Stress assisted pit and fissure coalescence during early stages of Stress corrosion cracking in Al-Li-Cu alloy AA2096

NACE - International Corrosion Conference Series

Volumn 2000-March, Issue , 2000, Pages

  Connolly, Brian J ^a   Scully, John R ^a  

^a UNIVERSITY OF VIRGINIA   (United States)

Author keywords

Aluminum lithium copper alloys; Corrosion fissures; Environmental cracking; Pit coalescence; Stress corrosion crack initiation

Indexed keywords

ALUMINUM COPPER ALLOYS; ALUMINUM CORROSION; COPPER CORROSION; INTERGRANULAR CORROSION; IRON ALLOYS; LITHIUM ALLOYS; RESIDUAL STRESSES; ROAD CONSTRUCTION; SODIUM CHLORIDE; TERNARY ALLOYS;

AGING HEAT TREATMENT; ALTERNATE IMMERSIONS; ALUMINUM LITHIUMS; APPLIED STRESS INTENSITY; CRACK VELOCITIES; ELECTROCHEMICAL FACTORS; ENVIRONMENTAL CRACKING; STRESS-DEPENDENT;

STRESS CORROSION CRACKING;

EID: 85046716882     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (103)

1. C. J. Peel, B. Evans, and D. S. McDarmaid, Metallurgical Materials. 3, 8(1987): p. 449.
2. K. Urushino, and K. Sugimoto, Corrosion Science, 19(1979): p. 225.
3. J. R. Galvele, and S. M. De Micheli, Corrosion Science, 10(1970): p. 795.
4. K. Sugimoto, K. Hoshino, M. Kageyama, S. Kageyama, and Y. Sawada, Corrosion Science, 15(1975): p. 709.
5. M. Yasuda, F. Weinberg, D. Tromans, Journal of the Electrochemical Society, 137, 12(1990): p. 3708.
6. P. Niskanen, T. H. Sanders, J. G. Rinker, and M. Merek, Corrosion Science, 22(1982): p. 283
7. J. O. Park, C. H. Paik, Y. H. Huang, and R. C. Alkire, Journal of the Electrochemical Society, 146, 2(1999): p. 517.
8. A. Roth, and H. Kaesche, "Electrochemical Investigation of Technical Aluminum-Lithium Alloys - Part I: General Aspects", Aluminum-Lithium 5, (Birmingham, UK: MCEP, 1989).
9. M. J. Robinson, and N. C. Jackson, Corrosion Science, 41(1999): p. 1013.
10. Z. Q. Hu, Y. Zhang, Y. L. Liu, and Z. Y. Zhu, Corrosion, 49, 6(1993): p. 491.
11. B. Bavarian, J. Becker, S. N. Parikh, and M. Zamanzadeh, "Localized Corrosion of 2090 and 2091 Al-Li Alloys", Aluminum-Lithium 5, (Birmingham, UK: MCEP, 1989).
12. R. Ambat, E. S. Dwarakadasa, Corrosion Science, 33(1992): p. 681.
13. T. Sheppard, and N. C. Parson, Materials Science and Technology, 3(1987): p. 345.
14. C. Kumai, J. Kusinski, G. Thomas, and T. M. Devine, Corrosion, 45, 4(1989): p. 294.
15. R. G. Buchheit, J. P. Moran, and G. E. Stoner, Corrosion, 46, 8(1990): p. 610.
16. R. G. Buchheit, J. P. Moran, F. D. Wall, and G. E. Stoner, "Rapid Anodic Dissolution Based SCC of an Al-Li-Cu Alloy by Isolated Pit Solutions", Parkins Symposium on Fundamental Aspects of Stress Corrosion Cracking, (Warrendale, PA: TMS, 1992).
17. J. P. Moran, R. G. Buchheit, and G. E. Stoner, "Mechanisms of SCC of Alloy 2090 (Al-Li-Cu) - A Comparison of Interpretations from Static and Slow-Strain-Rate Techniques", Parkins Symposium on Fundamental Aspects of Stress Corrosion Cracking, (Warrendale, PA: TMS, 1992).
18. R. G. Buchheit, J. P. Moran, and G. E. Stoner, Corrosion, 50, 2(1994): p. 120.
19. R. G. Buchheit, F. D. Wall, G. E. Stoner, and J. P. Moran, Corrosion, 51, 6(1995): p. 417.
20. F. D. Wall, and G. E. Stoner, "The Correlation of Critical Electrochemical Potentials Associated with Environmental Cracking of Al-Li-Cu Alloys to Cu Depletion Along Grain Boundaries", Critical Factors in Localized Corrosion II, (Pennington, NJ: The Electrochemical Society, 1996).
21. F. D. Wall, and G. E. Stoner, Corrosion Science, 39(1997): p. 835.
22. E. I. Meletis, and W. Huang, Materials Science and Engineering, 128 A, 2(1991): p. 197.
23. R. Balasubramaniam, D. J. Duquette, and K. Ragan, Acta Metallurgia et Materialia, 39, 11(1991): p. 2607.
24. A. Roth, and H. Kaesche, "Electrchemical Investigation of Technical Aluminum-Lithium Alloys - Part II: The Lithium Depleted Zone", Aluminum-Lithium 5, (Birmingham, UK: MCEP, 1989).
25. A. K. Vasudevan, P. R. Ziman, S. C. Jha, and T. H. Sanders, "Stress Corrosion Resistance of Al-Cu-Li-Zr Alloys", Aluminum-Lithium III, (London, UK: The Institute of Metals, 1986).
26. N. J. H. Holroyd, A. Gray, G. M. Seamans, and R. Hermann, "Environment-Sensitive Fracture of Al-Li-Cu-Mg Alloys", Aluminum-Lithium III, (London, UK: The Institute of Metals, 1986).
27. E. I. Meletis, "Microstructural Effects on the Environment-Assisted Fracture Mechanisms of Al-Li Alloys", Parkins Symposium on Fundamental Aspects of Stress Corrosion Cracking, (Warrendale, PA: TMS, 1992).
28. Z. F. Wang, Z. Y. Zhu, Y. Zhang, and W. Ke, Metallurgical Transactions A, 23 A, 12(1992): p. 3337.
29. R. C. Dorward, and K. R. Hasse, Corrosion 44, 12(1988): p. 932.
30. L. Christodoulou, L. Struble, and J. R. Pickens, "Stress-Corrosion Cracking in Al-Li Binary Alloys", Aluminum-Lithium Alloys II, (Warrendale, PA: TMS-AIME, 1983).
31. S.-M. Lee, S.-I. Pyun, and Y.-G. Chun, Metallurgical Transactions A, 22 A, 10(1991): p. 2407.
32. G. P. Cherepanov, "Ch. 7: Stress Corrosion Cracking", Comprehensive Treatise of Electrochemistry, Vol. 4: Electrochemical Materials Science, (New York, NY: Plenum Press, 1981).
33. N. J. H. Holroyd, A. K. Vasudevan, and L. Christodoulou, "Ch. 16: Stress Corrosion of High-Strength Aluminum Alloys", Treatise on Materials Science and Technology, Vol. 31, (San Diego, CA: Academic Press, 1989).
34. Z. Szklarska-Smialowska, "Films and Their Importance in the Nucleation of Stress Corrosion Cracking in Stainless Steel", Hydrogen Embrittlement and Stress Corrosion Cracking: A Troiano Festschrift, (Metals Park, OH: ASM, 1984).
35. R. P. Wei, K. Klier, G. W. Simmons, and Y. T. Chou, "Fracture Mechanics and Surface Chemistry Investigations of Environment-Assisted Crack Growth", Hydrogen Embrittlement and Stress Corrosion Cracking: A Troiano Festschrift, (Metals Park, OH: ASM, 1984).
36. R. N. Parkins, Materials Science and Engineering, A103(1988): p. 143.
37. N. J. H. Holroyd, "Environment-Induced Cracking of High-Strength Aluminum Alloys", Environment-Induced Cracking of Metals, (Houston: NACE, 1990).
38. D. J. McAdam, and G. W. Gell, Journal of the Proceedings of the American Society for Testing Materials, 41(1928): p. 696.
39. C. Laird, and D. J. Duquette, "Mechanisms of Fatigue Crack Nucleation", Corrosion Fatigue: Chemistry, Mechanics, and Microstructure, (Houston: NACE, 1973).
40. D. W. Hoeppner, "Corrosion Fatigue Considerations in Materials Selections and Engineering Design", Corrosion Fatigue: Chemistry, Mechanics, and Microstructure", (Houston: NACE, 1973).
41. C. Patel, T. Pyle, and V. Rollins, Nature, 266, 5602(1977): p. 517.
42. M. Kawahara, T. Fujita, M. Kurihara, H. Inagaki, and H. Kitagawa, "Corrosion Fatigue Crack Initiation of Carbon Steels in Seawater", Basic Questions in Fatigue: Volume II, ASTM STP 924, (Philadelphia: ASTM, 1988).
43. Y. H. Huang, and M. Metzger, "Initiation of Corrosion Fatigue at Pits in an Aluminum Alloy", Embrittlement by the Localized Crack Environment, (Philadelphia: AIME, 1984).
44. M. Rebiere, and T. Magnin, Materials Science and Engineering, A128(1990): p. 99.
45. M. R. Bayoumi, A. A. Ismail, and A. K. Abd El Latif, Engineering Fracture Mechanics, 53, 1(1996): p. 141.
46. H. Kitagawa, K. Tsuji, T. Hisada, and Y. Hashimoto, "An Analysis of Random Pits in Corrosion fatigue: A Statistical Three-Dimensional Evaluation of an Irregularly Corroded Surface", Corrosion Fatigue: Mechanics, Metallurgy, Electrochemistry, and Engineering: ASTM STP 801, (Philadelphia: ASTM, 1983).
47. J. Congleton, R. A. Olieh, and R. N. Parkins, Metals Technology, 9(1982): p. 94.
48. X. Y. Zhou, and W. Ke, Acta Metallurgica Sinica (abstract), 28, 8(1992): p. B356.
49. M. Kawahara, T. Fujita, H. Inagaki, T. Iwasaki, and A. Katoh, "Simulation of Crack Initiation and growth in Corrosion Fatigue of Carbon Steels in Seawater", Corrosion Cracking (Part of the Proceedings from the International Conference and Exposition on fatigue, Corrosion Cracking, Fracture Mechanics, and Failure Analysis), (Metals Park, OH: ASM, 1986).
50. R. Ebara, T. Yamada, and H. Kawano, ISIJ International, 30, 7(1990): p. 535.
51. R. Ebara, T. Yamada, T. Kobayashi, and H. Kawano, "Corrosion Fatigue Crack Initiation and Propagation Behavior of 12 Cr Stainless Steel", Mechanical Behavior of Materials VI (vol. 2), (Oxford, UK: Pergamon Press, 1992).
52. L. Ma, "Pitting Effects on the Corrosion Fatigue Life of 7075-T6 Aluminum Alloy", PhD Dissertation, University of Utah, 1994.
53. R. Akid, "The Role of Stress-Assisted Localized Corrosion in the Development of Short Fatigue Cracks", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
54. M. Goto, and H. Nisitani, Fatigue and Fracture of Engineering Materials and Structures, 15, 4(1992): p. 353.
55. Y. Nakasone, K. Tsuli, and H. Kitagawa, "Statistical evaluation of the Role of randomly Distributed Pits and Cracks in Corrosion Fatigue", Mechanical Behavior of Materials (vol. 2), (Cambridge, UK: ICM 3, 1979).
56. G. H. Bray, R. J. Bucci, E. L. Colvin, and M. Kulak, "Effect of Prior Corrosion on the S/N Fatigue Performance of Aluminum Sheet Alloys 2024-T3 and 2524-T3", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
57. C. G. Schmidt, J. E. Crocker, J. H. Giovanola, C. H. Kanazawa, D. A. Shockley, and T. H. Flournoy, "Corrosion-Fatigue Crack Nucleation in Alclad 2024-T3 Commercial Aircraft", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
58. H. D. Solomon, R. E. DeLair, and A. D. Unruh, "Crack Initiation in Low Alloy Steel in High Temperature Water", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
59. D. J. McAdam, Journal of the Proceedings of the American Society for Testing Materials, 26(1926): p. 224.
60. T. Pyle, V. Rollins, and D. Howard, Journal of the Electrochemical Society, 122, 11(1975): p. 1445.
61. T. C. Lindley, P. Mclntyre, and P. J. Trant, Metals Technology, 9(1982): p. 135.
62. A. J. McEvily, and R. P. Wei, "Fracture Mechanics and Corrosion Fatigue", Corrosion Fatigue: Chemistry, Mechanics, and Microstructure", (Houston: NACE, 1973).
63. S. Kawai, and K. Kasai, Fatigue and Fracture of Engineering Materials and Structures, 8, 2(1985): p. 115.
64. D. W. Hoeppner, "Model for Prediction of Fatigue Lives Based Upon a Pitting Corrosion Fatigue Process", Fatigue Mechanisms: ASTM STP 675, (Philadelphia: ASTM, 1979).
65. G. S. Chen, C.-M. Liao, K.-C. Wan, M. Gao, and R. P. Wei, "Pitting Corrosion and Fatigue Crack Nucleation", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
66. G. S. Chen, K.-C. Wan, M. Gao, R. P. Wei, and T. H. Flournoy, Materials Science and Engineering, A219(1996): p. 126.
67. Y. Kondo, Corrosion, 45, 1(1989): p. 7.
68. H. Kanasaki, K. Tsutsumi, and Y. Kondo, "Effect of Pits on fatigue Strength of Carbon Steel in Oxygenated High Temperature Water", Localized Damage IV: Computer-Aided Assessment and Control, (Billerica, MA: Computational Mechanics Publications, 1996).
69. D. W. Hoeppner, D. Mann, and J. Weekes, "Fracture Mechanics Based Modelling of the Corrosion Fatigue Process", AGARD Corrosion Fatigue, (BWI Airport, MD: Scientific and Technical Information Office, NASA, 1982).
70. Y. Kondo, and R. P. Wei, "Approach on Quantitative Evaluation of Corrosion Fatigue Crack Initiation Condition", EVALMET 89 - Proceedings of the International Conference on Evaluation of Materials Performance in Severe Environments, (Kobe, Japan: ICEMP, 1989).
71. M. Müller, Metallurgical Transactions A, 13 A, 4(1982): p. 649.
72. E. R. De Los Rios, X. D. Wu, and K. J. Miller, Fatigue and Fracture of Engineering Materials and Structures, 19, 11(1996): p. 1383.
73. B. F. Brown, and C. D. Beachem, Corrosion Science, 5(1965) p. 745.
74. H. Hänninen, and I. Aho-Mantila, Metals Technology, 9(1982): p. 109.
75. 2 Solutions at 80°C", Corrosion Cracking (Part of the Proceedings from the International Conference and Exposition on fatigue, Corrosion Cracking, Fracture Mechanics, and Failure Analysis), (Metals Park, OH: ASM, 1986).
76. T. K. Christman, Corrosion, 46, 6(1990): p. 450.
77. J. M. Silcock, Corrosion, 38, 3(1982): p. 144.
78. L. F. Lin, G. Cragnolino, Z. Szklarska-Smialowska, and D. D. MacDonald, Corrosion, 37, 11(1981): p. 616.
79. G. Cragnolino, L. F. Lin, and Z. Szklarska-Smialowska, Corrosion, 37, 6(1981): p. 312.
80. R. N. Parkins, and M. Mirzai, "Influence of a Mixed Nitrate Solution on the Initiation and Early Growth of Stress Corrosion Cracks in Low Alloy Steel", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
81. Y. Kondo, M. Bodai, M. Takei, Y. Sugita, and H. Inagaki, "Environmentally Assisted Cracking of 3.5NiCrMoV Low Alloy Steel Under Cyclic Straining", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
82. M. Akashi, and G. Nakayama, "A Process Model for the Initiation of Stress-Corrosion Crack Growth in BWR Plant Materials", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
83. A. Atrens, Metals Technology, 9(1982): p. 117.
84. R. N. Parkins, Metals Technology, 9(1982): p. 122.
85. H. S. Isaacs, and R. C. Newman, "Local Electrochemistry of Pitting Corrosion in Stainless Steels", Corrosion Chemistry within Pits, Crevices, and Cracks, (London: HMSO, 1987).
86. A. S. Dolphin, and A. Turnbull, "Experimental Determination of the Electrochemistry in Corrosion-Fatigue Cracks in Structural Steel in Marine Environments", Corrosion Chemistry within Pits, Crevices, and Cracks, (London: HMSO, 1987).
87. N. J. H. Holroyd, G. M. Scamans, and R. Hermann, "Environmental Conditions within Crevices and Stress-Corrosion Cracks in Aluminum Alloys", Corrosion Chemistry within Pits, Crevices, and Cracks, (London: HMSO, 1987).
88. K. R. Cooper, and R. G. Kelly, Journal of Chromatography A, 850(1999): p. 381.
89. O. Jonas, "Molecular Modeling of Corrosive Environments in Cracks", Effects of the Environment o the Initiation of Crack Growth: ASTM STP 1298, (Philadelphia: ASTM, 1997).
90. R. N. Parkins, Materials Science and Technology, 1(1985): p. 480.
91. J. G. Parker, and G. Wigmore, Metals Technology, 9(1982): p. 216.
92. K. Ebthehaj, D. Hardie, and R. N. Parkins, Corrosion Science, 28, 8(1988): p. 811.
93. D. Whitham, and U. R. Evans, Journal of Iron and Steel Institute, 165(1950): p. 72.
94. V. Rollins, and T. Pyle, Nature, 254, 5498(1975): p. 322.
95. C. Patel, T. Pyle, and V. Rollins, Metal Science, 11, 6(1977): p. 185.
96. B. A. Szabo, and I. Babuska, Finite Element Analysis (New York: Wiley, 1991).
97. B. J. Connolly, and J. R. Scully, submitted to Scripta Materialia September, 1999.
98. E. A. Starke, "Heat-Treatable Aluminum Alloys", Aluminum Alloys - Contemporary Research and Applications: treatise on Materials Science and Technology, Volume 31, (London: Academic Press, 1989).
99. E. H. Hollingsworth, and H. Y. Hunsicker, "Corrosion of Aluminum and Aluminum Alloys", ASM Handbook: Corrosion, Volume 13, (Metals Park, OH: ASM International, 1987).
100. M. A. Myers, and K. K. Chawla, Mechanical Metallurgy: Principals and Applications (Englewood Cliffs, NJ: Prentice-Hall, 1984).
101. J. R. Scully, T. O. Knight, R. G. Buchheit, and D. E. Peebles, Corrosion Science, 35(1993): p. 185.
102. J. C. Newman, and I. S. Raju, "Stress-Intensity Factor Equations for Cracks in Three-Dimensional Finite Bodies", Fracture Mechanics: Fourteenth Symposium - Volume I: Theory and Analysis, ASTM STP 791, (Philadelphia: ASTM, 1983).
103. J. C. Newman, and I. S. Raju, "Stress-Intensity Factor Equations for Cracks in Three-Dimensional Finite Bodies Subjected to Tension and Bending Loads", NASA Technical Memorandum 84793, (Hampton, VA: NASA, 1984).