10.02 - Stress Corrosion Cracking

Comprehensive Structural Integrity

Volumn 10, Issue , 2007, Pages 43-74

  Dietzel, W ^a   Turnbull, A ^b  

^a INSTITUTE OF MATERIALS RESEARCH   (Germany)

^b NATIONAL PHYSICAL LABORATORY   (United Kingdom)

Author keywords

Accelerated stress corrosion cracking test; Acronyms; Breaking load test; C(B); C(T); Cantilever bend; CERT; CMOD; COD; Compact; Constant displacement stress corrosion cracking tests; Constant extension rate tensile (= slow strain rate); Constant extension rate test; Constant load stress corrosion cracking test; Crack opening displacement; Crack mouth opening displacement; Crack tip opening angle; Crack tip opening displacement; CTOA; CTOD; DCB; Double cantilever beam; EAC; Environmentally assisted cracking; Fracture mechanics approach to stress corrosion cracking; Hydrogen embrittlement; IGSCC; Incubation time for stress corrosion cracking; Intergranular stress corrosion cracking; Linear variable displacement transducer; Linearly increasing stress test; LIST; LVDT; RA; Reduction in area; Rising displacement stress corrosion cracking test; Rising load stress corrosion cracking test; Scanning electron microscope; SCC; SE(B); SEM; Single edge notch; Slow strain rate test; Specimen Types; SSRT; Stress corrosion cracking; Subcritical crack extension; TGSCC; Threshold stress for stress corrosion cracking; Threshold stress intensity factor for stress corrosion cracking; Time to failure; Transgranular stress corrosion cracking; Wedge open loaded; WOL

Indexed keywords

ASPHALT PAVEMENTS; CANTILEVER BEAMS; CRACK PROPAGATION; CRACK TIPS; HYDROGEN EMBRITTLEMENT; INTERGRANULAR CORROSION; LOAD TESTING; NANOCANTILEVERS; RADIUM; RESIDUAL STRESSES; SCANNING ELECTRON MICROSCOPY; STRAIN RATE; STRESS INTENSITY FACTORS; TEXTURES; TIME-TO-FAILURE; TRANSDUCERS;

ACCELERATED STRESS; ACRONYMS; BREAKING LOAD; CANTILEVER BENDS; CERT; CMOD; COMPACT; CONSTANT EXTENSION RATE TESTS; CONSTANT LOADS; CRACK EXTENSION; CRACK MOUTH OPENING DISPLACEMENT; CRACK OPENING DISPLACEMENTS; CRACK TIP OPENING ANGLE; CRACK TIP OPENING DISPLACEMENT; CTOA; CTOD; DOUBLE CANTILEVER BEAM; ENVIRONMENTALLY ASSISTED CRACKING; FRACTURE MECHANICS APPROACH; IGSCC; INCUBATION TIME; INTERGRANULAR STRESS CORROSION CRACKING; LINEAR VARIABLE DISPLACEMENT TRANSDUCERS; LINEARLY INCREASING STRESS TESTS; LIST; LOAD STRESS; LVDT; REDUCTION IN AREA; SINGLE EDGE NOTCHES; SLOW STRAIN RATE TESTS; SLOW STRAIN RATES; SPECIMEN TYPES; SSRT; TGSCC; THRESHOLD STRESS; THRESHOLD STRESS INTENSITY FACTOR; TRANSGRANULAR STRESS CORROSION CRACKING; WEDGE OPEN LOADED;

STRESS CORROSION CRACKING;

EID: 84903404048     PISSN: None     EISSN: None     Source Type: Book    
DOI: 10.1016/B978-008043749-1/00325-5     Document Type: Chapter

References (51)

1. Abramson G., Evans J.T., Parkins R.N. Investigation of stress corrosion crack growth in Mg alloys using J-integral estimations. Metall. Trans. 1985, 16A:101-108.
2. Anderson D.R., Gudas J.P. Stress corrosion evaluation of titanium alloys using ductile fracture mechanics technology. ASTM STP 821, Environment Sensitive Fracture, Evaluation and Comparison of Tests Methods 1984, 98-113. American Society for Testing and Materials, West Conshohocken. S.W. Dean, E.N. Pugh, G.M. Ugiansky (Eds.).
3. Atrens A., Brosnan C.C., Ramamurthy S., Oehlert A., Smith I.O. Linearly increasing stress test (LIST) for SCC research. Meas. Sci. Technol. 1993, 4:1281-1292.
4. Atrens A., Humphrey S., Piper J.J.P., Wang J.Q. Recent advances in our understanding of the mechanism of intergranular SCC in pipeline steels and its relation to service experience. Proceedings of CORROSION/2004 Research Topical Symposium: Corrosion Modelling for Assessing the Condition of Oil and Gas Pipelines 2004, 275-325. NACE International, Houston. F. King, J. Beavers (Eds.).
5. Bruemmer S.M., Thomas L.E. High-resolution analytical electron microscopy characterization of corrosion and cracking at buried interfaces. Surf. Interface Anal. 2001, 31:571-581.
6. ISCC testing, Stress corrosion - new approaches. ASTM STP 610 1976, 108-127. American Society for Testing and Materials, West Conshohocken. H.L. Craig (Ed.).
7. Cooper, K. R. 2001. Chemistry and Electrochemistry of Environment-Assisted Cracking of an Al-Zn-Mg-Cu Alloy. Ph.D. thesis, University of Virginia.
8. Cottis, R. A. 2000. Stress corrosion cracking - guide to good practice in corrosion control. National Physical Laboratory (available as download from). http://www.npl.co.uk.
9. Dietzel, W. 1991. Zur Anwendung bruchmechanischer Methoden bei der Untersuchung des Umgebungseinflusses auf die Rißausbreitung bei zûgiger Beanspruchung (in German), Report GKSS 91/E/27, Geesthacht.
10. Dietzel W. ESIS guidelines for fracture mechanics based stress corrosion testing. Technol. Law Insur. 1996, 1:151-157.
11. Dietzel, W. 1999. Characterization of susceptibility of metallic materials to environmentally assisted cracking, Report GKSS 99/E/24, GKSS-Forschungszentrum Geesthacht GmbH, Geesthacht, Germany.
12. Dietzel W., Schwalbe K.-H. Monitoring stable crack growth using a combined AC/DC potential drop technique. Z. Materialprûfung/Materials Testing 1986, 28(11):368-372.
13. Dietzel W., Schwalbe K.-H. A study of the hydrogen induced stress corrosion cracking of a low alloy steel using fracture mechanics techniques. Hydrogen Effects on Material Behavior 1990, 975-983. The Minerals, Metals & Materials Society, Warrendale, PA. N.R. Moody, A.W. Thompson (Eds.).
14. Dietzel W., Schwalbe K.-H. Application of the rising displacement test to SCC investigations. ASTM STP 1210, Slow Strain Rate Testing for the Evaluation of Environmentally Induced Cracking: Research and Engineering Applications 1993, 134-148. American Society for Testing and Materials, Philadelphia. R.D. Kane (Ed.).
15. Dietzel W., Pfuff M., Juilfs G.G. Studies of SCC and hydrogen embrittlement of high strength alloys using fracture mechanics methods. Mater. Sci. Forum. 2005, 482:11-16.
16. Dietzel W., Schwalbe K.-H., Wu D. Application of fracture mechanics techniques to the environmentally assisted cracking of aluminium 2024. Fatigue Fract. Eng. Mater. Struct. 1989, 12(6):495-510.
17. Erlings J.G., de Groot H.W., Nauta J. The effect of slow plastic straining on sulphide stress cracking and hydrogen embrittlement of 3.5% Ni steel and API 5L X60 pipeline steel. Corros. Sci. 1987, 27:1153-1167.
18. Ford F.P. The crack-tip system and its relevance to the prediction of cracking in aqueous environments. NACE-10, National Association of Corrosion Engineers 1988, 139-166. R.P. Gangloff, M.B. Ives (Eds.).
19. Gangloff R.P., Ives M.P. Proceedings of Environment-Induced Cracking of Metals, Kohler, 1989 1990, National Association of Corrosion Engineers, Houston.
20. Hinds G., Turnbull A. Testing of supermartensitic stainless steel welds under cathodic protection at very low strain rates. Corrosion 2006, 62:371-374.
21. Judy, R. W. and Goode, R. J. 1970. Prevention and control of subcritical crack growth fracture resistance in high-strength metals. Naval Research Laboratory, Washington, D.C. Report 7780.
22. Kaufmann J.G. Stress corrosion - tradition vs. fractured mechanicians. Corrosion 1979, 35:i.
23. McHenry H.I., Read T., Shives T.R. Failure of an amine-absorber pressure vessel. Mater. Perf. 1987, 26:18-24.
24. McIntyre, P. and Priest, A. H. 1972. Accelerated test technique for the determination of K ISCC in steels, British Steel Corporation Report MG/31/71, London, UK.
25. Parkins R.N. Stress corrosion test methods. Br. Corros. J. 1972, 7:154-167.
26. Parkins R.N. Development of strain-rate testing and its implications. ASTM STP 665, Stress Corrosion Cracking - The Slow Strain-Rate Technique 1979, 5-25. American Society for Testing and Materials, West Conshohocken. G.M. Ugiansky, J.H. Payer (Eds.).
27. Parkins R.N., Belhimer E., Blanchard W.K. Stress corrosion cracking characteristics of a range of pipeline steels in carbonate-bicarbonate solution. Corrosion 1993, 49:951-966.
28. Pfuff, M. and Dietzel, W. 2005. Mesoscale modeling of hydrogen assisted crack growth in heterogeneous materials. Proceedings of 11th International Conference on Fracture, ICF 11, 20-25 March 2005, Turin, Italy(CD Rom).
29. Ramamurthy S., Atrens A. The stress corrosion cracking of as-quenched 4340 and 3.5NiCrMoV steels under stress rate control in distilled water at 90C. Corros. Sci. 1993, 34:1385-1402.
30. Raymond L., Crumly W.R. Accelerated low cost test method for measuring the susceptibility of HY-steels to hydrogen embrittlement. Proceeding of First Hydrogen Problems in Steel 1982, 477-480. American Society for Metals, Metals Park OH.
31. Rice J.R., Drugan W.J., Sham T.L. Elastic-plastic analysis of growing cracks. ASTM STP, Fracture Mechanics Twelfth Conference 1980, Vol. 700:189-221. American Society for Testing and Materials, Philadelphia.
32. Ritter S., Seifert H.-P. The effect of chloride and sulphate transients on the stress corrosion cracking behavior of low-alloy reactor pressure vessel steels under simulated BWR environment. Power Plant Chem. 2004, 6:748-760.
33. Schra L., Groep F.F. The ASCOR test: A simple automated method for stress corrosion testing of aluminium alloys. J. Test. Eval. 1993, 21(1):44-50.
34. 5 as an operational definition of the CTOD and its practical use. ASTM STP 1256 1995, 763-778. American Society for Testing and Materials, Philadelphia, Fracture Mechanics: 26th Volume. W.G. Reuter, J.H. Underwood, J.C. Newman (Eds.).
35. Proceedings of the Second Conference on Environment-Induced Cracking of Metals 2006, Elsevier, (in print). S. Shipilov (Ed.).
36. Speidel M.O. Current understanding of stress corrosion crack growth in aluminium alloys. The Theory of Stress Corrosion Cracking 1971, 289-344. NATO, Brussels. J.C. Scully (Ed.).
37. Sprowls, D. O., Bucci, R. J., Ponchel, B. M., Brazill, R. L., Bretz, P. E. 1984. A study of environmental characterization of conventional and advanced aluminium alloys for selection and design. Phase II - the breaking load test method. National Aeronautics and Space Administration, Washington, D.C., USA. NASA Contractor Report CR-172387.
38. Strieder K., Daum K.-H., Dietzel W., Mûller-Roos J. The use of slow strain rate tests for measuring the velocity of environmentally assisted cracking. Structural Integrity: Experiments - Models - Applications, Proceedings of the 10th European Conference on Fracture 1994, 715-720. Engineering Materials Advisory Services Ltd., Warley, UK. K.-H. Schwalbe, C. Berger (Eds.).
39. Turnbull, A. 1992. Test Methods for Environment-Assisted Cracking, NPL Report DMM(A)66, National Physical Laboratory, Teddington, Middlesex, UK, ISSN 0959 2423.
40. Turnbull A. Testing and modelling for prediction of hydrogen embrittlement. Proceedings of Ageing Studies and Lifetime Extension of Materials, Oxford, 1999 2001, 397-414. Kluwer Academic, New York. L.G. Mallinson (Ed.).
41. Turnbull, A. and Nimmo, W. 2004. Methodology for determining the resistance of welded corrosion resistant alloys to stress corrosion using the four-point bend method, NPL Report, DEPC-MPE 007, National Physical Laboratory, Teddington, Middlesex, UK.
42. Turnbull A., Saenz de Santa Maria M. Relative importance of crack-tip charging and bulk charging in hydrogen-assisted cracking in aqueous solutions. Proceedings of Environment-Induced Cracking of Metals 1990, 193-196. NACE-10, NACE International, Houston. R.P. Gangloff, M.B. Ives (Eds.).
43. Venkatasubramanian T.V., Unvala B.A. An AC potential drop system for monitoring crack length. J. Sci. Instrum. 1984, 17:765-771.
44. Wang Z.F., Atrens A. Initiation of stress corrosion cracking for pipeline steels in a carbonate-bicarbonate solution. Metall. Mater. Trans. 1996, 27A:2686-2691.
45. Wanhill R.J.H. Aqueous stress corrosion in titanium alloys. Br. Corros. J. 1975, 10:69-78.
46. Wanhill R.J.H. Fracture control guidelines for stress corrosion cracking of high strength alloys 1991, National Aerospace Laboratory NLR, Amsterdam, The Netherlands, NLR Technical Publication TP 91006 L.
47. ISCC and da/dt determination procedures for high-strength steels. J. Test. Eval. 1987, 15:38-75.
48. Winzer N., Song G., Atrens A., Dietzel W., Blawert C. Transgranular SCC of magnesium. Proceedings of Corrosion and Prevention 2005 2005, 37-48. Australasian Corrosion Association, Inc., Melbourne. G. Kelley (Ed.).
49. Winzer, N., Song, G., Atrens, A., Dietzel, W., and Blawert, C. 2006. Evaluation of Mg TGSCC using LIST and SSRT. To be presented at the 7th International Conference on Magnesium Alloys and their Applications, November 2006, Dresden.
50. ISCC testing procedure by round robin tests on steel. ASTM STP 945, Fracture Mechanics: Eighteenth Symposium 1988, 843-866. American Society for Testing and Materials, Philadelphia. D.T. Read, R.P. Reed (Eds.).
51. Zhou S., Turnbull A. Effect of stress transients on the crack propagation rate in steam turbine disc steel. Corrosion 2006, 62:508-513.