Making yttria-stabilized tetragonal zirconia translucent

Dental Materials

Volumn 30, Issue 10, 2014, Pages 1195-1203

  Zhang, Yu ^a  

^a NEW YORK UNIVERSITY   (United States)

Author keywords

Grain size; Light scattering; Microstructure; Optical birefringence; Translucency; Zirconia (Y TZP)

Indexed keywords

BIREFRINGENCE; LIGHT SCATTERING; MICROSTRUCTURE; PORCELAIN; REFRACTIVE INDEX; YTTRIA STABILIZED ZIRCONIA; YTTRIUM OXIDE; ZIRCONIA;

GOVERNING PARAMETERS; GRAIN SIZE; GRAIN SIZE DEPENDENCE; HIGH REFRACTIVE INDEX; OPTICAL BIREFRINGENCE; TETRAGONAL YTTRIA-STABILIZED ZIRCONIAS; TRANSLUCENCY; YTTRIA STABILIZED TETRAGONAL ZIRCONIAS;

GRAIN SIZE AND SHAPE;

YTTRIUM; ZIRCONIUM; ZIRCONIUM OXIDE;

CHEMICAL MODEL; CHEMISTRY;

MODELS, CHEMICAL; YTTRIUM; ZIRCONIUM;

EID: 84922326073     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.dental.2014.08.375     Document Type: Article

References (43)

1. Sax C, Hammerle CH, Sailer I. 10-year clinical outcomes offixed dental prostheses with zirconia frameworks. Int JComput Dent 2011;14:183-202.
2. Larsson C, Vult Von Steyern P. Implant-supported full-archzirconia-based mandibular fixed dental prostheses. Eight-year results from a clinical pilot study. Acta Odontol Scand 2012;71:1118-22.
3. Ortorp A, Kihl ML, Carlsson GE. A 5-year retrospective studyof survival of zirconia single crowns fitted in a privateclinical setting. J Dent 2012;40:527-30.
4. Schmitter M, Mussotter K, Rammelsberg P, Gabbert O, Ohlmann B. Clinical performance of long-span zirconiaframeworks for fixed dental prostheses: 5-year results. J Oral Rehabil 2012;39:552-7.
5. Zhang Y, Kim JW. Graded zirconia glass for resistance toveneer fracture. J Dent Res 2010;89:1057-62.
6. Aboushelib MN, Feilzer AJ, Kleverlaan CJ. Bridging the gapbetween clinical failure and laboratory fracture strengthtests using a fractographic approach. Dent Mater 2009;25:383-91.
7. Baldassarri M, Zhang Y, Thompson VP, Rekow ED, Stappert CF. Reliability and failure modes of implant-supportedzirconium-oxide fixed dental prostheses related toveneering techniques. J Dent 2011;39:489-98.
8. Liu Y, Liu G, Wang Y, Shen JZ, Feng H. Failure modes andfracture origins of porcelain veneers on bilayer dentalcrowns. Int J Prosthodont 2014;27:147-50.
9. Beuer F, Stimmelmayr M, Gueth JF, Edelhoff D, Naumann M. In vitro performance of full-contour zirconia single crowns. Dent Mater 2012;28:449-56.
10. Christensen R. Focus on: monolithic crowns. Dent Today 2013;32:22.
11. Griffin Jr JD. Tooth in a bag: same-day monolithic zirconiacrown. Dent Today 2013;32(124):126-31.
12. Ma L, Guess PC, Zhang Y. Load-bearing properties ofminimal-invasive monolithic lithium disilicate and zirconiaocclusal onlays: finite element and theoretical analyses. Dent Mater 2013;29:742-51.
13. Rinke S, Fischer C. Range of indications for translucentzirconia modifications: clinical and technical aspects. Quintessence Int 2013;44:557-66.
14. Stober T, Bermejo JL, Rammelsberg P, Schmitter M. Enamelwear caused by monolithic zirconia crowns after 6 monthsof clinical use. J Oral Rehabil 2014;41:314-22.
15. Zhang Y, Kim JW. Graded structures for damage resistantand aesthetic all-ceramic restorations. Dent Mater 2009;25:781-90.
16. Zhang Y, Lee JJ, Srikanth R, Lawn BR. Edge chipping andflexural resistance of monolithic ceramics. Dent Mater 2013;29:1201-8.
17. 2. Phys Rev B 1994;49:5133-41.
18. Klimke J, Trunec M, Krell A. Transparent tetragonalyttria-stabilized zirconia ceramics: influence of scatteringcaused by birefringence. J Am Ceram Soc 2011;94:1850-8.
19. Krell A, Klimke J, Hutzler T. Transparent compact ceramics:inherent physical issues. Opt Mater 2009;31:1144-50.
20. Yamashita I, Tsukuma K. Light scattering by residual poresin transparent zirconia ceramics. J Ceram Soc Jpn 2011;119:133-5.
21. Zhang HB, Li ZP, Kim BN, Morita K, Yoshida H, Hiraga K, et al. Effect of alumina dopant on transparency of tetragonalzirconia. J Nanomater 2012. Article ID 269064.
22. Anselmi-Tamburini U, Woolman JN, Munir ZA. Transparentnanometric cubic and tetragonal zirconia obtained byhigh-pressure pulsed electric current sintering. Adv Funct Mater 2007;17:3267-73.
23. Zhang HB, Li ZP, Kim BN, Morita K, Yoshida H, Hiraga K, et al. Highly infrared transparent nanometric tetragonal zirconiaprepared by high-pressure spark plasma sintering. J AmCeram Soc 2011;94:2739-41.
24. Wood DL, Nassau K. Refractive-index of cubic zirconiastabilized with yttria. Appl Opt 1982;21:2978-81.
25. Alaniz JE, Perez-Gutierrez FG, Aguilar G, Garay JE. Opticalproperties of transparent nanocrystalline yttria stabilizedzirconia. Opt Mater 2009;32:62-8.
26. Zhang HB, Kim BN, Morita K, Yoshida H, Lim JH, Hiraga K. Optical properties and microstructure of nanocrystallinecubic zirconia prepared by high-pressure spark plasmasintering. J Am Ceram Soc 2011;94:2981-6.
27. Peuchert U, Okano Y, Menke Y, Reichel S, Ikesue A. Transparent cubic-zro(2) ceramics for application as opticallenses. J Eur Ceram Soc 2009;29:283-91.
28. Krell A, Hutzler T, Klimke J. Transmission physics andconsequences for materials selection, manufacturing, andapplications. J Eur Ceram Soc 2009;29:207-21.
29. Zhang HB, Kim BN, Morita K, Hiraga HYK, Sakka Y. Effect ofsintering temperature on optical properties andmicrostructure of translucent zirconia prepared byhigh-pressure spark plasma sintering. Sci Technol Adv Mater 2011;12:055003.
30. Casolco SR, Xu J, Garay JE. Transparent/translucent polycrystalline nanostructured yttria stabilized zirconia with varying colors. Scr Mater 2008;58:516-9.
31. Trunec M, Chlup Z. Higher fracture toughness of tetragonalzirconia ceramics through nanocrystalline structure. Scr Mater 2009;61:56-9.
32. Apetz R, van Bruggen MPB. Transparent alumina: alight-scattering model. J Am Ceram Soc 2003;86:480-6.
33. Heiroth S, Ghisleni R, Lippert T, Michler J, Wokaun A. Opticaland mechanical properties of amorphous and crystallineyttria-stabilized zirconia thin films prepared by pulsed laserdeposition. Acta Mater 2011;59:2330-40.
34. Ding Y, Jiang S, Luo T, Hu Y, Miura Y, Peyghambarian N. Lithium disilicate crystalline slab waveguides from surfacecrystallised glass. Electron Lett 1999;35:504-5.
35. Heffernan MJ, Aquilino SA, Diaz-Arnold AM, Haselton DR, Stanford CM, Vargas MA. Relative translucency of sixall-ceramic systems. Part i: Core materials. J Prosthet Dent 2002;88:4-9.
36. Coble RL. Transparent alumina and method of preparation.US Patent 3,026,210 March 20, 1962.
37. van Vliet J, de Groot JJ. High-pressure sodium dischargelamps. IEE Proc Sci Meas Technol 1981;128:415-41.
38. Rice RW. Effects of environment and temperature onceramic tensile strength grain size relations. J Mater Sci 1997;32:3071-87.
39. Chantikul P, Bennison SJ, Lawn BR. Role of grain size in thestrength and R-curve properties of alumina. J Am Ceram Soc 1990;73:2419-27.
40. Bravo-Leon A, Morikawa Y, Kawahara M, Mayo MJ. Fracturetoughness of nanocrystalline tetragonal zirconia with lowyttria content. Acta Mater 2002;50:4555-62.
41. 3 system. J Mater Sci 1982;17:240-6.
42. van de Hulst HC. Light scattering by small particles. New York: John Wiley and Sons, Inc.; 1957.
43. Savoini B, Ballesteros C, Muñoz Santiuste JE, González R, Chen Y. Thermochemical reduction ofyttria-stabilized-zirconia crystals: optical and electronmicroscopy. Phys Rev B 1998;57:13439-47.