Factors other than chloride level influencing corrosion rate of reinforcement

American Concrete Institute, ACI Special Publication

Volumn SP-192, Issue , 2000, Pages 629-644

  Castel, Arnaud ^a   Francois, Raoul ^b   Arliguie, Ginette ^a  

^a UNIVERSITÉ PAUL SABATIER   (France)

^b INSA   (France)

Author keywords

Chlorides; Corrosion; Damage; Reinforced concretes; Steel construction

Indexed keywords

CHLORINE COMPOUNDS; CORROSION RATE; DURABILITY; REINFORCEMENT; STEEL CORROSION;

AGGRESSIVE ENVIRONMENT; COMPRESSION REINFORCEMENT; CORROSION THRESHOLD; LONGITUDINAL REINFORCEMENT; MECHANICAL DEGRADATION; STEEL-CONCRETE INTERFACE; TENSILE REINFORCEMENT; TOTAL CHLORIDE CONTENT;

CONCRETES;

EID: 0742300222     PISSN: 01932527     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (25)

1. Pourbaix, H. "Atlas of electrochemical equilibrium in aqueous solution" Oxford, 1966.
2. Hausmann D.A., "Steel corrosion in concrete" Materials Protection, 1967, vol. 4, n°. 11.
3. Gouda V.K. "Corrosion and corrosion inhibition of reinforcing steel" British Corrosion Journal, vol. 5, 1970, pp. 198-203.
4. Hussain S.E., Al-Gahtani A.S., Rasheeduzzafar. "Chloride threshold for corrosion of reinforcement in concrete" A.C.I. Materials Journal. 1996, Nov-Dec, pp. 534-538.
5. Thomas M. "Chloride thresholds in marine concrete" Cement and Concrete Research, vol. 26, 1996, pp. 513-519.
6. Brett W. and Schiessl P. "Time to depassivation depending on concrete composition and environmental conditions" R.I.L.E.M. Proceeding 1995, pp. 441-452, St-Remy-les-Chevreuse, France.
7. Sandberg P., Pettersson K., Sorensen H.E. Arup H. "Critical chloride concentrations for the onset of active reinforcement corrosion" R.I.L.E.M. Proceeding 1995, pp. 453-459, St-Remy-les-Chevreuse, France.
8. Nilsson L.O., Poulsen E., Sandberg P., Sorensen H.E. and Klinghoffer O. "Transport processes-corrosion initiation, test methods and prediction models" H.E.T.E.K. Chloride penetration into concrete, State of the art. Report n°53, Road Directorate, Ministry of Transport, Denmark, 1996.
9. BS 8110. "Structural use of concrete" (British Standards Institution, London, 1985).
10. NS 3420, vol. 1, "Specification texts for building and construction" Technical specification, (Norges Standardiseringsforbund, Oslo, 1986).
11. RILEM technical committee 124-SRC. "Draft recommendation for repair strategies for concrete structures damaged by reinforcement corrosion" Materials and Structures, vol. 27, 1994, pp. 415-436.
12. ACI committee 222. "Corrosion of metal in concrete" ACI J. Proc. 82 (1), 1985, pp. 3-32.
13. Vassie P. "Reinforcement corrosion and durability of concrete bridges" Proc. Inst. Civil Engnrs. Part.l, vol. 76, 1984, pp. 713-723.
14. Yonezawa T. Ashworth V., Procter R.P.M. "Pore solution composition and chloride effects on the corrosion of steel in concrete" Corrosion Engineering, 44, n°7, 1988, pp. 489-499.
15. Glass G.K., Buenfeld N.R. "Chloride threshold level for corrosion induced deterioration of steel in concrete" Chloride Penetration into Concrete, R.I.L.E.M. Proceeding 1995, pp. 429, St-Remy-les-Chevreuse, France.
16. Francis R., Arliguie G, Maso J.C. "Durability of reinforced concrete, syntheses Report" L.M.D.C. I.N.S.A.-U.P.S. 1994, Toulouse, France (in French).
17. Franfois R., Arliguie G. "Effect of microcracking and cracking on the development of corrosion in reinforced concrete members", Magazine of Concrete Research, Vol. 51, No. 2, April 1999, pp. 143-150.
18. Poulsen E. "Chloride profiles - analysis and interpretation of observations" AEC Laboratory, Ed. AEC Consulting Engineers Ltd, 1993, Vedbaek Denmark.
19. Fran?ois R., Arliguie G. "Durability of loaded reinforced concrete in chloride environnment" Third CANMET/ACI Int. Conf. 1994, ACI SP145-30, V.M. Malhotra Editor, pp. 573-595, Nice, France.
20. Francois R., Arliguie G. "Influence of service cracking on reinforcement steel corrosion", Journal of materials in civil engineering, ASCE, feb. 98, Vol. 10, No. 1, pp. 14-20.
21. Goto Y. "Cracks formed in concrete around deformed tension bars" ACI Journal, Proceeding, vol. 68, n°.4, 1971, pp. 244-251.
22. Konin A. Fran£ois R. and Arliguie G. "Analysis of progressive damage to reinforced ordinary and high performance concrete in relation to loading" Materials and Structures, vol. 1, 1998, pp. 27-35.
23. Konin A. Francois R. and Arliguie G. "Durabilite des BHP armes soumis a Taction des chlorures, influence de la fissuration et de la microfissuration" Annales du B.T.P. N°3, 1999, pp. 17-29.
24. Joisel A. "Les fissures du ciment" Edition de la revue des materiaux de Construction. Paris 1961.
25. Monfore G.E., Verbeck G.J. "Corrosion of prestressed wire in concrete" ACI J. Proc. 57 Vol. 11, 1960, pp. 491-515.