The effect of roll-processing orientation on stress corrosion cracking of warm-rolled 304L stainless steel in oxygenated and deoxygenated high temperature pure water

Corrosion Science

Volumn 52, Issue 8, 2010, Pages 2547-2555

  Lu, Zhanpeng ^a   Shoji, Tetsuo ^a   Dan, Tichun ^a,b   Qiu, Yubing ^a   Yonezawa, Toshio ^a  

^a TOHOKU UNIVERSITY   (Japan)

^b INSTITUTE OF GEOLOGY AND GEOPHYSICS   (China)

Author keywords

A. 304L stainless steel; C. Crack growth rate; C. High temperature water; C. Rolling orientation; C. Stress corrosion cracking; C. Warm roll hardening

Indexed keywords

304L STAINLESS STEEL; C. HIGH TEMPERATURE WATER; C. ROLLING ORIENTATION; C. STRESS CORROSION CRACKING; CRACK GROWTH RATES; HIGH-TEMPERATURE WATER;

CORROSION RESISTANT ALLOYS; CRACKING (CHEMICAL); CRACKS; GROWTH RATE; HARDENING; RESIDUAL STRESSES; STRESS CORROSION CRACKING; TEXTURES;

STAINLESS STEEL;

EID: 77954816185     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2010.03.027     Document Type: Article

References (27)

1. Jones R.L., Gordon G.M., Neils G.H. Environmental degradation of materials in boiling water reactors. Proc. Fourth Int. Symp. Environ. Degradation of Materials in Nuclear Power Systems-Water Reactors 1989, 1-10. New Port Beach, CA.
2. Andresen P.L., Ford F.P. Mater. Sci. Eng. A 1988, 103:167-184.
3. T. Shoji, Progress in the mechanistic understanding of BWR SCC and its implication to the prediction of SCC growth behavior in plants, in: Proc. 11th Int. Symp. Environ. Degradation of Materials in Nuclear Power Systems-Water Reactors, held August 10-14, 2003, Skamania, Stevenson, Washington, ANS, 2003, pp. 588-598.
4. Suzuki S., Kumagayi K., Shitara C., Mizutani J., Sakashita A., Tohkuma H., Yamashita H. Maintenology 2004, 3:65-70.
5. T.M. Angeliu, P.L. Andresen, E. Hall, J.A. Sutliff, S. Sitzman, R.M. Horn, Intergranular stress corrosion cracking of unsensitized stainless steels in BWR environments, in: F.P. Ford, S.M. Bruemmer, G.S. Was (Eds.), Proc. Ninth Int. Symp. Environ. Degradation of Materials Nuclear Power Systems-Water Reactors, TMS, 1999, pp. 311-317.
6. NISA, Documents Presented at Fifth Structural Integrity Evaluation Committee, Feb. 18, 2003.
7. U. Ehrnstén, H. Hänninen, P. Aaltonen, C. Jansson, P. Nenonen, T. Angeliu, Intergranular cracking of AISI 316NG stainless steel in BWR environment, in: Prof. 10th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, 2001, NACE, CDROM.
8. Andresen P.L., Morra M.M. J. Nucl. Mater. 2008, 383:97-111.
9. T. Shoji, G.F. Li, J.H. Kwon, S. Matsushima, Z.P. Lu, Quantification of yield strength effects on IGSCC of austenitic stainless steels in high temperature waters, in: Proc. 11th Int. Symp. Environ. Degradation of Materials in Nuclear Power Systems-Water Reactors, August 10-14, 2003, Skamania, Stevenson, Washington, ANS, 2003, pp. 834-843.
10. M.L. Castaño Marín, M.S. García Redondo, G. de Diego Velasco, D. Gómez Briceño. Crack growth rate of hardened austenitic stainless steels in BWR and PWR environments, in: Proc. 11th Int. Symp. Environ. Degradation of Materials in Nuclear Power Systems-Water Reactors, August 10-14, 2003, Skamania, Stevenson, Washington, ANS, 2003, pp. 845-854.
11. P.L. Andresen, T.M. Angeliu, L.M. Young, Effect of Martensite and hydrogen on SCC of stainless steels and alloy 600, Corrosion/2001, Paper No.228, 2001.
12. Lu Z.P., Shoji T., Takeda Y., Kai A., Ito Y. Corrosion 2007, 63:1021-1032.
13. Lu Z.P., Shoji T., Takeda Y., Ito Y., Yamazaki S. Corros. Sci. 2008, 50:698-712.
14. Lu Z.P., Shoji T., Takeda Y., Ito Y., Kai A., Yamazaki S. Corros. Sci. 2008, 50:561-575.
15. T. Shoji, Z.P. Lu, Y. Takeda, H. Murakami and C.Y. Fu, Deterministic prediction of stress corrosion crack growth rates in high temperature water by combination of interface oxidation kinetics and crack tip asymptotic field, 2008 ASME Pressure Vessels and Piping Division Conference (ASME PVP 2008), ASME 2008, PVP2008-61417.
16. T. Shoji, Z. P. Lu, N.K. Das, H. Murakami, Y. Takeda, T. Ismail, Modeling stress corrosion crack growth rates based upon the effect of stress/strain on crack tip interface degradation and oxidation reaction kinetics, in: 2009 ASME Pressure Vessels and Piping Division Conference (ASME PVP 2009), ASME, 2009, PVP2009-77615.
17. Shoji T., Lu Z.P., Murakami H. Corros. Sci. 2010, 52:769-779.
18. M. Ando, K. Nakata, M. Itow, N. Tanaka, M. Koshiishi, R. Obata, Y. Miwa, Y. Kaji, M. Hayakawa, CGR behavior of low carbon stainless steel of hardened heat affected zone in PLR piping weld joints, in: Proc. 13th Int. Symp. Environ. Degradation of Mater. Nuclear Power Systems-Water Reactors, CNS, 2007, CDROM.
19. Lu Z.P., Shoji T., Takeda Y., Ito Y., Kai A. N. Tsuchiya. Corros. Sci. 2008, 50:625-638.
20. Arioka K., Yamada T., Terachi T. Corrosion 2006, 62:568-575.
21. P.L. Andresen, M. Morra, K. Ahluwalia, J. Hickling, J. Wilson, Effect of deformation and orientation on SCC of Alloy 690, Corrosion/2009, Paper No. 412, NACE, 2009.
22. Moshier W.C., Brown C.M. Corrosion 2000, 56:307-320.
23. Terachi T., Yamada T., Chiba G., Arioka K. Stress corrosion cracking of stainless steel under deoxygenated high-temperature water-influence of cold work and processing orientation. INSS J. 2006, 179-193.
24. OIM Analysis for Windows, User Manual, TexSEM Laboratories, Inc., Utah, USA, 2005.
25. Kumar B.R., Mahato B., Bandyopadhyay N.R., Bhattacharya D.K. Mat. Sci. Eng. A 2005, 394:296-301.
26. Arioka K., Yamada T., Terachi T., Miyamoto T. Corrosion 2008, 64:691-706.
27. Lozano-Perez S., Yamada T., Terachi T., Schroder M., English C.A., Smith G.D.W., Grovenor C.R.M., Eyre B.L. Acta Mater. 2009, 57:5361-5381.