Effects of non-uniform corrosion on the cracking and service life of reinforced concrete structures

Cement and Concrete Research

Volumn 40, Issue 9, 2010, Pages 1441-1450

  Jang, Bong Seok ^a   Oh, Byung Hwan ^b  

^a Korea Water Resources Corporation   (South Korea)

^b Seoul National University   (South Korea)

Author keywords

Concrete cover; Cracking pressure; Durability; Non uniform corrosion; Service life

Indexed keywords

ANALYSIS RESULTS; CONCRETE COMPRESSIVE STRENGTH; CONCRETE COVER; CONCRETE STRUCTURES; CRACKING BEHAVIOR; CRACKING OF CONCRETE; CRACKING PRESSURES; DIAMETER RATIO; NONUNIFORM; REINFORCED CONCRETE STRUCTURES; TEST DATA; UNIFORM CORROSION;

CEMENTS; COMPRESSIVE STRENGTH; CORROSION; DURABILITY; REINFORCED CONCRETE; SERVICE LIFE; STRUCTURAL MEMBERS;

CRACKING (CHEMICAL);

EID: 77955327302     PISSN: 00088846     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.cemconres.2010.03.018     Document Type: Article

References (27)

1. A. Costa, and J. Appeleton Chloride penetration into concrete in marine environment-Part I: main parameters affecting chloride penetration Materials and Structures 32 1999 252 259
2. A. Costa, and J. Appeleton Chloride penetration into concrete in marine environment-Part II: penetration of long term chloride penetration Materials and Structures 32 1999 252 259
3. B.H. Oh, and S.Y. Jang Prediction of diffusivity of concrete based on simple analytic equations Cement and Concrete Research 34 3 2004 463 480
4. B.H. Oh, and S.Y. Jang Effects of material and environmental parameters on chloride penetration profiles in concrete structures Cement and Concrete Research 37 1 2007 47 53
5. B.H. Oh, and B.S. Jang Chloride diffusion analysis of concrete structures considering the effects of reinforcements ACI Material Journal 100 2 2003 143 149
6. B.H. Oh, and S.Y. Jang Experimental investigation of the threshold chloride concentration for corrosion initiation in reinforced concrete structures Magazine of Concrete Research 55 2 2003 117 124
7. O.E. Gjoerv, and E. Vennesland Diffusion of chloride from seawater into concrete Cement and Concrete Research 9 2 1979 229 238
8. B.B. Hope, and A.K.C. Ip Chloride corrosion threshold in concrete ACI Materials Journal 84 4 1987 306 314
9. S.E. Hussain, A.S. Al-Gahtani, and S. Rasheeduzzafar Chloride threshold for corrosion of reinforcement in concrete ACI Materials Journal 93 1996 534 538
10. M. Thomas Chloride thresholds in marine concrete Cement and Concrete Research 26 4 1996 513 519
11. C. Andrade, and C. Alonso Corrosion rate monitoring in the laboratory and on-site Construction and Building Materials 10 5 1996 315 328
12. C. Andrade, and C. Alonso On-site measurements of corrosion rate of concretes Construction and Building Materials 15 2001 141 145 (Pubitemid 32139081)
13. J. Abdul-Hamid, J. Al-Tayyib, and M.S. Khan Corrosion rate measurements of reinforcing steel in concrete by electrochemical techniques ACI Materials Journal 85 2 1988 172 177
14. C. Arya, N.R. Buenfeld, and J.B. Newmann Assessment of simple methods of determining the free chloride content of cement pastes Cement and Concrete Research 17 6 1987 907 918
15. A. Castel, R. Francois, and G. Arliguie Factors other than chloride level influencing corrosion rate of reinforcement V.M. Malhotra, Proc. of CANMET/ACI Durability of Concrete 2000 American Concrete Institute Detroit 629 644
16. Q. T. Nguyen, S. Care, Y. Berthaud, A. Millard, F. Ragueneau, in press. Experimental and numerical behavior of reinforced mortar plates subjected to accelerated corrosion, Int. J. Numer. Anal. Meth. Geomech.
17. O. Poupard, V. L'hostis, S. Catinaud, and I. Petre-Lazar Corrosion damage diagnosis of a reinforced concrete beam after 40 years natural exposure in marine environment Cement and Concrete Research 36 2006 504 520
18. Y. Liu Y., R. E. Weyer, Modeling of time-to-corrosion cracking in chloride contaminated reinforced concrete structures ACI Materials Journal 95 6 1998 675 681
19. B.H. Oh, K.H. Kim, and B.S. Jang Critical corrosion amounts to cause cracking of reinforced concrete structures ACI Materials Journal 106 4 2009 333 339
20. K.H. Kim, S.Y. Jang, and B.H. Oh Modeling mechanical behavior of reinforced concrete due to corrosion of steel bar ACI Materials Journal 107 2 2010 106 113
21. S.J. Williamson, and L.A. Clark Pressure required to cause cover cracking of concrete due to reinforcement corrosion Magazine of Concrete research 52 6 2000 455 467
22. M. Maage, S. Helland, E. Poulsen, O. Vennesland, and J.E. Carlsen Service life prediction of existing concrete structures exposed to marine environment ACI Material Journal 93 6 1996 602 608
23. K. Tuutti Service life of structures with regard to corrosion of embedded steel, performance of concrete in marine environment, SP-65 American Concrete Institute 1980 223 236
24. J.R. Clifton, and L.I. Knab Service life of concrete, Report No. NISTIR 89-4086 1989 National Bureau of Standards
25. J.A. González, C. Andrade, C. Alonso, and S. Feliu Comparison of rates of general corrosion and maximum pitting penetration on concrete embedded steel reinforcement Cement and Concrete Research 25 2 1995 257 264
26. F.A. Oluokun Prediction of concrete tensile strength from its compressive strength evaluation relations for normal weight concrete ACI Materials Journal 88 3 1991 302 309
27. A. Hillerborg, M. Modeer, and P.E. Petersson Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements Cement and Concrete Research 6 1976 773 782