Cubic AgPbmSbTe2+m: Bulk Thermoelectric Materials with High Figure of Merit

Author keywords

[No Author keywords available]

Indexed keywords

DOPING (ADDITIVES); ELECTRIC POWER GENERATION; ENERGY UTILIZATION; HIGH TEMPERATURE EFFECTS; SEMICONDUCTOR MATERIALS; THERMOELECTRICITY;

EID: 0842331448     PISSN: 00368075     EISSN: None     Source Type: Journal    
DOI: 10.1126/science.1092963     Document Type: Article
Times cited : (2928)

References (26)
  • 1
    • 0842309149 scopus 로고    scopus 로고
    • note
    • 2) is called the power factor.
  • 15
    • 0037183949 scopus 로고    scopus 로고
    • T. C. Harman et al., Science 297, 2229 (2002).
    • (2002) Science , vol.297 , pp. 2229
    • Harman, T.C.1
  • 16
    • 0034635446 scopus 로고    scopus 로고
    • D. Y. Chung et al., Science 287, 1024 (2000).
    • (2000) Science , vol.287 , pp. 1024
    • Chung, D.Y.1
  • 17
    • 0842287545 scopus 로고    scopus 로고
    • note
    • Materials and methods are available as supporting material on Science Online.
  • 19
    • 0842309147 scopus 로고    scopus 로고
    • note
    • These data were obtained with the flash diffusivity-specific heat method at the Thermophysical Properties Research Laboratory, West Lafayette, IN (www. tprl.com/). The sample configuration was in the form of a flat disk of ∼14-mm diameter and 2.5-mm thickness.
  • 20
    • 0842309148 scopus 로고    scopus 로고
    • note
    • 2N·s and similar to those reported for the MBE-grown thin-film superlattice PbSe/PbTe systems (15).
  • 21
    • 0842309146 scopus 로고    scopus 로고
    • in preparation
    • D. Bilc et al., in preparation.
    • Bilc, D.1
  • 22
    • 0842287547 scopus 로고    scopus 로고
    • note
    • hot)] where ΔT is the temperature difference across the device. The first fraction in this expression is the Carnot efficiency. ZT is defined in (1).
  • 24
  • 26
    • 0842265878 scopus 로고    scopus 로고
    • note
    • Financial support from the Office of Naval Research and Defense Advanced Research Projects Agency is gratefully acknowledged.


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.