Synthesis of uniform Cu2S nanowires from copper-thiolate polymer precursors by a solventless thermolytic method

Journal of the American Chemical Society

Volumn 126, Issue 50, 2004, Pages 16334-16335

  Chen, Ling ^a   Chen, Yu Biao ^a,b   Wu, Li Ming ^a  

^a FUJIAN INSTITUTE OF RESEARCH ON THE STRUCTURE OF MATTER   (China)

^b UNIVERSITY OF CHINESE ACADEMY OF SCIENCES   (China)

Author keywords

[No Author keywords available]

Indexed keywords

COPPER; COPPER SULFATE; POLYMER; THIOL DERIVATIVE;

ARTICLE; CHEMICAL PROCEDURES; CHEMICAL REACTION; DESORPTION; POLYMERIZATION; SYNTHESIS; TEMPERATURE; TRANSMISSION ELECTRON MICROSCOPY;

EID: 11444256581     PISSN: 00027863     EISSN: None     Source Type: Journal    
DOI: 10.1021/ja045074f     Document Type: Article

References (31)

1. Xia, Y.; Yang, P.; Sun, Y.; Wu, Y.; Mayers, B.; Gates, B.; Yin, Y.; Kim, F.; Yan, H. Adv. Mater. 2003, 15, 353-389.
2. (a) Lieber, C. M. Sci. Am. 2001, 285, 58-64.
3. (b) Hu, J.; Odom, T. W.; Lieber, C. M. Acc. Chem. Res. 1999, 32, 435-445.
4. Kovtyukhova, N. I.; Mallouk, T. E. Chem.-Eur. J. 2002, 8, 4355-4363.
5. Voit, J. Rep. Prog. Phys. 1995, 58, 977-1116.
6. (a) Flood, A.; Ramirez, R.; Deng, W.; Muller, R.; Goddard, W.; Stoddart, J. F. Aust. J. Chem. 2004, 57, 301-302.
7. (b) Fasol, G. Science 1998, 280, 545-546.
8. (a) Hyun, J.; Kim, J.; Craig, S. L.; Chilkoti, A. J. Am. Chem. Soc. 2004, 126, 4770-4771.
9. (b) Cerrina, F.; Marrian, C. MRS Bull. 1996, 21, 56-62.
10. (c) Madou, M. Fundamentals of Microfabrication; CRC Press: Boca Raton, FL, 1997.
11. (d) Hulteen, J. C.; Martin, C. R. J. Mater. Chem. 1997, 7, 1075-1087.
12. (e) Kim, F.; Song, J.; Yang, P. J. Am. Chem. Soc. 2002, 124, 14316-14317.
13. (f) Bates, F. S.; Fredrickson, G. H. Phys. Today 1999, 52, 32-38.
14. (g) Pan, Z. W.; Dai, Z. R.; Wang, L. Z. Science 2001, 291, 1947-1949.
15. (h) Morales, A. M.; Lieber, C. M. Science 1998, 279, 208-211.
16. (i) Trentler, T. J.; Hichman, K. M.; Geol, S. C.; Viano, A. M.; Gibbons, P. C.; Buhro, W. E. Science 1995, 270, 1791-1794.
17. (j) Cheon, J.; Kang, N. J.; Lee, S. M.; Lee, J. H.; Yoon, J. H.; Oh, S. J. J. Am. Chem. Soc. 2004, 126, 1950-1951.
18. (k) Yan, P.; Xie, Y.; Wang, W.; Liu, F.; Qian, Y. J. Am. Chem. Soc. 1999, 121, 4062-4063.
19. (a) Larsen, T. H.; Sigman, M.; Ghezelbash, A.; Doty, R. C.; Korgel, B. A. J. Am. Chem. Soc. 2003, 125, 5638-5639.
20. (b) Sigman, M. B.; Ghezelbash, A.; Hanrath, T.; Saunders, A. E.; Lee, F.; Korgel, B. A. J. Am. Chem. Soc. 2003, 125, 16050-16057.
21. Ghezelbash, A.; Sigman, M. B.; Korgel, B. A. Nano Lett. 2004, 4, 537-542.
22. (a) Dance, I. G. Polyhedron 1986, 5, 1037-1104.
23. (b) Henkel, G.; Krebs, B. Chem. Rev. 2004, 104, 801-824.
24. Neville, R. C. Solar Energy Conversion: The Solar Cell, 2nd ed.; Elsevier: Amsterdam, 1995.
25. (a) Wang, S. H.; Yang, S. H. Chem. Phys. Lett. 2000, 322, 567-571.
26. (b) Wang, S. H.; Guo, L.; Wen, X. G.; Yang, S. H.; Zhao, J.; Liu, J.; Wu, Z. H. Mater. Chem. Phys. 2002, 75, 32-38.
27. The viscosity of precursor is measured with the aid of an NDJ-9S viscometer (ShangPing) at room temperature with a rotor (diameter = 19 mm) speed at 60 r/min. The viscosity of each sample was read after the rotor had been in the sample for 10 min.
28. Dance, I. G.; Fisher, K. J.; Banda, R. M. H.; Scudder, M. L. Inorg. Chem. 1991, 30, 183-187.
29. Buerger, M. J.; Wuensch, B. J. Science 1963, 141, 276-277.
30. Elemental analysis performed by EDX of nanocrystals on a Mo grid with the aid of a JEOL 2010F TEM equipped with an Oxford INCA spectrometer showed that the Cu:S atomic ratio is 1.8:1.
31. The thermal desorption measurements were performed on TDS Gerstel (thermodesorption system), Agilent 6890N, GC, and Agilent 5973N MS.