Technical note: Testing of supermartensitic stainless steel welds under cathodic protection at very low strain rates

Corrosion

Volumn 62, Issue 5, 2006, Pages 371-374

  Hinds, Gareth ^a   Turnbull, A ^b  

^a NATIONAL PHYSICAL LABORATORY   (United Kingdom)

^b NONE

Author keywords

Cathodic protection; Hydrogen embrittlement; Slow strain rate testing; Supermartensitic stainless steel; Welds

Indexed keywords

FAILURE ANALYSIS; HYDROGEN EMBRITTLEMENT; STAINLESS STEEL; STRAIN RATE; STRESS CORROSION CRACKING; WELDS;

HYDROGEN-ASSISTED CRACKING; SLOW STRAIN RATE TESTING; SUPERMARTENSITIC STAINLESS STEEL WELDS;

CATHODIC PROTECTION;

CATHODIC PROTECTION; FAILURE ANALYSIS; HYDROGEN EMBRITTLEMENT; STAINLESS STEEL; STRAIN RATE; STRESS CORROSION CRACKING; WELDS;

EID: 33750859228     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3278274     Document Type: Article

References (8)

1. A. Turnbull, A. Griffiths, Corros. Eng. Sci. Technol. 38 (2003): p. 21.
2. S. Olsen, J. Enerhaug, "Common Pitfalls During SSC and Pitting Testing of Supermartensitic Stainless Steels for Use in Pipelines," CORROSION/2002, paper no. 38 (Houston, TX: NACE International, 2002).
3. Supermartensitics 2002 (Zutphen, The Netherlands: KCI Publishing BV, 2002).
4. T. Rogne, B. Nyhus, M. Svenning, H.I. Lange, O. Orjasaeter, T.E. Eggen, "Evaluation of Hydrogen Embrittlement of S13Cr Stainless Steels Based on SSR and CTOD Testing," CORROSION/2003, paper no. 534 (Houston, TX: NACE, 2003).
5. A. Griffiths, G. Hinds, A. Turnbull, Corrosion 61 (2005): p. 111.
6. NACE TMO198-98, "Slow Strain Rate Test Method for Screening Corrosion-Resistant Alloys (CRAs) for Stress Corrosion Cracking in Sour Oilfield Service" (Houston, TX: NACE, 1998).
7. A. Griffiths, W. Nimmo, B. Roebuck, G. Hinds, A. Turnbull, Mater. Sci. Eng. 384 (2004): p. 83.
8. C.H.L.J. Ten Horn, A. Bakker, R.W. Koers, J.T. Martin, J. Zuidema, "Cyclic Plastic Deformation of Pipeline Steel," Proc. ICF10, Advances in Fracture Processes, eds. K. Ravi-Chandler, B.L. Karihaloo, T. Kishi, R.O. Ritchie, A.T. Yokobori, Jr., T. Yokobori, paper no. ICF100398OR (Honolulu, HI, and Oxford, U.K.: Elsevier Science, 2001).