Effects of MgO-based expansive additive on compensating the shrinkage of cement paste under non-wet curing conditions

Cement and Concrete Composites

Volumn 34, Issue 3, 2012, Pages 377-383

  Mo, L ^a   Deng, M ^a   Wang, A ^a,b  

^a NANJING TECH UNIVERSITY   (China)

^b ANHUI JIANZHU UNIVERSITY   (China)

Author keywords

Cement pastes; Expansive additive; MgO; Non wet curing condition; Shrinkage

Indexed keywords

AUTOGENOUS SHRINKAGE; CEMENT BASED MATERIAL; CEMENT PASTE; CURING CONDITION; DRYING SHRINKAGES; EARLY AGE; ETTRINGITES; FLY ASH CEMENT PASTE; MGO; MICROSTRUCTURE ANALYSIS; MOISTURE EXCHANGE; NON-WET CURING CONDITION; SCANNING ELECTRON MICROSCOPE; THERMAL SHRINKAGE; WATER-TO-CEMENT RATIOS; WET CURING;

CEMENT ADDITIVES; EXPANSION; FLY ASH; SCANNING ELECTRON MICROSCOPY; SHRINKAGE; WATER SUPPLY;

CURING;

EID: 84856210102     PISSN: 09589465     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.cemconcomp.2011.11.018     Document Type: Article

References (23)

1. D.P. Bentz, and O.M. Jensen Mitigation strategies for autogenous shrinkage cracking Cem Concr Compos 26 6 2004 677 685
2. M. Sahmaran, M. Lachemi, K.M.A. Hossain, and V.C. Li Internal curing of engineered cementitious composites for prevention of early age autogenous shrinkage cracking Cem Concr Res 39 10 2009 893 901
3. D. Cusson, and T. Hoogeveen Internal curing of high-performance concrete with pre-soaked fine lightweight aggregate for prevention of autogenous shrinkage cracking Cem Concr Res 38 6 2008 757 765
4. O.M. Jensen, and P.F. Hansen Water-entrained cement-based materials: 1. Principle and theoretical background Cem Concr Res 31 4 2001 647 654 (Pubitemid 32457414)
5. B. Akcay, and M.A. Tasdemir Effects of distribution of lightweight aggregates on internal curing of concrete Cem Concr Compos 32 8 2010 611 616
6. S. Zhutovsky, K. Kovler, and A. Bentur Influence of cement paste matrix properties on the autogenous curing of high-performance concrete Cem Concr Compos 26 5 2004 499 507
7. A. Bentur, S. Igarashi, and K. Kovler Prevention of autogenous shrinkage in high-strength concrete by internal curing using wet lightweight aggregates Cem Concr Res 31 11 2001 1587 1591 (Pubitemid 33149317)
8. D.P. Bentz, M.R. Geiker, and K.K. Hansen Shrinkage-reducing admixtures and early-age desiccation in cement pastes and mortars Cem Concr Res 31 2001 1075 1085 (Pubitemid 32698364)
9. J. Saliba, E. Rozire, F. Grondin, and A. Loukili Influence of shrinkage-reducing admixtures on plastic and long-term shrinkage Cem Concr Compos 33 2 2011 209 217
10. M.S. Meddah, M. Suzuki, and R. Sato Influence of a combination of expansive and shrinkage-reducing admixture on autogenous deformation and self-stress of silica fume high-performance concrete Constr Build Mater 25 1 2011 239 250
11. M. Collepardi, A. Borsoi, S. Collepardi, J.J. Ogoumah Olagot, and R. Troli Effects of shrinkage reducing admixture in shrinkage compensating concrete under non-wet curing conditions Cem Concr Compos 27 6 2005 704 708 (Pubitemid 40556506)
12. S. Nagataki, and H. Gomi Expansive admixtures (mainly ettringite) Cem Concr Compos 20 2-3 1998 163 170 (Pubitemid 128401508)
13. ASTM C845-96. Standard specification for expansive hydraulic cement.
14. Z. Liu, X. Cui, and M. Tang MgO-type delayed expansive cement Cem Concr Res 21 6 1991 1049 1057 (Pubitemid 21718091)
15. J. Gajda, and M. Vangeem Controlling temperatures in mass concrete Concr Int 24 1 2002 59 62
16. Z. Cao, and J. Xu Technique of MgO concrete used in dam constrction 2003 Chinese Electric Power Press Beijing [in Chinese]
17. Mehta PK, Pirtz D, Komandant GJ. Magnesium oxide additive for producing selfstress in mass concrete. In: Proceedings of 7th international congress on the chemistry of cement, vol. III, Paris; 1980. p. 6-9.
18. L. Xu, and M. Deng Dolomite used as raw material to produce MgO-based expansive agent Cem Concr Res 35 8 2005 1480 1485
19. L. Mo, M. Deng, and M. Tang Effects of calcination condition on expansion property of MgO-type expansive agent used in cement-based materials Cem Concr Res 40 3 2010 437 447
20. K.O. Kjellsen, A. Monsoy, K. Isachsen, and R.J. Detwiler Preparation of flat-polished specimens for SEM-backscattered electron imaging and X-ray microanalysis - importance of epoxy impregnation Cem Concr Res 33 4 2003 611 616
21. M. Deng, X. Cui, and M. Tang Expansion mechanism of magnesia in cement J Nanjing Inst Chem Technol 12 4 1990 1 11 [in Chinese]
22. Zhao X. Properties of MgO-based expansive additive used in RCC of Longtan hydropower station. Master dissertation, Nanjing, Nanjing University of Technology; 2004 [in Chinese].
23. S. Chatterji Mechanism of expansion of concrete due to the presence of dead-burnt CaO and MgO Cem Concr Res 25 1 1995 51 56