Low-bandgap donor/acceptor polymer blend solar cells with efficiency exceeding 4%

Advanced Energy Materials

Volumn 4, Issue 3, 2014, Pages

  Mori, Daisuke ^a   Benten, Hiroaki ^a   Okada, Izumi ^a   Ohkita, Hideo ^a   Ito, Shinzaburo ^a  

^a KYOTO UNIVERSITY   (Japan)

Author keywords

charge carrier mobility; energy transfer; photoluminescence quenching; polymer blend solar cells; polymer phase separation

Indexed keywords

EID: 84894499170     PISSN: 16146832     EISSN: 16146840     Source Type: Journal    
DOI: 10.1002/aenm.201301006     Document Type: Article

References (37)

1. R. Sφndergaard, M. Hösel, D. Angmo, T. T. Larsen-Olsen, F. C. Krebs, Mater. Today 2012, 15, 36.
2. M. T. Dang, L. Hirsch, G. Wantz, J. D. Wuest, Chem. Rev. 2013, 113, 3734.
3. G. Li, R. Zhu, Y. Yang, Nat. Photonics 2012, 6, 153.
4. C. J. Brabec, S. Gowrisanker, J. J. M. Halls, D. Laird, S. Jia, S. P. Williams, Adv. Mater. 2010, 22, 3839.
5. H. Ohkita, S. Ito, Polymer 2011, 52, 4397.
6. a) C. R. McNeill, Energy Environ. Sci. 2012, 5, 5653
7. b) C. R. McNeill, N. C. Greenham, Adv. Mater. 2009, 21, 3840.
8. D. Mori, H. Benten, H. Ohkita, S. Ito, K. Miyake, ACS Appl. Mater. Interfaces 2012, 4, 3325.
9. D. Mori, H. Benten, J. Kosaka, H. Ohkita, S. Ito, K. Miyake, ACS Appl. Mater. Interfaces 2011, 3, 2924.
10. E. Zhou, J. Cong, Q. Wei, K. Tajima, C. Yang, K. Hashimoto, Angew. Chem. Int. Ed. 2011, 50, 2799.
11. Z. He, C. Zhong, S. Su, M. Xu, H. Wu, Y. Cao, Nat. Photonics 2012, 6, 591.
12. C. R. McNeill, A. Abrusci, I. Hwang, M. A. Ruderer, P. Müller-Buschbaum, N. C. Greenham, Adv. Funct. Mater. 2009, 19, 3103.
13. X. Liu, S. Huettner, Z. Rong, M. Sommer, R. H. Friend, Adv. Mater. 2012, 24, 669.
14. M. Schubert, D. Dolfen, J. Frisch, S. Roland, R. Steyrleuthner, B. Stiller, Z. Chen, U. Scherf, N. Koch, A. Facchetti, D. Neher, Adv. Energy Mater. 2012, 2, 369.
15. a) H. Yan, B. A. Collins, E. Gann, C. Wang, H. Ade, C. R. McNeill, ACS Nano 2012, 6, 677
16. b) S. Swaraj, C. Wang, H. Yan, B. Watts, J. Lüning, C. R. McNeill, H. Ade, Nano Lett. 2010, 10, 2863.
17. C. R. McNeill, S. Westenhoff, C. Groves, R. H. Friend, N. C. Greenham, J. Phys. Chem. C 2007, 111, 19153.
18. R. C. Mulherin, S. Jung, S. Huettner, K. Johnson, P. Kohn, M. Sommer, S. Allard, U. Scherf, N. C. Greenham, Nano Lett. 2011, 11, 4846.
19. E. Wang, L. Hou, Z. Wang, S. Hellström, F. Zhang, O. Inganäs, M. R. Andersson, Adv. Mater. 2010, 22, 5240.
20. H. Yan, Z. Chen, Y. Zheng, C. Newman, J. R. Quinn, F. Dötz, M. Kastler, A. Facchetti, Nature 2009, 457, 679.
21. G. Dennler, M. C. Scharber, C. J. Brabec, Adv. Mater. 2009, 21, 1323.
22. T. W. Holcombe, J. E. Norton, J. Rivnay, C. H. Woo, L. Goris, C. Piliego, G. Griffini, A. Sellinger, J. L. Brédas, A. Salleo, J. M. J. Fréchet, J. Am. Chem. Soc. 2011, 133, 12106.
23. a) K. Feron, W. J. Belcher, C. J. Fell, P. C. Dastoor, Int. J. Mol. Sci. 2012, 13, 17019
24. b) S. R. Scully, P. B. Armstrong, C. Edder, J. M. J. Fréchet, M. D. McGehee, Adv. Mater. 2007, 19, 2961.
25. a) J. Nakamura, K. Murata, K. Takahashi, Appl. Phys. Lett. 2005, 87, 132105
26. b) L. J. A. Koster, V. D. Mihailetchi, M. Lenes, P. W. M. Blom, in Organic Photovoltaics: Materials, Device Physics, and Manufacturing Technologies, (Ed:, C. Brabec, V. Dyakonov, U. Scherf,), Wiley-VCH, Weinheim, Germany 2008, pp. 283.
27. Y. Shen, A. R. Hosseini, M. H. Wong, G. G. Malliaras, ChemPhysChem. 2004, 5, 16.
28. L. M. Andersson, Org. Electron. 2011, 12, 300.
29. R. Steyrleuthner, M. Schubert, F. Jaiser, J. C. Blakesley, Z. Chen, A. Facchetti, D. Neher, Adv. Mater. 2010, 22, 2799.
30. V. D. Mihailetchi, J. K. J. van Duren, P. W. M. Blom, J. C. Hummelen, R. A. J. Janssen, J. M. Kroon, M. T. Rispens, W. J. H. Verhees, M. M. Wienk, Adv. Funct. Mater. 2003, 13, 43.
31. J. K. J. van Duren, X. Yang, J. Loos, C. W. T. Bulle-Lieuwma, A. B. Sieval, J. C. Hummelen, R. A. J. Janssen, Adv. Funct. Mater. 2004, 14, 425.
32. L. M. Andersson, F. Zhang, O. Inganäs, Appl. Phys. Lett. 2007, 91, 071108.
33. S. Wakim, S. Beaupré, N. Blouin, B. Aich, S. Rodman, R. Gaudiana, Y. Tao, M. Leclerc, J. Mater. Chem. 2009, 19, 5351.
34. V. Shrotriya, G. Li, Y. Yao, T. Moriarty, K. Emery, Y. Yang, Adv. Funct. Mater. 2006, 16, 2016.
35. A. Cravino, P. Schilinsky, C. J. Brabec, Adv. Funct. Mater. 2007, 17, 3906.
36. G. J. A. H. Wetzelaer, M. Kuik, Y. Olivier, V. Lemaur, J. Cornil, S. Fabiano, M. A. Loi, P. W. M. Blom, Phys. Rev. B 2012, 86, 165203.
37. The LUMO energy of N2200 determined from cyclic voltammetry measurements performed on the polymer thin film was -3.91 eV:, Z. Chen, Y. Zheng, H. Yan, A. Facchetti, J. Am. Chem. Soc. 2009, 131, 8.