Influence of foreign-object damage on crack initiation and early crack growth during high-cycle fatigue of Ti-6Al-4V

Engineering Fracture Mechanics

Volumn 67, Issue 3, 2000, Pages 193-207

  Peters, J O ^a   Ritchie, R O ^a  

^a Lawrence Berkeley National Laboratory   (United States)

Author keywords

Fatigue crack growth threshold; Foreign object damage; High cycle fatigue; Small cracks; Ti 6Al 4V

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; FATIGUE OF MATERIALS; FRACTURE MECHANICS; METALLOGRAPHIC MICROSTRUCTURE; STRESS ANALYSIS; STRESS CONCENTRATION;

FOREIGN-OBJECT DAMAGE (FOD); HIGH-CYCLE FATIGUE (HCF);

TITANIUM ALLOYS;

BLADE; CRACKING; FATIGUE; TURBINE; WEAR;

EID: 0034307916     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(00)00045-X     Document Type: Article

References (21)

1. High cycle fatigue in aircraft gas turbines - an industry perspective
2. On the use of the Goodman diagram for high cycle fatigue design
3. An assessment of the role of near-threshold crack growth in high cycle fatigue life prediction of aeroscpace titanium alloys under turbine engine spectra
4. Small cracks and high-cycle fatigue
5. High-cycle fatigue of Ti-6Al-4V
6. Erosion, corrosion and foreign object damage effects in gas turbines
7. Impact damage on titanium leading edges from small hard objects
8. Role of foreign object damage on thresholds for high-cycle fatigue in Ti-6Al-4V
9. Investigation of the effects of shed-rate, initial K(max), and geometric constraint on K(th) in Ti-6Al-4V at room temperature
10. Stress intensity factor for small notch-emanating cracks
11. Stress concentration caused by the presence of a spherical cavity or a spherical-surfaced hollow
12. Foreign object damage and fatigue cracking: On the shallow indentation
13. Measurement of residual stresses in impact-damaged Ti-6Al-4V
14. Microcrack propagation in Ti-6Al-4V alloys
15. Validation of the step test method for generating Haigh diagrams for Ti-6Al-4V
16. Thresholds for high-cycle fatigue in a turbine engine Ti-6Al-4V alloy
17. Small fatigue cracks: A statement of the problem and potential solutions
18. Applicability of fracture mechanics to very small cracks or the cracks in the early stage
19. Prediction of non propagating cracks