Volumn 21, Issue 3, 2004, Pages 175-185

Characterization of the breakaway al content in alumina-forming alloys

Author keywords

Alumina forming alloys; Residual Al contents

Indexed keywords

DATA REDUCTION; DEGRADATION; DIFFUSION; FAILURE ANALYSIS; IRON ALLOYS; MICROANALYSIS; NICKEL ALLOYS; OXIDATION; PERFORMANCE; THERMODYNAMICS;

EID: 9244248659     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2004.021     Document Type: Article
Times cited : (48)

References (34)
  • 1
    • 0020876894 scopus 로고
    • Cyclic oxidation of superalloys
    • R. A. Rapp, ed., NACH, Houston, TX
    • Lowell, C. E., Smialek, J. L. and Barrett, C. A., Cyclic oxidation of superalloys. In: High-Temperature Corrosion, pp. 219-226, R. A. Rapp, ed., NACH, Houston, TX (1983).
    • (1983) High-temperature Corrosion , pp. 219-226
    • Lowell, C.E.1    Smialek, J.L.2    Barrett, C.A.3
  • 2
    • 0343476492 scopus 로고
    • Oxidation between 1000°C and 1600°C and limiting criteria for the use of Zr-doped β-NiAl and β/γ' alloys
    • V. Srinivasan and K. Vedula, eds, TMS, Warrendale, PA
    • Doychak, J., Barrett, C. A. and Smialek, J. L. Oxidation between 1000°C and 1600°C and limiting criteria for the use of Zr-doped β-NiAl and β/γ' alloys. In: Corrosion & Particle Erosion at High Temperature, pp. 487-514, V. Srinivasan and K. Vedula, eds, TMS, Warrendale, PA (1989).
    • (1989) Corrosion & Particle Erosion at High Temperature , pp. 487-514
    • Doychak, J.1    Barrett, C.A.2    Smialek, J.L.3
  • 4
    • 0026862756 scopus 로고
    • Diffusional transport and predicting oxidative failure during cyclic oxidation of β-NiAl alloys
    • Nesbitt, J. A., Vinarcik, E. J., Barrett, C. A. and Doychak, J., Diffusional transport and predicting oxidative failure during cyclic oxidation of β-NiAl alloys. Mater. Sci. Eng., A153, 561-566 (1992).
    • (1992) Mater. Sci. Eng. , vol.A153 , pp. 561-566
    • Nesbitt, J.A.1    Vinarcik, E.J.2    Barrett, C.A.3    Doychak, J.4
  • 5
    • 0027274581 scopus 로고
    • Prediction of the high temperature oxidative life of intermetallics
    • Symp. Proc., I. Baker, R. Darolia, J. D. Whittenberger and M. H. Yoo eds. (MRS, Pittsburgh, PA)
    • Nesbitt, J. A. and Lowell, C. E., Prediction of the high temperature oxidative life of intermetallics. In: High Temperature Ordered Intermetallics V, Symp. Proc. v.288, I. Baker, R. Darolia, J. D. Whittenberger and M. H. Yoo eds. (MRS, Pittsburgh, PA, 1993) pp. 107-118.
    • (1993) High Temperature Ordered Intermetallics V , vol.288 , pp. 107-118
    • Nesbitt, J.A.1    Lowell, C.E.2
  • 6
    • 0002417864 scopus 로고    scopus 로고
    • Cyclic oxidation testing and modelling: A NASA Lewis perspective
    • M. Schütze and W. J. Quadakkers, eds, Institute of Materials, London, UK
    • Smialek, J. L., Nesbitt, J. A., Barrett, C. A. and Lowell, C. E., Cyclic oxidation testing and modelling: A NASA Lewis perspective. In: Cyclic Oxidation of High Temperature Materials, pp. 148-68, M. Schütze and W. J. Quadakkers, eds, Institute of Materials, London, UK (1999).
    • (1999) Cyclic Oxidation of High Temperature Materials , pp. 148-168
    • Smialek, J.L.1    Nesbitt, J.A.2    Barrett, C.A.3    Lowell, C.E.4
  • 7
    • 0016072228 scopus 로고
    • Effects of diffusion on aluminum depletion and degradation of NiAl coatings
    • Smialek, J. L. and Lowell, C. E., Effects of diffusion on aluminum depletion and degradation of NiAl coatings. J. Electrochem. Soc., 121, 800-805 (1974).
    • (1974) J. Electrochem. Soc. , vol.121 , pp. 800-805
    • Smialek, J.L.1    Lowell, C.E.2
  • 8
    • 84974883959 scopus 로고
    • Oxidation induced lifetime limits of thin walled, iron based, alumina forming, oxide dispersion strengthened alloy components
    • Quadakkers, W. J. and Bennett, M. J., Oxidation induced lifetime limits of thin walled, iron based, alumina forming, oxide dispersion strengthened alloy components. Mater. Sci. Tech., 10, 126-31 (1994).
    • (1994) Mater. Sci. Tech. , vol.10 , pp. 126-131
    • Quadakkers, W.J.1    Bennett, M.J.2
  • 9
    • 0028410084 scopus 로고
    • The prediction of breakaway oxidation for alumina forming ODS alloys using oxidation diagrams
    • Quadakkers, W. J. and Bongartz, K., The prediction of breakaway oxidation for alumina forming ODS alloys using oxidation diagrams. Werkst. Korros., 45, 232-241 (1994).
    • (1994) Werkst. Korros. , vol.45 , pp. 232-241
    • Quadakkers, W.J.1    Bongartz, K.2
  • 10
    • 0042960806 scopus 로고
    • The prediction of oxidation limited life of thin walled ODS heat exchangers for high temperature applications
    • D. Coutsouradis, et al., eds Kluwer Academic Publishers, Dordrecht, Netherlands
    • Quadakkers, W. J., Bongartz, K. and Schubert, F., The prediction of oxidation limited life of thin walled ODS heat exchangers for high temperature applications. In: Materials for Advanced Power Engineering II, pp.1533-1542, D. Coutsouradis, et al., eds Kluwer Academic Publishers, Dordrecht, Netherlands (1994).
    • (1994) Materials for Advanced Power Engineering II , pp. 1533-1542
    • Quadakkers, W.J.1    Bongartz, K.2    Schubert, F.3
  • 12
    • 0032650696 scopus 로고    scopus 로고
    • Long-term oxidation performance of ingot-produced Fe3Al alloys
    • Pint, B. A., Tortorelli, P. F. and Wright, I .G., Long-term oxidation performance of ingot-produced Fe3Al alloys. Mater. High Temp., 16, 1-13 (1999).
    • (1999) Mater. High Temp. , vol.16 , pp. 1-13
    • Pint, B.A.1    Tortorelli, P.F.2    Wright, I.G.3
  • 13
    • 0012928117 scopus 로고    scopus 로고
    • Life-time extension of alumina forming FeCrAl-RE alloys: Influence of alloy thickness
    • Wilber, J. P., Bennett, M. J. and Nicholls, J. R., Life-time extension of alumina forming FeCrAl-RE alloys: Influence of alloy thickness. Mater. High Temp., 17, 125-132 (2000).
    • (2000) Mater. High Temp. , vol.17 , pp. 125-132
    • Wilber, J.P.1    Bennett, M.J.2    Nicholls, J.R.3
  • 14
    • 0034174050 scopus 로고    scopus 로고
    • Factors governing breakaway oxidation of FeCrAl-based alloys
    • Gurrappa, I., Weinbruch, S., Naumenko, D. and Quadakkers, W. J., Factors governing breakaway oxidation of FeCrAl-based alloys. Mater. Corr., 51, 224-235 (2000).
    • (2000) Mater. Corr. , vol.51 , pp. 224-235
    • Gurrappa, I.1    Weinbruch, S.2    Naumenko, D.3    Quadakkers, W.J.4
  • 16
    • 0013016043 scopus 로고    scopus 로고
    • Experimental results and modeling related to oxidation lifetimes
    • M. Schütze, W. J. Quadakkers and J. R. Nicholls, eds, Maney, London
    • Wright, I. G., Pint, B. A., Hall, L. M. and Tortorelli, P. F. Experimental results and modeling related to oxidation lifetimes. In: Lifetime Modelling of High Temperature Corrosion Processes, pp.339-358, M. Schütze, W. J. Quadakkers and J. R. Nicholls, eds, Maney, London (2001).
    • (2001) Lifetime Modelling of High Temperature Corrosion Processes , pp. 339-358
    • Wright, I.G.1    Pint, B.A.2    Hall, L.M.3    Tortorelli, P.F.4
  • 17
    • 0012933217 scopus 로고    scopus 로고
    • Measures to improve the oxidation limited service life of Fe-Based ODS alloys
    • S. B. Newcomb and J. A. Little, eds, Institute of Metals, London, U.K.
    • Quadakkers, W. J., Clemens, D. and Bennett, M. J., Measures to improve the oxidation limited service life of Fe-Based ODS alloys. In: Microscopy of Oxidation 3, pp.195-206, S. B. Newcomb and J. A. Little, eds, Institute of Metals, London, U.K., (1997).
    • (1997) Microscopy of Oxidation , vol.3 , pp. 195-206
    • Quadakkers, W.J.1    Clemens, D.2    Bennett, M.J.3
  • 18
    • 0033076172 scopus 로고    scopus 로고
    • The effect of an oxide dispersion on the critical Al content in Fe-Al Alloys
    • Pint, B. A., Leibowitz, J. and DeVan, J. H., The effect of an oxide dispersion on the critical Al content in Fe-Al Alloys. Oxid. Met., 51, 183-99 (1999).
    • (1999) Oxid. Met. , vol.51 , pp. 183-199
    • Pint, B.A.1    Leibowitz, J.2    DeVan, J.H.3
  • 19
    • 0001340674 scopus 로고    scopus 로고
    • The application of a wedge-shaped sample technique for the study of breakaway oxidation in Fe-20%Cr-5Al base alloys
    • Tatlock, G. and Al-Badairy, H., The application of a wedge-shaped sample technique for the study of breakaway oxidation in Fe-20%Cr-5Al base alloys. Oxid. Met., 53, 157-170 (2000).
    • (2000) Oxid. Met. , vol.53 , pp. 157-170
    • Tatlock, G.1    Al-Badairy, H.2
  • 20
    • 0012932092 scopus 로고    scopus 로고
    • Effect of cycle frequency on high temperature oxidation behavior of alumina-forming alloys
    • Pint, B. A., Tortorelli, P. F., and Wright, I. G., Effect of cycle frequency on high temperature oxidation behavior of alumina-forming alloys. Oxid. Met., 58, 73-101 (2002).
    • (2002) Oxid. Met. , vol.58 , pp. 73-101
    • Pint, B.A.1    Tortorelli, P.F.2    Wright, I.G.3
  • 21
    • 0242599441 scopus 로고    scopus 로고
    • The oxidation behaviour of iron aluminides at 1300°C
    • S. B. Newcomb and J. A. Little, eds, Institute of Metals, London, U.K.
    • Bennett, M. J., DeVan, J. H. and Tortorelli, P. F., The oxidation behaviour of iron aluminides at 1300°C. In: Microscopy of Oxidation 3, pp.233-45, S. B. Newcomb and J. A. Little, eds, Institute of Metals, London, U.K. (1997).
    • (1997) Microscopy of Oxidation , vol.3 , pp. 233-245
    • Bennett, M.J.1    DeVan, J.H.2    Tortorelli, P.F.3
  • 22
    • 34249758359 scopus 로고
    • The influence of alloying elements on the development and maintenance of protective scales
    • Stott, F. H., Wood, G, C. and Stringer, J. The influence of alloying elements on the development and maintenance of protective scales. Oxid. Met., 44, 113-145 (1995).
    • (1995) Oxid. Met. , vol.44 , pp. 113-145
    • Stott, F.H.1    Wood, G.C.2    Stringer, J.3
  • 23
    • 0023960369 scopus 로고
    • Diffusional transport during the cyclic oxidation of γ + β, Ni-Cr-Al (Y, Zr) alloys
    • Nesbitt, J. A. and Heckel, R. W., Diffusional transport during the cyclic oxidation of γ + β, Ni-Cr-Al (Y, Zr) alloys. Oxid. Met., 29, 75-102 (1988).
    • (1988) Oxid. Met. , vol.29 , pp. 75-102
    • Nesbitt, J.A.1    Heckel, R.W.2
  • 26
    • 0032655518 scopus 로고    scopus 로고
    • Mechanisms of breakaway oxidation and application to a chromia-forming steel
    • Evans, H. E., Donaldson, A. T. and Gilmour, T. C., Mechanisms of breakaway oxidation and application to a chromia-forming steel. Oxid. Met., 52, 379-402 (1999).
    • (1999) Oxid. Met. , vol.52 , pp. 379-402
    • Evans, H.E.1    Donaldson, A.T.2    Gilmour, T.C.3
  • 28
    • 0043246703 scopus 로고    scopus 로고
    • Evaluation of iron-aluminide CVD coatings for high temperature corrosion protection
    • Pint, B. A., Zhang, Y., Tortorelli, P. F., Haynes, J. A. and Wright, I. G., Evaluation of iron-aluminide CVD coatings for high temperature corrosion protection. Mater. High Temp., 18, 185-192 (2001).
    • (2001) Mater. High Temp. , vol.18 , pp. 185-192
    • Pint, B.A.1    Zhang, Y.2    Tortorelli, P.F.3    Haynes, J.A.4    Wright, I.G.5
  • 29
    • 8744247404 scopus 로고    scopus 로고
    • The oxidation behavior of Fe-Al alloys
    • Pint, B. A. The oxidation behavior of Fe-Al alloys. Mater. Sci. Forum, 461-464, 799-806 (2004).
    • (2004) Mater. Sci. Forum , vol.461-464 , pp. 799-806
    • Pint, B.A.1
  • 30
    • 0000418929 scopus 로고
    • The influence of diffusion-related mechanisms in limiting oxide-scale failure
    • Evans, H. E., Nicholls, J. R. and Saunders, S. R. J., The influence of diffusion-related mechanisms in limiting oxide-scale failure. Solid State Phenom., 41, 137-156 (1995).
    • (1995) Solid State Phenom. , vol.41 , pp. 137-156
    • Evans, H.E.1    Nicholls, J.R.2    Saunders, S.R.J.3
  • 31
    • 9244234288 scopus 로고    scopus 로고
    • Materials selection for high temperature (750-1000°C) metallic recuperators for improved efficiency microturbines
    • ASME Paper #2001-GT-445, New Orleans, LA, June 4-7
    • Pint, B. A., Swindeman, R. W., More, K. L. and Tortorelli, P. F., Materials selection for high temperature (750-1000°C) metallic recuperators for improved efficiency microturbines. ASME Paper #2001-GT-445, presented at the International Gas Turbine & Aeroengine Congress & Exhibition, New Orleans, LA, June 4-7, 2001.
    • (2001) International Gas Turbine & Aeroengine Congress & Exhibition
    • Pint, B.A.1    Swindeman, R.W.2    More, K.L.3    Tortorelli, P.F.4
  • 34
    • 0000741578 scopus 로고
    • Influence of an alloy addition of Y on the oxidation behaviour of an austenitic and a ferritic stainless steel in carbon dioxide
    • Antill, J. E. and Peakall, K. A., Influence of an alloy addition of Y on the oxidation behaviour of an austenitic and a ferritic stainless steel in carbon dioxide. J. Iron Steel Inst., 205, 1136-1144 (1967).
    • (1967) J. Iron Steel Inst. , vol.205 , pp. 1136-1144
    • Antill, J.E.1    Peakall, K.A.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.