Foreign-object damage and high-cycle fatigue: Role of microstructure in Ti-6Al-4V

International Journal of Fatigue

Volumn 23, Issue SUPPL. 1, 2001, Pages 413-421

  Peters, J O ^a   Ritchie, R O ^a  

^a Lawrence Berkeley National Laboratory   (United States)

Author keywords

Fatigue crack growth threshold; Foreign object damage; High cycle fatigue; Small cracks; Ti 6Al 4V

Indexed keywords

LOADING; MICROCRACKS; MICROSTRUCTURE; STEEL STRUCTURES; STRENGTH OF MATERIALS; STRESS CONCENTRATION; TITANIUM;

FOREIGN OBJECT DAMAGE (FOD); HIGH-CYCLE FATIGUE (HCF);

FATIGUE OF MATERIALS;

EID: 0035210409     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/s0142-1123(01)00168-2     Document Type: Article

References (26)

1. High cycle fatigue in aircraft gas turbines - An industry perspective
2. On the use of the Goodman diagram for high cycle fatigue design
3. An assessment of the role of near-threshold crack growth in high cycle fatigue life prediction of aerospace titanium alloys under turbine engine spectra
4. Small cracks and high-cycle fatigue
5. High-cycle fatigue of Ti-6Al-4V
6. Role of foreign-object damage on thresholds for high-cycle fatigue in Ti-6Al-4V
7. Influence of foreign-object damage on crack initiation and early crack growth during high-cycle fatigue of Ti-6Al-4V
8. Impact damage on titanium leading edges from small hard objects
9. High cycle fatigue of turbine blade materials
10. Small fatigue cracks: Mechanics, mechanisms and engineering applications
11. Applicability of fracture mechanics to very small cracks or the cracks in the early stage
12. Summary of the available information on the processing of the Ti-6Al-4V HCF/LCF program plates
13. Microcrack propagation in Ti-6Al-4V alloys
14. Stress intensity factor for small notch-emanating cracks
15. Stress concentration caused by the presence of a spherical cavity or a spherical-surfaced hollow
16. An empirical stress-intensity factor equation for the surface crack
17. The residual stress state due to a spherical hard-body impact
18. Foreign object damage and fatigue crack threshold: Cracking outside shallow indents
19. Mixed-mode high-cycle fatigue thresholds in Ti-6Al-4V: A comparison of large and small crack behavior
20. Propagation of short fatigue cracks
21. Influence of shot peening parameters on the surface layer properties and the fatigue life of Ti-6Al-4V
22. Influence of a shot peening treatment on the fatigue limit of Ti-6Al-4V
23. Prediction of non propagating cracks