Finite element analysis of stresses due to pitting of steel specimens under different cyclic bending stresses

Engineering Fracture Mechanics

Volumn 53, Issue 1, 1996, Pages 141-151

  Bayoumi, M R ^a   Ismail, A A ^b   Abd El Latif, A K ^c  

^a Assiut University   (Egypt)

^b SAMARC   (Saudi Arabia)

^c KING ABDULAZIZ UNIVERSITY   (Saudi Arabia)

Author keywords

[No Author keywords available]

Indexed keywords

BENDING STRENGTH; CORROSION FATIGUE; CRACK INITIATION; CRACK PROPAGATION; FINITE ELEMENT METHOD; FRACTURE; PITTING; POLYNOMIALS; SHEAR STRESS; STEEL;

CRACK FORMATION; CYCLIC BENDING STRESSES; FATIGUE FAILURE; PITTING INTENSITY CONDITIONS; STRESS CONTOURS;

STRESS ANALYSIS;

EID: 0029731948     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/0013-7944(95)00073-5     Document Type: Article

References (9)

1. H. U. Herbert, Corrosion and Corrosion Control. John Wiley (1992).
2. G. Butler and H. C. K. Ison, Corrosion and its Prevention in Water. Robert E. Krieger, Huntigton, New York, U.S.A. (1978).
3. U. R. Evans and S. M. Tchorabd, Jr. Proc. Roy. Soc. A. 188, 372 (1947).
4. M. Paul and H. Weiland, Electrochim, ACTA 14, 1025 (1969).
5. V. Rollins, B. Arnold and E. Lardner, Br. Corrosion J. 5, 33 (1970).
6. W. G. Clerk, Fracture Toughness and Slow-stable Cracking STP 559, 205, Philadelphia, U.S.A. (1974).
7. M. P. Muller, Corrosion 38, 431 (1982).
8. H. M. Shalaby and V. K. Gouda, Effect of chloride concentration and pH on fatigue crack initiation morphology of type 403 stainless steel. Br Corrosion J. 16 (1985).
9. C. P. Derveins, E. R. Meletis and R. F. Hochman, Corrosion fatigue in Al-Al alloy 2090. Materials Science and Engng, A Structural Material 102, 151-160 (1988).