Comparison of curing depth of a colored polyacid-modified composite resin with different light-curing units

Quintessence International

Volumn 41, Issue 9, 2010, Pages 787-794

  Vandenbulcke, Jeroen D E ^a   Marks, Luc A M ^a   Martens, Luc C ^a   Verbeeck, Ronald M H ^a  

^a GHENT UNIVERSITY   (Belgium)

Author keywords

Colored polyacid modified composite resin; Compomer; Curing depth; Light curing unit; Penetrometer

Indexed keywords

ALUMINUM SILICATE; BIOMEDICAL AND DENTAL MATERIALS; COMPOMER; GLASIOSITE; METHACRYLIC ACID DERIVATIVE; RESIN; SILICON DIOXIDE; Z100 COMPOSITE RESIN; ZIRCONIUM;

ARTICLE; CHEMISTRY; CLASSIFICATION; COLOR; COMPARATIVE STUDY; DENTAL EQUIPMENT; HUMAN; MATERIALS TESTING; PHOTOCHEMISTRY; POLYMERIZATION; RADIATION EXPOSURE; SURFACE PROPERTY;

ALUMINUM SILICATES; COLOR; COMPOMERS; COMPOSITE RESINS; CURING LIGHTS, DENTAL; DENTAL MATERIALS; HUMANS; MATERIALS TESTING; METHACRYLATES; PHOTOCHEMICAL PROCESSES; POLYMERIZATION; SILICON DIOXIDE; SURFACE PROPERTIES; ZIRCONIUM;

EID: 79952110535     PISSN: 00336572     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (45)

1. Shortall AC, Wilson HJ, Harrington E. Depth of cure of radiation-activated composite restoratives:Influence of shade and opacity. J Oral Rehabil 1995; 22:337-342.
2. Kawaguchi M, Fukushima T, Miyazaki T. The relationship between cure depth and transmission coefficient of visible-light-activated resin composites. J Dent Res 1994;73:516-521.
3. Musanje L, Darvell BW. Curing-light attenuation in filled-resin restoratives materials. Dent Mater 2006; 22:804-817.
4. Koupis NS, Vercruysse CWJ, Marks LAM, Martens LC, Verbeeck RMH. Curing depth of polyacid-modified composite resins determined by scraping and a penetrometer. Dent Mater 2004;20:908-914.
5. Lindberg A, Emami N, Van Dijken JWV. A Fourier Transform Raman spectroscopy analysis of the degree of conversion of a universal hybrid resin composite cured with light-emitting diode curing units. Swed Dent J 2005;29:105-112.
6. Koupis NS, Martens LC, Verbeeck RMH. Relative curing degree of polyacid-modified and conventional resin composites determined by surface Knoop hardness. Dent Mater 2006;22:1045-1050.
7. Turssi CP, Ferracane JL, Vogel K. Filler features and their effects on wear and degree of conversion of particulate dental resin composites. Biomaterials 2005;26:4932-4937.
8. Enami N, Sjodahl M, Soderholm KJ. How filler properties, filler fraction, sample thickness and light source affect light attenuation in particulate filled resin composites. Dent Mater 2005;21:721-730.
9. Halvorson RH, Erickson RL, Davidson CL. The effect of filler and silane content on conversion of resinbased composite. Dent Mater 2003;19:327-333.
10. Uhl A, Mills RW, Jandt KD. Photoinitiator dependent composite depth of cure and Knoop hardness with halogen and LED light curing units. Biomaterials 2003;24:1787-1795.
11. Park YJ, Chae KH, Rawls HR. Development of a new photoinitiation system for dental light-cure composite resins. Dent Mater 1999;15:120-127.
12. Yoon TH, Lee YK, Lim BS. Degree of polymerization of resin composites by different light sources. J Oral Rehabil 2002;29:1165-1173.
13. Rahiootis C, Kakaboura A, Loukidis M, Vougiouklakis G. Curing efficiency of various types of light-curing units. Eur J Oral Sci 2004;112:89-94.
14. Bennett AW, Watts DC. Performance of two blue light emitting diode dental light curing units with distance and irradiation time. Dent Mater 2004;20:72-79.
15. Emami N, Soderholm KJM. How light irradiance and curing time affect monomer conversion in lightcured resin composites. Eur J Oral Sci 2003;111:536-542.
16. DeWald JP, Ferracane JL. A comparison of four modes of evaluating depth of cure of light-activated composites. J Dent Res 1987;66:727-730.
17. Shortall AC, Harrington E. Guidelines for the selection, use and maintenance of visible light activation units. Br Dent J 1996;180:383-387.
18. Price RBT, Felix CA, Andreou P. Knoop hardness of ten resin composites irradiated with high-power LED and quartz-tungsten-halogen lights. Biomaterials 2005;26:2631-2641.
19. Wiggins KM, Hartung M, Althoff O. Curing performance of a new-generation light-emitting diode dental curing unit. J Am Dent Assoc 2004;135:1471-1479.
20. Ferracane JL, Mitchem JC, Condon JR, Todd R. Wear and marginal breakdown of composites with various degrees of cure. J Dent Res 1997;76:1508-1516.
21. Pearson PJ, Longman CM. Water sorption and solubility of resin-based materials following inadequate polymerization by a visible-light curing system. J Oral Rehabil 1989;16:57-61.
22. Ferracane JL. Elution of leachable components from composites. J Oral Rehabil 1994;21:441-452.
23. Moharamzadeh K, Van Noort R. Cytotoxicity of resin monomers on human gingival fibroblasts and HaCaT keratinocytes. Dent Mater 2007;23:40-44.
24. Reichl FX, Simon S, Esters M. Cytotoxicity of dental composite (co)monomers and the amalgam component Hg2+ in human gingival fibroblasts. Arch Toxicol 2006;80:465-472.
25. Al-Hiyasat AS, Darmani H. In vivo effects of BISGMA- a component of dental composite-on male mouse reproduction and fertility. J Biomed Mater Res A 2006;78:66-72.
26. Al-Hiyasat AS, Darmani H, Milhem MM. Cytotoxicity evaluation of dental resin composites and their flowable derivatives. Clin Oral Investig 2005;9:21-25.
27. Schweikl H, Hiller KA, Bolay C. Cytotoxic and mutagenic effects of dental composite materials. Biomaterials 2005;26:1713-1719.
28. Sletten GBG, Dahl JE. Cytotoxic effects of extracts of compomers. Acta Odontol Scand 1999;57:316-322.
29. Halvorson RH, Erickson RL, Davidson CL. Energy dependent polymerization of resin-based composite. Dent Mater 2002;18:463-469.
30. Calheiros FC, Kawano Y, Stansbury JW, Braga RR. Influence of radiant exposure on contraction stress, degree of conversion and mechanical properties of resin composites. Dent Mater 2006;22:799-803.
31. Nomoto R, Asada M, McCabe J, Hirano S. Light exposure required for optimum conversion of light activated resin systems. Dent Mater 2006;22:1135-1142.
32. Tsai PCL, Meyers IA, Walsh LJ. Depth of cure and surface microhardness of composite resin cured with blue LED curing lights. Dent Mater 2004;20:364-369.
33. Asmussen E, Peutzfeld A. Temperature rise induced by some light emitting diode and quartz-tungstenhalogen curing units. Eur J Oral Sci 2005;113:96-98.
34. Meyer JM, Cattani-Lorente MA, Depuis V. Compomers:Between glass-ionomer cements and composites. Biomaterials 1998;19:529-539.
35. Kramer N, Frankenberger R. Compomers in restorative therapy of children: A literature review. Int J Paed Dent 2007;17:2-9.
36. Wiegand A, Buchalla W, Attin T. Review on fluoridereleasing restorative materials-Fluoride release and uptake characteristics, antibacterial activity and influence on caries formation. Dent Mater 2007;23:343-362.
37. Marks LAM, Weerheijm KL, van Amerongen WE, Groen HJ, Martens LC. Dyract versus Tytin class II restorations in primary molars: 36 months evaluation. Caries Res 1999;33:387-392.
38. Welbury RR, Shaw AJ, Murray JJ, Gordon PH, McCabe JF. Clinical evaluation of paired compomer and glass-ionomer restorations in primary molars: Final results after 42 months. Br Dent J 2000;189:93-97.
39. Harrington E, Wilson HJ. Depth of cure of radioactivated materials-Effect of mould material and cavity size. J Dent 1993;21:305-311.
40. Yap AU, Soh MS. Curing efficacy of a new generation high-power LED lamp. Oper Dent 2005;30:758-763.
41. Croll TP. MagicFil: A coulorful kiddie compomer. Compend Contin Educ Dent 2002;23:1044-1048.
42. Correr GM, Alonso RC, Consani S, Puppin-Rontani RM, Ferracane JL. In vitro wear of primary and permanent enamel. Simultaneous erosion and abrasion. Am J Dent 2007;20:394-399.
43. Hansen EK, Asmussen E. Correlation between depth of cure and surface hardness of a light-activated resin. Scand J Dent Res 1993;101:62-64.
44. DeWald JP, Ferracane JL. A comparison of four modes of evaluating depth of cure of light-activated composites. J Dent Res 1987;66:727-730.
45. Koupis NS, Vercruysse CW, Martens LC, Verbeeck RM. Knoop hardness depth profile of polyacid-modified composite resins. Quintessence Int 2008;39:733-743.