Life-time extension of alumina forming FeCrAI-RE alloys: Influence of alloy thickness

Materials at High Temperatures

Volumn 17, Issue 1, 2000, Pages 125-132

  Wilber, J R ^a   Bennett, M J ^b   Nicholls, J R ^c  

^a CRANFIELD UNIVERSITY   (United Kingdom)

^b PRAXAIR INC   (United States)

^c Materials Research Consultant   (United Kingdom)

Author keywords

Alloy thickness; Alumina scales; Chemical failure; Fecrai re alloys; Mechanical failure

Indexed keywords

EID: 0012928117     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2000.019     Document Type: Article

References (20)

1. Quadakkers W. J., Clemens D. and Bennett M. J. Measures to improve the oxidation limited service life of Fe based ODS alloys'. In: Nevvcomb S. B. and Little J. A. (eds) Microscopy of Oxidation Vol. 3, pp. 195-206. The Institute of Materials, London, (1997).
2. Pint B. A., Tortorelli P. F. and Wright I. G. The oxidation behaviour of ODS iron aluminides. Verst. Korros. 47, 663-674 (1996).
3. Pint B. A., Tortorelli P. F. and Wright I. G., 'Long-term oxidation performance of ingot-produced Fe3Al Alloys. Mater. High Temp, 16, 1-13(1999).
4. Wilber J. P., Nicholls J. R., and Bennett M. J. Assessment of defects in alumina scales formed on ferritic ODS alloys. In: Newcomb S. B. and Little J. A. (eds) Microscopy of Oxidation Vol. 3, pp. 207-220. The Institute of Materials, London, (1997).
5. Wilber J. P., Bennett M. J. and Nicholls J. R. Failure modes of alumina scales on FeCrAl alloys with reactive element additions. In: Lacomte-Beckers J., Schubert F. and Ennis P. J. (eds) Materials for Advanced Power Engineering 1998. Vol. 5 (Pt II), 835-846. Schriften das Forschungzentrum Julich, Raihe Energietechnik/Energy Technology (1998).
6. Evans H. E. Stress effects in high temperature oxidation of metals. Int. Mater. Rev., 40, 1-40 (1995).
7. Quadakkers W. J. and Bennett M. J. Oxidation induced lifetime limits of thin walled, iron based alumina forming oxide dispersion strengthened alloy components. Mater. Sci. Techno!., 10, 126-131 (1994).
8. Bennett M. J. Recent studies and current problems concerning the high temperature behaviour of alumina forming iron-based alloys, Solid State Phenomena, 41, 235-252 (1995).
9. Tatlock G. and Al-Badairy H. The application of a wedge-shaped sample technique for the study of breakaway oxidation in Fe-20°Cr-5AI base alloys. Oxid Met., 53, No. 1/2, 157-170 (2000).
10. Bennett M. J., De Van J. H. and Tortorelli P. F. The oxidation behaviour of iron aluminide at 1,300°C. In: Newcombe S. B. and Little J. A. (eds) Microscopy of Oxidation Vol. 3, pp. 233-245. The Institute of Materials, London (1997).
11. Material Data Sheet PM2000, Plansee, Austria
12. Material Data Sheet, Kanthai APM, Kanthal, Sweden
13. Material Data Sheet, Kanthal AF, Kanthal, Sweden
14. First Draft Code of Practice for Discontinuous Corrosion Testing in High Temperature gaseous Atmospheres, European Commission Project SMT4-CT95-2001.TESTCORR, ERA Technology (1996).
15. Final Report European Brite/Euram Project How to Improve the Failure Resistance of Alumina Scales on High Temperature Materials (Contract Number BRE2-CT94-0605). April 1997.
16. Hiramatsu N. and Stott F. H. The Effect of Lanthanum on the Scales Developed on Thin Foils of Fe-20°Cr-5Al at Very High Temperatures. Oxid. Met., 51,479-494 (1999).
17. Schütze M. and Quadakkers W. J. (eds) Cyclic Oxidation of High Temperature Materials European Federation of Corrosion Publication No. 27, loM Communication, London (1999).
18. Wright J. K, Williamson R. L., Hou P. V, Cannon R. M., Renusch D., Veal B., Grimsditch M. Finite Element Modelling of the Effect of Interface Anomalies on Thermal Stresses in Alumina Scales. Electrochemical Society Mtg, San Diego, May 3-8, (1998).
19. Evans H. E. In: Schütze M. and Quadakkers W. J. (eds) Cyclic Oxidation of High Temperature Materials pp. 3-16. EFC Publication 27, loM. Communication, London (1999).
20. Evans H. E., Donaldson A. T. and Gilmour T. C. Mechanisms of Breakaway Oxidation and Application to a Chromia-forming Steel. Oxid. Met. 52,379-402, (1999).