. Meng, L. D. Zhang, and F. Fillipp, Appl. Phys. Lett. 76, 2011 (2000).
2. Y. C. Kong, D. P. Yu, B. Zhang, W. Fang, and S. Q. Feng, Appl. Phys. Lett. 78, 407 (2001).
3. M. H. Huang, Y. Y. Wu, H. Feick, N. Tran, E. Weber, and P. D. Yang, Adv. Mater. (Weinheim, Ger.) 13, 113 (2001).
4. M. Law, X. F. Zhang, R. Yu, T. Kuykendall, and P. D. Yang, Small 1, 858 (2005).
5. N. S. Xu and S. Ejaz Huq, Mater. Sci. Eng., R. 48, 47 (2005).
6. C. M. Tan, J. J. Jia, and W. B. Yu, Appl. Phys. Lett. 86, 263104 (2005).
7. M. H. Huang, S. Mao, H. Feick, H. Q. Yan, Y. Y. Wu, H. Kind, E. Weber, R. Russo, and P. D. Yang, Science 292, 1897 (2001).
8. Y. W. Zhu, H. Z. Zhang, X. C. Sun, S. Q. Feng, J. Xu, Q. Zhao, B. Xiang, R. M. Wang, and D. P. Yu, Appl. Phys. Lett. 83, 144 (2003).
9. H. Z. Zhang, R. M. Wang, and Y. W. Zhu, J. Appl. Phys. 96, 624 (2004).
10. Q. Zhao, H. Z. Zhang, Y. W. Zhu, S. Q. Feng, X. C. Sun, J. Xu, and D. P. Yu, Appl. Phys. Lett. 86, 203115 (2005).
11. S. Bhattacharyya, A. Rastogi, S. V. Bhat, K. S. R. K. Rao, A. V. Subramanyam, and D. Kanjilal, Solid State Commun. 105, 543 (1998).
12. X.-Z. Ding, D.-S. Mao, B. K. Tay, S. P. Lau, J. R. Shi, Y. J. Li, Z. Sun, X. Shi, H. S. Tan, F.-M. Zhang, and X.-H. Liu, J. Appl. Phys. 88, 5087 (2000).
13. R. H. Fowler and L. W. Nordheim, Proc. R. Soc. London, Ser. A 119, 173 (1928).
14. K. Vanheusden, W. L. Warren, C. H. Seager, D. R. Tallant, J. A. Voigt, and B. E. Gnade, J. Appl. Phys. 79, 7983 (1996).
15. Y. J. Xing, Z. H. Xi, Z. Q. Xue, X. D. Zhang, J. H. Song, R. M. Wang, J. Xu, Y. Song, S. L. Zhang, and D. P. Yu, Appl. Phys. Lett. 83, 1689 (2003).
16. J. D. Ye, S. L. Gu, S. M. Zhu, F. Qin, S. M. Liu, W. Liu, X. Zhou, L. Q. Hu, R. Zhang, Y. Shi, and Y. D. Zheng, J. Appl. Phys. 96, 5308 (2004).
17. Y. F. Lu, H. Q. Ni, Z. H. Mai, and Z. M. Ren, J. Appl. Phys. 88, 498 (2000).
18. W. Zhu, G. P. Kochanski, S. Jin, and L. Seibles, J. Appl. Phys. 78, 2707 (1995).
19. H. Y. Yu, Y. C. Liu, R. Mu, C. L. Shao, Y. M. Lu, D. Z. Shen, and X. W. Fan, Appl. Phys. Lett. 86, 123107 (2005).
20. Z. Y. Fan, D. W. Wang, P.-C. Chang, W.-Y. Tseng, and J. G. Lu, Appl. Phys. Lett. 85, 5923 (2004).