Effects of calcination condition on expansion property of MgO-type expansive agent used in cement-based materials

Cement and Concrete Research

Volumn 40, Issue 3, 2010, Pages 437-446

  Mo, Liwu ^a   Deng, Min ^a   Tang, Mingshu ^a  

^a NANJING TECH UNIVERSITY   (China)

Author keywords

(A) Hydration; (A) Temperature; (B) Microstructure; (C) Expansion; (D) MgO

Indexed keywords

(A) HYDRATION; (A) TEMPERATURE; (B) MICROSTRUCTURE; (C) EXPANSION; CALCINATION CONDITIONS; CEMENT BASED MATERIAL; CRYSTAL SIZE; EARLY AGE; EXPANSION PROPERTIES; EXPANSIVE AGENTS; HIGHER TEMPERATURES; HYDRATION ACTIVITY; INTRINSIC EFFECTS; INTRINSIC FACTORS; RESIDENCE TIME;

CALCINATION; CEMENTS; HYDRATION; MICROSTRUCTURE;

EXPANSION;

EID: 73949149884     PISSN: 00088846     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.cemconres.2009.09.025     Document Type: Article

References (23)

1. Bentz D.P., and Jensen O.M. Mitigation strategies for autogenous shrinkage cracking. Cem. Concr. Compos. 26 (2004) 677-685
2. Nagataki S., and Gomi H. Expansive admixtures. Cem. Concr. Compos. 21 11 (1998) 163-170
3. Frederick R.K., Bentley C.L., Walker W.W., and Holland J.A. Shrinkage-compensating concrete pavements perform well. Concr. Int. 1 (2006) 47-51
4. Yan P., Zheng F., et al. Relationship between delayed ettringite formation and delayed expansion in massive shrinkage-compensating concrete[J]. Cem. Concr. Compos. 26 (2004) 687-693
5. Yan P., and Qin X. The effect of expansive agent and possibility of delayed ettringite formation in shrinkage-compensating massive concrete[J]. Cem. Concr. Res. 31 (2001) 335-337
6. Mehta P.K. History and status of performance tests for evaluation of soundness of cements. Cement standards-Evolution and Trends. Am Soc Test Mater vol. 663 (1978), ASTM STP
7. th Int Congr Chem Cem. VO. III Paris (1980) v6-v9
8. Cao Z., and Xu J. Dam construction technology using MgO concrete (2003), China Electric Power Press, Beijing
9. X. Wang, Hydration and Expansion of MgO and the Preparation and Performance of the Novel MgO - type Expansive Agent, PhD thesis, Nanjing, 2002.
10. Xu L., and Deng M. Dolomite used as raw material to produce MgO-based expansive agent[J]. Cem. Concr. Res. 35 (2005) 1480-1485
11. Chatterji S. Mechanism of expansion of concrete due to the presence of dead-burnt CaO and MgO[J]. Cem. Concr. Res. 25 1 (1995) 51-56
12. Deng M., Hong D., Lan X., and Tang M. Mechanism of expansion in hardened cement pastes with dead-burnt free lime. Cem. Concr. Res. 25 2 (1995) 440-448
13. Deng M., Cui X., Liu Y., and Tang M. Expansive mechnismof magnesia as an additive of cement. J. Nanjing Inst. Chem. Technol. 12 4 (1990) 1-11
14. Suryanarayana C., and Grant Norton M. X-ray diffraction - a practical approach (1998), Plenum Press, New York 212 pp
15. GB/T 208-94, Standard test method for cement density [S], 1994.
16. Kjellsen K.O., Monsφ{symbol}y A., Isachsen K., and Detwiler R.J. Preparation of flat-polished specimens for SEM-backscattered electron imaging and X-ray microanalysis - importance of epoxy impregnation. Cem. Concr. Res. 33 4 (2003) 611-616
17. Kleiman S., and Chaim R. Thermal stability of MgO nanoparticles. Mater. Lett. 61 (2007) 4489-4491
18. Sun W., Cui C., Zhang H., and Cui K. Relationship between crystalline size and lattice distortion of MgO and its activity. J. Wuhan Univ. Technol. 13 4 (1991) 21-24
19. Wogelius R.A., Refson K., Fraser D.G., Grime G.W., and Goff J.P. Periclase surface hydroxylation during dissolution. Geochim. Cosmochim. Acta 59 9 (1995) 1875-1881
20. Lv J., Qiu L., and Qu B. Controlled growth of three morphological structures of magnesium hydroxide nanoparticles by wet precipitation method[J]. J. Cryst. Growth 267 (2004) 676-684
21. Salomão R., Bittencourt L.R.M., and Pandolfelli V.C. A novel approach for magnesia hydration assessment in fractory castables[J]. Ceram. Int. 33 (2007) 803-810
22. Kitamura A., Onizuka K., and Tanaka K. Hydration characteristics of magnesia [J]. Taikabutsu Overseas 16 3 (1995) 3-11
23. Chatterji S. Aspects of generation of destructive crystal growth pressure. J. Cryst. Growth 277 (2005) 566-577