The role of stress-assisted localized corrosion in the development of short fatigue cracks

ASTM Special Technical Publication

Volumn 1298, Issue , 1997, Pages 3-17

  Akid, Robert ^a  

^a UNIVERSITY OF SHEFFIELD   (United Kingdom)

Author keywords

Corrosion fatigue; Microstructural fracture mechanics; Modelling; Pitting; Scanning reference electrode; Short cracks

Indexed keywords

CORROSION FATIGUE; CRACK PROPAGATION; FRACTURE MECHANICS; INTERFACES (MATERIALS); MICROSTRUCTURE; PITTING; STAINLESS STEEL; STRENGTH OF MATERIALS;

SCANNING REFERENCE ELECTRODES;

STRESS CORROSION CRACKING;

EID: 0031122923     PISSN: 00660558     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1520/stp19950s     Document Type: Article

References (40)

1. Magnin, T., "Influence of surface defects on hydrogen effects during stress corrosion and corrosion fatigue", In Hydrogen Transport and Cracking in Metals , The Institute of Materials, Ed by A Turnbull 1995, pp 38-49.
2. Akid, R., "The influence of cathodic over-potential on Microstructural and Physically-small crack growth". As ref 1 pp50-61.
3. Gangloff, R., "Critical issues in reducing corrosion of steel" NACE Eds H. Leidheiserand S. Haruyuma., 1986, pp28-50.
4. The Behaviour of Short Fatigue Cracks, Eds. K. J.Miller and E.R. de los Rios, EGF Publication 1., MEP, Instn Mech Engs, London, 1986.
5. Short Fatigue Cracks, Eds by K. J. Miller and E. R. de los Rios, Mechanical Engineering Publications 1992
6. Small Fatigue Cracks Eds. R O. Ritchie and J Lankford., TMS-ASME, Warrandale PA., 1986.
7. Hobson, P. D., Brown, M. W., and de los Rios, E. R., "Two Phases of Short Crack Growth in a Medium Carbon Steel", The Behaviour of Short Fatigue Cracks, Eds. by K. J. Miller and E. R. de los Rios, EGF Publication 1, 1986, pp. 441-459.
8. Navarro, A., and de los Rios, E. R., "A Microstructurally-Short Fatigue Crack Growth Equation", Fat. Fract. Engng. Mat. Struct., 11, 1988, pp. 383-396.
9. Akid, R., "The Initiation and Growth of Short Fatigue Cracks in an Aqueous Saline Environment", PhD thesis, University of Sheffield 1987.
10. Akid, R., and Miller, K. J., "Short Fatigue Crack Growth Behaviour of a Low Carbon Steel Under Corrosion Fatigue Conditions". Fat. Fract. Engng. Mat. Struct. 14, 1991, pp 637-649.
11. Akid, R., and Murtaza, G., "Environmental-Assisted Short Fatigue Crack Growth Behaviour of a High Strength Steel" In 'Short Fatigue Cracks' ESIS 13, Eds K. J. Miller and E. R. de los Rios, MEP, Instn Mech Engs, London, 1992, pp 193-207.
12. Akid, R., Wang, Y. Z., and Fernando, U., "Influence of Loading Mode on Environment-Assisted Fatigue Crack Growth", , In Corrosion-Deformation Interactions, Eds T. Magnin and J. M. Gras. Publishers, Les Editions de Physique Les Ulis, 1993, pp 659-670.
13. Zhang, W., and Akid, R., "The Influence of Environment and Biaxial Mean Stress on the Behaviour of Short Fatigue Crack Growth", In preparation, 1996.
14. Wu, X. D., PhD Thesis "Experimental and Theoretical Studies of Corrosion Fatigue in a High Strength Steel", The University of Sheffield, 1995.
15. Boukerrou, and Cottis, "The Influence of Corrosion on the Growth of Short Fatigue cracks in Structural Steels", In Short Fatigue Cracks ESIS 13, Eds K. J. Miller and E. R. de los Rios, MEP, Instn Mech Engs, London, 1992, pp. 209-216.
16. Isaacs, H. S., and Kissel, G., "Surface Preparation and Pit Propagation in Steels" J. Elect. Soc. 116 , 1972, pp 1628-1631.
17. Ambrose, J. R., and Kruger, J. 4th International Congress on Metallic Corrosion, 1969.
18. Akid, R., "Modelling Environment-Assisted Short Fatigue Crack Growth" Advances in Fracture Resistance and Structural Integrity, Ed. V. V. Panasyuk, D. M. R., Taplin et al, Pergamon Press, 1993, pp 261-269.
19. Szklarska-Smialowska, Z., Pitting Corrosion of Metals, NACE, 1986, Texas USA.
20. Ray, G. P., et al, "Some Aspects of Crack Initiation in Mild Steel under Corrosion Fatigue Conditions" J. Mat. Sci. 29, 1994, pp 47-53.
21. Akid, R., and Miller, K. J., "The effect of Solution pH on the Initiation and Growth of Short Fatigue Cracks", Fracture Behaviour and Design of Materials and Structures, Proceedings of ECF 8, EMAS, Torino, 1990, pp. 1753-1758.
22. Annual Book of ASTM Standards, 03.02, 1985.
23. Hunkeler, F. and Bohni, H., "On the Mechanism of Localised Corrosion", Corrosion 43, 1987, pp 189-191
24. Magnin, T., and Landon, J. M., "The Influence of a 3.5% NaCl Solution on the Fatigue Damage Evolution in a Plane Slip f.c.c Stainless Steel", Mat. Sci. and Engineering, 76 L7-L10, 1995.
25. Newman, R. C., "Measurement and Interpretation of Electrochemical Kinetics on Bare Metal Surfaces", In Corrosion Chemistry within Pits and Cracks. Ed. A. Turnbull, 1987, pp. 317-356.
26. Akid, R., Localised Corrosion: A new evaluation approach. Materials World, 11, 1995, pp. 522-525.
27. Akid, R., and Murtaza, G., "Corrosion Fatigue Crack Growth Modelling of a High Strength Steel Subjected to Torsional Loading", Life Prediction of Corrodible Structures. NACE publication, Eds. R. Parkins and R. W. Staehle, 1994, pp. 1296-1308.
28. Wu, X. D., PhD Thesis "Experimental and Theoretical Studies of Corrosion Fatigue in a High Strength Steel", The University of Sheffield, 1995.
29. Wu, X. J., PhD Thesis "Short Fatigue Crack Behaviour of a Submarine Hull Steel in Inert and Aggressive Environments"., University of Sheffield., 1995.
30. Dmytrakh, I. M., Akid, R., and Miller, K. J., "Electrochemistry of Deformed Smooth Surfaces and Short Corrosion Fatigue Crack Growth Behaviour". To be published in British Corrosion Journal ,1996.
31. Murtaza, G., PhD Thesis "Corrosion Fatigue Short Crack Growth Behaviour in a High Strength Steel" The University of Sheffield, 1994
32. Guilhem, F., MPhil thesis, In preparation, The University of Sheffield, 1996.
33. Goto, M., "Corrosion Fatigue Behaviour of Heat Treated Carbon Steel and its Statistical Characteristics", Eng. Fract. Mech. 42, 1992, pp 893-909.
34. Daeubler, M. A., Thompson, A. W., and Bernstein, I. M., "Fatigue Behaviour in the Potentiostatic Passive Corrosiion Regime of the Iron-Base Superalloy A-286" Metall Trans 22A, 1991, pp. 513-519.
35. Nakajima, N., and Tokaji, K., "Fatigue Life Distribution and Growth of Corrosion Pits in a Medium Carbon Steel in 3% - NaCl Solution", Fat. Fract. Engng. Mat. Struct., 18, 1995, pp. 345-351.
36. Zhang, W., and Akid, R., "Effects of Biaxial Mean Stress on Cyclic Stress-Strain Response and Behaviour of Short Cracks", Submitted to Fat. Fract. Engg. Mat. Struct , 1996
37. Akid. R., and Wu, X. J., "An Investigation of Short Fatigue Crack Growth of a High Strength Marine Steel in Seawater", In Structural Materials in Marine Environments, The Institute of Materials, 1994, pp. 330-345.
38. Rollins, V., Arnold, B., and Lardner, E., "Corrosion Fatigue in High Carbon Steel", Br. Corros J. , 5, 1970, pp 33-40.
39. Miller K. J., and Akid R., "The Application of Microstructural Fracture Mechanics to Various Metal Surface States.", Proc. R. Soc. Lond , 452, 1996, pp 1411-1432
40. Turnbull A., "Mathematical Modelling of Localised Corrosion", In Modelling Aqueous Corrosion, Eds. K.R. Trethewey and P.R. Roberge, NATO ASI Series, 226, 1994, pp 29-63