Volumn 53, Issue 11, 2011, Pages 3466-3485

Novel images of the evolution of stress corrosion cracks from corrosion pits

Author keywords

A. Low alloy steel; C. Pitting corrosion; C. Stress Corrosion

Indexed keywords

A. LOW ALLOY STEEL; C. STRESS CORROSION; CORROSION PITS; CRACK NUCLEATION; MICROTOMOGRAPHIC IMAGES; PIT WALLS; PIT-TO-CRACK TRANSITIONS; STRESS CORROSION CRACK; TURBINE DISC;

EID: 80052337631     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2011.05.050     Document Type: Article
Times cited : (197)

References (52)
  • 1
    • 0007334007 scopus 로고
    • Pitting and its effect on the fatigue limit of steels corroded under various conditions
    • McAdam D.J., Geil G.W. Pitting and its effect on the fatigue limit of steels corroded under various conditions. J. Proc. Am. Soc. Test. Mater. 1928, 41:696-732.
    • (1928) J. Proc. Am. Soc. Test. Mater. , vol.41 , pp. 696-732
    • McAdam, D.J.1    Geil, G.W.2
  • 2
    • 0042798893 scopus 로고
    • Corrosion-fatigue crack initiation in metals
    • Patel C., Pyle T., Rollins V. Corrosion-fatigue crack initiation in metals. Nature 1977, 266:517-518.
    • (1977) Nature , vol.266 , pp. 517-518
    • Patel, C.1    Pyle, T.2    Rollins, V.3
  • 4
    • 80052340927 scopus 로고
    • Corrosion fatigue crack initiation and propagation behaviour of 12 Cr stainless steel
    • Pergamon Press, Oxford
    • Ebara R., Yamada T., Kobayashi T., Kawano H. Corrosion fatigue crack initiation and propagation behaviour of 12 Cr stainless steel. Mechanical Behaviour of Materials VI 1992, Pergamon Press, Oxford.
    • (1992) Mechanical Behaviour of Materials VI
    • Ebara, R.1    Yamada, T.2    Kobayashi, T.3    Kawano, H.4
  • 5
    • 0016059328 scopus 로고
    • The effect of mean stress and environment on corrosion fatigue behavior of 7075-T6 aluminium
    • Corsetti L.V., Duquette D.J. The effect of mean stress and environment on corrosion fatigue behavior of 7075-T6 aluminium. Metall. Trans. 1974, 5:1087-1093.
    • (1974) Metall. Trans. , vol.5 , pp. 1087-1093
    • Corsetti, L.V.1    Duquette, D.J.2
  • 6
    • 0018690793 scopus 로고
    • Model for prediction of fatigue lives based upon a pitting corrosion fatigue process
    • ASTM, Philadelphia
    • Hoeppner D.W. Model for prediction of fatigue lives based upon a pitting corrosion fatigue process. Fatigue Mechanisms (STP 675) 1979, ASTM, Philadelphia.
    • (1979) Fatigue Mechanisms (STP 675)
    • Hoeppner, D.W.1
  • 7
    • 0020114479 scopus 로고
    • Theoretical considerations on corrosion fatigue crack initiation
    • Muller M. Theoretical considerations on corrosion fatigue crack initiation. Metall. Trans. 1982, 13A:649-655.
    • (1982) Metall. Trans. , vol.13 A , pp. 649-655
    • Muller, M.1
  • 8
    • 0024301935 scopus 로고
    • Prediction of fatigue crack initiation life based on pit growth
    • Kondo Y. Prediction of fatigue crack initiation life based on pit growth. Corrosion 1989, 45:7-11.
    • (1989) Corrosion , vol.45 , pp. 7-11
    • Kondo, Y.1
  • 9
  • 10
    • 0022188419 scopus 로고
    • Considerations of allowable stress of corrosion fatigue
    • Kawai S., Kasai K. Considerations of allowable stress of corrosion fatigue. Fatigue Fract. Eng. Mater. Struct. 1985, 8:115-127.
    • (1985) Fatigue Fract. Eng. Mater. Struct. , vol.8 , pp. 115-127
    • Kawai, S.1    Kasai, K.2
  • 11
    • 44649100147 scopus 로고    scopus 로고
    • Current understanding of environment-induced cracking of steam turbine steels
    • Turnbull A. Current understanding of environment-induced cracking of steam turbine steels. Corrosion 2008, 64:420-438.
    • (2008) Corrosion , vol.64 , pp. 420-438
    • Turnbull, A.1
  • 12
    • 1642488893 scopus 로고    scopus 로고
    • Pit to crack transition in stress corrosion cracking of a steam turbine disc steel
    • Turnbull A., Zhou S. Pit to crack transition in stress corrosion cracking of a steam turbine disc steel. Corros. Sci. 2004, 46:1239-1264.
    • (2004) Corros. Sci. , vol.46 , pp. 1239-1264
    • Turnbull, A.1    Zhou, S.2
  • 13
    • 0031270621 scopus 로고    scopus 로고
    • Prediction of failures of low-pressure steam turbine disks
    • Liu C., Macdonald D.D. Prediction of failures of low-pressure steam turbine disks. J. Press. Vessel Technol. Trans. ASME 1997, 119:393-400.
    • (1997) J. Press. Vessel Technol. Trans. ASME , vol.119 , pp. 393-400
    • Liu, C.1    Macdonald, D.D.2
  • 14
    • 28544438825 scopus 로고    scopus 로고
    • Modelling of the evolution of stress corrosion cracks from corrosion pits
    • Turnbull A., McCartney L.N., Zhou S. Modelling of the evolution of stress corrosion cracks from corrosion pits. Scripta Mater. 2006, 54:575-578.
    • (2006) Scripta Mater. , vol.54 , pp. 575-578
    • Turnbull, A.1    McCartney, L.N.2    Zhou, S.3
  • 15
    • 33746218004 scopus 로고    scopus 로고
    • A model to predict the evolution of pitting corrosion and the pit-to-crack transition incorporating statistically distributed input parameters
    • Turnbull A., McCartney L.N., Zhou S. A model to predict the evolution of pitting corrosion and the pit-to-crack transition incorporating statistically distributed input parameters. Corros. Sci. 2006, 48:2084-2105.
    • (2006) Corros. Sci. , vol.48 , pp. 2084-2105
    • Turnbull, A.1    McCartney, L.N.2    Zhou, S.3
  • 16
    • 11344292645 scopus 로고    scopus 로고
    • Unification of the deterministic and statistical approaches for predicting localized corrosion damage. I. Theoretical foundation
    • Engelhardt G., Macdonald D.D. Unification of the deterministic and statistical approaches for predicting localized corrosion damage. I. Theoretical foundation. Corros. Sci. 2004, 46:2755-2780.
    • (2004) Corros. Sci. , vol.46 , pp. 2755-2780
    • Engelhardt, G.1    Macdonald, D.D.2
  • 17
    • 28544442483 scopus 로고    scopus 로고
    • Deterministic prediction of corrosion damage in low pressure steam turbines
    • Engelhardt G., Macdonald D.D., Zhang Y., Dooley B. Deterministic prediction of corrosion damage in low pressure steam turbines. Power Plant Chem. 2004, 6:647-661.
    • (2004) Power Plant Chem. , vol.6 , pp. 647-661
    • Engelhardt, G.1    Macdonald, D.D.2    Zhang, Y.3    Dooley, B.4
  • 18
    • 33845709026 scopus 로고    scopus 로고
    • Technical note: visualization of stress corrosion cracks emerging from pits
    • Turnbull A., Zhou S., Orkney L., McCormick N. Technical note: visualization of stress corrosion cracks emerging from pits. Corrosion 2006, 62:555-558.
    • (2006) Corrosion , vol.62 , pp. 555-558
    • Turnbull, A.1    Zhou, S.2    Orkney, L.3    McCormick, N.4
  • 20
    • 0033328617 scopus 로고    scopus 로고
    • X-ray microtomography of materials
    • Stock S.R. X-ray microtomography of materials. Int. Mater. Rev. 1999, 44:141-164.
    • (1999) Int. Mater. Rev. , vol.44 , pp. 141-164
    • Stock, S.R.1
  • 21
    • 44649173773 scopus 로고    scopus 로고
    • Recent advances in X-ray microtomography applied to materials
    • Stock S.R. Recent advances in X-ray microtomography applied to materials. Int. Mater. Rev. 2008, 53:129-181.
    • (2008) Int. Mater. Rev. , vol.53 , pp. 129-181
    • Stock, S.R.1
  • 23
    • 0031818083 scopus 로고    scopus 로고
    • Desktop X-ray microscopy and microtomography
    • Sasov A., Van Dyck D. Desktop X-ray microscopy and microtomography. J. Microsc. Oxf. 1998, 191:151-158.
    • (1998) J. Microsc. Oxf. , vol.191 , pp. 151-158
    • Sasov, A.1    Van Dyck, D.2
  • 28
    • 47749134845 scopus 로고    scopus 로고
    • Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal
    • King A., Johnson G., Engelberg D., Ludwig W., Marrow T.J. Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal. Science 2008, 321:382-385.
    • (2008) Science , vol.321 , pp. 382-385
    • King, A.1    Johnson, G.2    Engelberg, D.3    Ludwig, W.4    Marrow, T.J.5
  • 29
    • 33749573475 scopus 로고    scopus 로고
    • X-ray microtomographic observation of intergranular stress corrosion cracking in sensitized austenitic stainless steel
    • Babout L., Marrow T.J., Engelberg D., Withers P.J. X-ray microtomographic observation of intergranular stress corrosion cracking in sensitized austenitic stainless steel. Mater. Sci. Technol. 2006, 22:1068-1075.
    • (2006) Mater. Sci. Technol. , vol.22 , pp. 1068-1075
    • Babout, L.1    Marrow, T.J.2    Engelberg, D.3    Withers, P.J.4
  • 30
    • 0031139751 scopus 로고    scopus 로고
    • Direct observation of crack opening as a function of applied load in the interior of a notched tensile sample of Al-Li 2090
    • Guvenilir A., Breunig T.M., Kinney J.H., Stock S.R. Direct observation of crack opening as a function of applied load in the interior of a notched tensile sample of Al-Li 2090. Acta Mater. 1997, 45:1977-1987.
    • (1997) Acta Mater. , vol.45 , pp. 1977-1987
    • Guvenilir, A.1    Breunig, T.M.2    Kinney, J.H.3    Stock, S.R.4
  • 31
    • 0032050148 scopus 로고    scopus 로고
    • High resolution computed tomography and implications for fatigue crack closure modelling
    • Guvenilir A., Stock S.R. High resolution computed tomography and implications for fatigue crack closure modelling. Fatigue Fract. Eng. Mater. Struct. 1998, 21:439-450.
    • (1998) Fatigue Fract. Eng. Mater. Struct. , vol.21 , pp. 439-450
    • Guvenilir, A.1    Stock, S.R.2
  • 33
    • 1842865096 scopus 로고    scopus 로고
    • High resolution X-ray tomography of short fatigue crack nucleation in austempered ductile cast iron
    • Marrow T.J., Buffiere J.-Y., Withers P.J., Johnson G., Engelberg D. High resolution X-ray tomography of short fatigue crack nucleation in austempered ductile cast iron. Int. J. Fatigue 2004, 26:717-725.
    • (2004) Int. J. Fatigue , vol.26 , pp. 717-725
    • Marrow, T.J.1    Buffiere, J.-Y.2    Withers, P.J.3    Johnson, G.4    Engelberg, D.5
  • 34
    • 27144432834 scopus 로고    scopus 로고
    • 3-D characterization of the nucleation of a short fatigue crack at a pore in a cast Al alloy using high resolution synchrotron microtomography
    • Ferrie E., Buffiere J.-Y., Ludwig W. 3-D characterization of the nucleation of a short fatigue crack at a pore in a cast Al alloy using high resolution synchrotron microtomography. Int. J. Fatigue 2005, 27:1215-1220.
    • (2005) Int. J. Fatigue , vol.27 , pp. 1215-1220
    • Ferrie, E.1    Buffiere, J.-Y.2    Ludwig, W.3
  • 35
    • 1242351775 scopus 로고    scopus 로고
    • A 3-D measurement procedure for internal local crack driving forces via synchrotron X-ray microtomography
    • Toda H., Sinclair I., Buffière J.-Y., Maire E., Khor K.H., Gregson P., Kobayashi T. A 3-D measurement procedure for internal local crack driving forces via synchrotron X-ray microtomography. Acta Mater. 2004, 52:1305-1317.
    • (2004) Acta Mater. , vol.52 , pp. 1305-1317
    • Toda, H.1    Sinclair, I.2    Buffière, J.-Y.3    Maire, E.4    Khor, K.H.5    Gregson, P.6    Kobayashi, T.7
  • 36
    • 31044443178 scopus 로고    scopus 로고
    • Fatigue crack propagation: in situ visualization using X-ray microtomography and 3-D simulation using the extended finite element method
    • Ferrie E., Buffiere J.-Y., Ludwig W., Gravouil A., Edwards L. Fatigue crack propagation: in situ visualization using X-ray microtomography and 3-D simulation using the extended finite element method. Acta Mater. 2006, 54:1111-1122.
    • (2006) Acta Mater. , vol.54 , pp. 1111-1122
    • Ferrie, E.1    Buffiere, J.-Y.2    Ludwig, W.3    Gravouil, A.4    Edwards, L.5
  • 37
    • 80052332586 scopus 로고    scopus 로고
    • ASTM Standard, E 8, 2000, Standard test methods for tension testing of metallic materials, West Conshohocken, PA: ASTM International.
    • ASTM Standard, E 8, 2000, Standard test methods for tension testing of metallic materials, West Conshohocken, PA: ASTM International.
    • (2000)
  • 38
    • 80052316746 scopus 로고    scopus 로고
    • SkyScan 1072. Desktop X-ray microtomograph instruction manual. Skyscan n.v., Vluchtenburgstraat 3, 2630 Aartselaar, Belgium.
    • SkyScan 1072. Desktop X-ray microtomograph instruction manual. Skyscan n.v., Vluchtenburgstraat 3, 2630 Aartselaar, Belgium. 2001. p. 11, 32.
    • (2001) , pp. 32
  • 39
    • 80052325968 scopus 로고    scopus 로고
    • Finite element analysis of the stress and strain associated with a corrosion pit in a cylindrical specimen under applied tensile load, NPL Report DEPC-MPE 034,
    • A. Turnbull, L. Crocker, Finite element analysis of the stress and strain associated with a corrosion pit in a cylindrical specimen under applied tensile load, NPL Report DEPC-MPE 034, 2006.
    • (2006)
    • Turnbull, A.1    Crocker, L.2
  • 40
    • 0024865640 scopus 로고
    • The significance of the local electrode potential within pits, crevices and cracks
    • Pickering H.W. The significance of the local electrode potential within pits, crevices and cracks. Corros. Sci. 1989, 29:325-341.
    • (1989) Corros. Sci. , vol.29 , pp. 325-341
    • Pickering, H.W.1
  • 42
    • 0018294868 scopus 로고
    • The influence of stress on the pitting susceptibility of a 12% CrMoV martensitic stainless steel
    • Chastell D., Doig P., Flewitt P.E.J., Ryan K. The influence of stress on the pitting susceptibility of a 12% CrMoV martensitic stainless steel. Corros. Sci. 1979, 19:335-341.
    • (1979) Corros. Sci. , vol.19 , pp. 335-341
    • Chastell, D.1    Doig, P.2    Flewitt, P.E.J.3    Ryan, K.4
  • 43
    • 0000480775 scopus 로고    scopus 로고
    • Pit initiation on stainless steels in 1M NaCl with and without mechanical stress
    • Suter T., Webb E.G., Bohni H., Alkire R.C. Pit initiation on stainless steels in 1M NaCl with and without mechanical stress. J. Electrochem. Soc. 2001, 148:B174-B185.
    • (2001) J. Electrochem. Soc. , vol.148
    • Suter, T.1    Webb, E.G.2    Bohni, H.3    Alkire, R.C.4
  • 44
    • 0025198228 scopus 로고
    • Relationships between pitting, stress, and stress corrosion cracking of line pipe steels
    • Christman T.K. Relationships between pitting, stress, and stress corrosion cracking of line pipe steels. Corrosion 1990, 46:450-453.
    • (1990) Corrosion , vol.46 , pp. 450-453
    • Christman, T.K.1
  • 45
    • 80052313580 scopus 로고
    • The role of crevices in comparison to pits in initiating stress corrosion cracks of type 310S steel in different concentrations of MgCl2 solutions at 80°C. Corrosion cracking, in: Proceedings from the International Conference and Exposition on Fatigue, Corrosion Cracking, Fracture Mechanics, and Failure, ASM, Metals Park, OH,
    • S. Tsujikawa, T. Shinohara, Y. Hisamatsu, The role of crevices in comparison to pits in initiating stress corrosion cracks of type 310S steel in different concentrations of MgCl2 solutions at 80°C. Corrosion cracking, in: Proceedings from the International Conference and Exposition on Fatigue, Corrosion Cracking, Fracture Mechanics, and Failure, ASM, Metals Park, OH, 1986.
    • (1986)
    • Tsujikawa, S.1    Shinohara, T.2    Hisamatsu, Y.3
  • 46
    • 0008916232 scopus 로고
    • Predictions and experimental verification of the slip dissolution model for stress corrosion cracking of low strength alloys
    • NACE, Unieux-Firminy, France
    • Staehle R.W. Predictions and experimental verification of the slip dissolution model for stress corrosion cracking of low strength alloys. Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys 1973, NACE, Unieux-Firminy, France.
    • (1973) Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys
    • Staehle, R.W.1
  • 47
    • 77249091636 scopus 로고    scopus 로고
    • New insight into the pit-to-crack transition from finite element analysis of the stress and strain distribution around a corrosion pit
    • Turnbull A., Wright L., Crocker L. New insight into the pit-to-crack transition from finite element analysis of the stress and strain distribution around a corrosion pit. Corros. Sci. 2010, 52:1492-1498.
    • (2010) Corros. Sci. , vol.52 , pp. 1492-1498
    • Turnbull, A.1    Wright, L.2    Crocker, L.3
  • 49
    • 0036568097 scopus 로고    scopus 로고
    • Pit growth studies in stainless steel foils. I. Introduction and pit growth kinetics
    • Ernst P., Newman R.C. Pit growth studies in stainless steel foils. I. Introduction and pit growth kinetics. Corros. Sci. 2002, 44:927-941.
    • (2002) Corros. Sci. , vol.44 , pp. 927-941
    • Ernst, P.1    Newman, R.C.2
  • 50
    • 0036568081 scopus 로고    scopus 로고
    • Pit growth studies in stainless steel foils. II. Effect of temperature, chloride concentration and sulphate addition
    • Ernst P., Newman R.C. Pit growth studies in stainless steel foils. II. Effect of temperature, chloride concentration and sulphate addition. Corros. Sci. 2002, 44:943-954.
    • (2002) Corros. Sci. , vol.44 , pp. 943-954
    • Ernst, P.1    Newman, R.C.2
  • 52
    • 33744913773 scopus 로고    scopus 로고
    • Analysis of the stress intensity factor around corrosion pits developed on structures subjected to mixed loading
    • Acuna N., Gonzalez-Sanchez J., Ku-Basulto G., Dominquez L. Analysis of the stress intensity factor around corrosion pits developed on structures subjected to mixed loading. Scripta Mater. 2006, 55:363-366.
    • (2006) Scripta Mater. , vol.55 , pp. 363-366
    • Acuna, N.1    Gonzalez-Sanchez, J.2    Ku-Basulto, G.3    Dominquez, L.4


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.