Modeling mechanical behavior of reinforced concrete due to corrosion of steel bar

ACI Materials Journal

Volumn 107, Issue 2, 2010, Pages 106-113

  Kim, Ki Hyun ^d   Jang, Seung Yup ^a   Jang, Bong Seok ^b   Oh, Byung Hwan ^c  

^a Korea Railroad Research Institute   (South Korea)

^b Korea Water Resources Corporation   (South Korea)

^c International Association of Fracture Mechanics for Concrete and Concrete Structures (IA FraMCoS)   (United States)

^d NONE

Author keywords

Corrosion; Cracking; Durability; Expansion pressure; Reinforced concrete; Stiffness

Indexed keywords

ANALYSIS/DESIGN; AVERAGE STRAIN; CONCRETE COVER; CONCRETE STRENGTH; CONCRETE STRUCTURES; CORROSION AMOUNT; CORROSION CRACKING; CORROSION LAYERS; CORROSION OF STEEL; CORROSION PRODUCTS; EXPANSION PRESSURE; EXPERIMENTAL DATA; MECHANICAL BEHAVIOR; REINFORCING BAR; STEEL BARS; SURFACE STRAINS; TEST DATA;

ALUMINUM CORROSION; BARS (METAL); CEMENTS; CONCRETE BUILDINGS; CRACKING (CHEMICAL); DURABILITY; MECHANICAL PROPERTIES; REINFORCED CONCRETE; STEEL CORROSION; STIFFNESS; STRUCTURAL MEMBERS;

STRAIN;

EID: 77950973417     PISSN: 0889325X     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (13)

1. Oh, B. H., and Jang, B. S., "Chloride Diffusion Analysis of Concrete Structures Considering the Effects of Reinforcements," ACI Materials Journal, V. 100, No.2, Mar.-Apr., 2003, pp. 143-149.
2. Oh, B. H., and Jang, S. Y., "Experimental Investigation of the Threshold Chloride Concentration for Corrosion Initiation in Reinforced Concrete Structures," Magazine of Concrete Research, V. 55, No.2, Apr. 2003, pp. 117-124.
3. 3. Bažant, Z. P., "Physical Model for Steel Corrosion in Concrete Sea Structures - Application," Journal of the Structural Division, ASCE, V. 105, No.6, 1979, pp. 1155-1166. (Pubitemid 9441994)
4. 4. Liu, Y., and Weyers, R. E., "Modeling the Time-to-Corrosion Cracking in Chloride Contaminated Reinforced Concrete Structures," ACI Materials Journal, V. 95, No.6, Nov.-Dec. 1998, pp. 675-681. (Pubitemid 128547641)
5. Martin-Perez, B., "Service Life Modeling of RC Highway Structures Exposed to Chlorides," PhD thesis, Department of Civil Engineering, University of Toronto, Toronto, ON, Canada, 1999, pp. 87-159.
6. 6. Ohtsu, M., and Yosimura, S., "Analysis of Crack Propagation and Crack Initiation due to Corrosion of Reinforcement," Construction and Building Materials, V. 11, No.7-8, 1997, pp. 437-442. (Pubitemid 127425445)
7. 7. Dagher, H. J., and Kulendran, S., "Finite Element Modeling of Corrosion Damage in Concrete Structures," ACI Structural Journal, V. 89, No.6, Nov.-Dec. 1992, pp. 699-708. (Pubitemid 23592696)
8. Broomfield, J. P., "Corrosion of Steel in Concrete," E&FN Spon, Chapter 2 and 3, 2007, pp. 5-28.
9. Lundgren, K., "Modeling Bond between Corroded Reinforcement and Concrete," Fracture Mechanics of Concrete Structures, V. 1, Proceedings of the Fourth International Conference on Fracture Mechanics of Concrete and Concrete Structures, Cachan, France, May 28-June 1, 2001, pp. 247-254.
10. Bourdette, B.; Ringot, E.; and Ollivier, J.-P., "Modeling of the Transition Zone Porosity," Cement and Concrete Research, V. 25, No.4, 1995, pp. 741-751.
11. Delagrave, A.; Bigas, J. P.; Ollivier, J.-R; Marchand, J.; and Pigeon, M., "Influence of Interfacial Zone on the Chloride Diffusivity of Mortars," Advanced Cement Based Materials, V. 5, 1997, pp. 86-91.
12. Oh, B. H., and Jang, S. Y., "Prediction of Diffusivity of Concrete Based on Simple Analytic Equations," Cement and Concrete Research, V. 34, No.3, 2004, pp. 463-480.
13. Oh, B. H.; Cha, S. W.; and Jang, S. Y., "Development of High-Performance Concrete Having High Resistance to Chloride Penetration," Nuclear Engineering and Design, 212, Issues 1-3, Mar. 2002, pp. 221-231.