The residual stress state due to a spherical hard-body impact

Mechanics of Materials

Volumn 33, Issue 8, 2001, Pages 441-454

  Boyce, B L ^a   Chen, X ^b   Hutchinson, J W ^b   Ritchie, R O ^a  

^a UNIVERSITY OF CALIFORNIA   (United States)

^b HARVARD UNIVERSITY   (United States)

Author keywords

Fatigue; Foreign object damage; Impact; Residual stress; Ti 6Al 4V; Titanium; X ray diffraction

Indexed keywords

FATIGUE OF MATERIALS; IMPACT TESTING; MATHEMATICAL MODELS; NUMERICAL ANALYSIS; RESIDUAL STRESSES; STRAIN RATE; STRESS ANALYSIS; SYNCHROTRON RADIATION; X RAY DIFFRACTION ANALYSIS;

HARD-BODY IMPACT;

TITANIUM ALLOYS;

EID: 0035424236     PISSN: 01676636     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0167-6636(01)00064-3     Document Type: Article

References (27)

1. A rudimentary analysis of improving fatigue life of metals by shot peening
2. Understanding and preventing failures and their causes in gas turbine engines
3. Foreign object debris and damage prevention
4. Foreign object damage and fatigue crack threshold: Cracking outside shallow indents
5. High cycle fatigue in gas turbines - An industry perspective
6. Navy foreign object damage and its impact on future gas turbine low pressure compression system
7. An analysis of the low temperature, low and high strain-rate deformation of Ti-6Al-4V
8. Mechanism of creation of compressive residual stress by shot peening
9. An assessment of the role of near-threshold crack growth in high-cycle-fatigue life prediction of aerospace titanium alloys under turbine engine spectra
10. Mechanical approach to the residual stress field induced by shot peening
11. Role of foreign-object damage on thresholds for high-cycle fatigue in Ti-6Al-4V
12. Influence of foreign-object damage on crack initiation and early crack growth during high-cycle fatigue of Ti-6Al-4V
13. Role of residual stresses on high-cycle fatigue of impact-damaged Ti-6Al-4V: Surface vs. subsurface crack initiation
14. A method of determining the elastic properties of alloys in selected crystallographic directions for X-ray diffraction residual stress measurement
15. Influence of foreign object damage (FOD) on the fatigue life of simulated Ti-6Al-4V airfoils
16. Decay of residual stress at indentation cracks during slow crack growth in soda-lime glass
17. Erosion, corrosion and foreign object damage in gas turbines
18. The indentation of hard metals: The role of residual stresses
19. A new method for estimating residual stress by instrumented sharp indentation
20. Shot peening and residual stress
21. Elastic-plastic analysis of indentation damages in copper: Work hardening and residual stress
22. Residual stress fields at the surface of sharp pyramid indentations