Impact of surface condition on sulphide stress corrosion cracking of 316L stainless steel

Corrosion Science

Volumn 71, Issue , 2013, Pages 43-52

  Hinds, G ^a   Wickstrom L ^a   Mingard, K ^a   Turnbull, A ^a  

^a NATIONAL PHYSICAL LABORATORY   (United Kingdom)

Author keywords

A. Stainless steel; C. Stress corrosion; C. Sulphide cracking; C. Welding

Indexed keywords

316 L STAINLESS STEEL; ELECTRON BACK SCATTER DIFFRACTION; FOCUSED ION BEAM MILLING; FOUR POINT BEND TESTS; FOUR-POINT BEND SPECIMEN; MECHANICAL DEFECTS; NANO-CRYSTALLINE LAYERS; STRESS CORROSION;

AUSTENITIC STAINLESS STEEL; DRILLING PLATFORMS; PITTING; RESIDUAL STRESSES; STRESS CORROSION CRACKING; STRESS MEASUREMENT; SURFACE DEFECTS; SURFACES; X RAY DIFFRACTION;

CRACKS;

EID: 84876304124     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2013.02.002     Document Type: Article

References (27)

1. Szklarska-Smialowska Z. Pitting Corrosion of Metals 1986, NACE Int, Houston.
2. Isaacs H.S., Kissel G. J. Electrochem. Soc. 1972, 119:1628-1632.
3. Burstein G.T., Pistorius P.C. Corrosion 1995, 51:380-385.
4. Moayed M.H., Laycock N.J., Newman R.C. Corros. Sci. 2003, 45:1203-1216.
5. Hong T., Nagano M. Corros. Sci. 1997, 39:1665-1672.
6. Jargelius-Pettersson R.F.A., Pires Duarte B., Duchamp G. Mater. Sci. For. 1998, 289-292:1029-1039.
7. Zuo Y., Wang H., Xiong J. Corros. Sci. 2002, 44:25-35.
8. Coates G.C. Mater. Perf. 1990, (August):61-65.
9. M.J. Olszta, L.E. Thomas, K. Asano, S. Ooki, S.M. Bruemmer, Crack initiation precursors originating from surface grinding, in: Proceedings of the 14th Int. Conf. on Environmental Degradation of Materials in Nuclear Power Systems, Virginia Beach, 2009 p. 549-561.
10. Scenini F., Newman R.C., Cottis R.A., Jacko R.J. Corrosion 2008, 64:824-834.
11. Lee W.-S., Lin C.-F. Mater. Sci. Eng. 2001, A308:124-135.
12. Y. Katayama, M. Tsubota, Y. Saito, Effect of the plastic strain level quantified by EBSP method on the stress corrosion cracking of L-grade stainless steels, in: Proceedings of the 12th International Conference on Environmental Degradation of Materials in Nuclear Power System - Water Reactors, The Minerals, Metals & Materials Society, 2005, p. 31-36.
13. M. Koshiishi, R. Obata, Z. Sagawa, H. Anzai, Effect of Surface Machining on SCC Susceptibility of L-Grade Stainless Steels, in: Workshop on Detection, Avoidance, Mechanisms, Modeling, and Prediction of Stress Corrosion Cracking Initiation in Water-Cooled Nuclear Plants, Beaune, 2008. (Appendix 7.3.).
14. Turnbull A., Mingard K., Lord J.D., Roebuck B., Tice D., Mottershead K., Fairweather N., Bradbury A. Corros. Sci. 2011, 53:3398-3415.
15. Lozano-Perez S., Yamada T., Terachi T., Schroder M., English C.A., Smith G.D.W., Grovenor C.R.M., Eyre B.L. Acta Mat. 2009, 57:5361-5381.
16. Ghosh S., Kain V. Mat. Sci. Eng. 2010, A527:679-683.
17. Ghosh S., Kain V. J. Nucl. Mat. 2010, 403:62-67.
18. Lu Z., Shoji T., Dan T., Qiu Y., Yonezawa T. Corros. Sci. 2010, 52:2547-2555.
19. American Welding Society Standard, ANSI/AWS D18.2:2009, Guide To Weld Discoloration Levels On Inside Of Austenitic Stainless Steel Tube, American Welding Society, Opa-Locka, FL, 2009.
20. ASTM Standard G61, 1986 (2009), Conducting Cyclic Potentiodynamic Polarization. Measurements for Localized Corrosion Susceptibility of Iron-, Nickel-, or Cobalt-Based Alloys, ASTM International, West Conshohocken, PA, 2003, http://www.astm.org.
21. M.E. Fitzpatrick, A.T. Fry, P. Holdway, F.A. Kandil, J. Shackleton, L. Suominen, Determination of residual stresses by X-ray diffraction, NPL Good Practice Guide No. 52, 2005.
22. P.V. Grant, J.D. Lord, P. Whitehead, The measurement of residual stresses by the incremental hole drilling technique - issue 2, NPL Good Practice Guide No. 53, 2006.
23. Randle V. Microtexture Determination and its Applications 2003, Institute of Materials/Maney Publishing, London. second ed.
24. Horner D.A., Connolly B.J., Zhou S., Crocker L., Turnbull A. Corros. Sci. 2011, 53:3466-3485.
25. EFC 17 Corrosion Resistant Alloys for Oil and Gas Production, European Federation of Corrosion 2006, Maney Publishing, US.
26. Fry A.D., Lord J.D. Powder Diffr. 2009, 24:S41-S44.
27. S.B. Mat, R.C. Newman, Local chemistry aspects of hydrogen sulphide assisted SCC of stainless steel, Corrosion/1994, Paper No. 228, 1994.