Synthesis of Polymer Dielectric Layers for Organic Thin Film Transistors via Surface-Initiated Ring-Opening Metathesis Polymerization

Journal of the American Chemical Society

Volumn 126, Issue 13, 2004, Pages 4062-4063

  Rutenberg, Isaac M ^a   Scherman, Oren A ^a   Grubbs, Robert H ^a   Jiang, Weirong ^b   Garfunkel, Eric ^b   Bao, Zhenan ^c,d  

^a California Institute of Technology   (United States)

^b RUTGERS UNIVERSITY   (United States)

^c LUCENT TECHNOLOGIES   (United States)

^d Stanford University   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ARTICLE; CHEMICAL COMPOSITION; DIELECTRIC CONSTANT; ELECTRIC POTENTIAL; FILM; REACTION ANALYSIS; RING OPENING METATHESIS POLYMERIZATION; SEMICONDUCTOR; SURFACE PROPERTY; SYNTHESIS; THICKNESS;

EID: 1842555252     PISSN: 00027863     EISSN: None     Source Type: Journal    
DOI: 10.1021/ja035773c     Document Type: Article

References (19)

1. (a) Rogers, J. A.; Bao, Z. J. Polym. Sci., Polym. Chem. 2002, 40, 3327-3334.
2. (b) Sheraw, C. D.; Zhou, L.; Huang, J. R.; Gundlach, D. J.; Jackson, T. N.; Kane, M. G.; Hill, I. G.; Hammond, M. S.; Campi, J.; Greening, B. K.; Francl, J.; West, J. Appl. Phys. Lett. 2002, 80, 1088-1090.
3. (c) Huitema, H. E. A.; Gelinck, G. H.; van der Putten, J. B. P. H.; Kuijk, K. E.; Hart, C. M.; Cantatore, E.; Herwig, P. T.; van Breemen, A. J. J. M.; de Leeuw, D. M. Nature 2001, 414, 599.
4. (a) Gelinck, G. H.; Geuns, T. C. T.; de Leeuw, D. M. Appl. Phys. Lett. 2000, 77, 1487-1489.
5. (b) Crone, B. K.; Dodabalapur, A.; Sarpeshkar, R.; Filas, R. W.; Lin, Y. Y.; Bao, Z.; O'Neill, J. H.; Li, W.; Katz, H. E. J. Appl. Phys. 2001, 89, 5125-5132.
6. Performance as measured by mobility and on/off ratio. See Katz, H. E.; Bao, Z. J. Phys. Chem. B 2000, 104, 671-678.
7. (a) Halik, M.; Klauk, H.; Zschieschang, U.; Schmid, G.; Radlik, W.; Weber, W. Adv. Mater. 2002, 14, 1717-1721.
8. (b) Bao, Z. N.; Feng, Y.; Dodabalapur, A.; Raju, V. R.; Lovinger, A. J. Chem. Mater. 1997, 9, 1299-1301.
9. (c) Kawase, T.; Sirringhaus, H.; Friend, R. H.; Shimoda, T. Adv. Mater. 2001, 13, 1601-1604.
10. (a) Weck, M.; Jackiw, J. J.; Rossi, R. R.; Weiss, P. S.; Grubbs, R. H. J. Am. Chem. Soc. 1999, 121, 4088-4089.
11. (b) Juang, A.; Scherman, O. A.; Grubbs, R. H.; Lewis, N. S. Langmuir 2001, 17, 1321-1323.
12. (c) Kim, N. Y.; Jeon, N. L.; Choi, I. S.; Takami, S.; Harada, Y.; Finnie, K. R.; Girolami, G. S.; Nuzzo, R. G.; Whitesides, G. M.; Laibinis, P. E. Macromolecules 2000, 33, 2793-2795.
13. Watson, K. J.; Zhu, J.; Nguyen, S. T.; Mirkin, C. A. J. Am. Chem. Soc. 1999, 121, 462-463.
14. Bielawski, C. W.; Grubbs, R. H. Angew. Chem., Int. Ed. 2000, 39, 2903-2906.
15. In general, films produced with linker 4 were thicker than those produced with linker 5. Catalyst attachment is likely more efficient with 4; the reasons for this are currently under investigation.
16. Choi, T.-L.; Grubbs, R. H. Angew. Chem., Int. Ed. 2003, 42, 1743-1746.
17. Bao, Z. N.; Rogers, J. A.; Katz, H. E. J. Mater. Chem. 1999, 9, 1895-1904.
18. Loo, Y.-L.; Someya, T.; Baldwin, K. W.; Bao, Z.; Ho, P.; Dodabalapur, A. ; Katz, H. E.; Rogers, J. A. Proc. Natl. Acad. Sci. U.S.A. 2002, 99, 10252-10256.
19. Increased grain size was observed when pentacene was deposited over SI-ROMP polymer lavers that had been annealed.