Responsive micellar films of amphiphilic block copolymer micelles: Control on micelle opening and closing

Langmuir

Volumn 26, Issue 11, 2010, Pages 8869-8874

  Chen, Zhiquan ^a   He, Changcheng ^b   Li, Fengbin ^a   Tong, Ling ^a   Liao, Xingzhi ^a   Wang, Yong ^a  

^a NANJING TECH UNIVERSITY   (China)

^b BEIJING NORMAL UNIVERSITY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

2-VINYLPYRIDINE; AMPHIPHILIC BLOCK COPOLYMERS; AMPHIPHILICS; DIFFERENT SOLVENTS; MICELLAR FILMS; MICELLE SIZE; POLAR SOLVENTS; SELECTIVE SOLVENTS;

BLOCK COPOLYMERS; ETHANOL; ORGANIC SOLVENTS; POLYSTYRENES;

MICELLES;

ALCOHOL; POLY(2 VINYLPYRIDINE); POLY(2-VINYLPYRIDINE); POLYSTYRENE DERIVATIVE; POLYVINYL DERIVATIVE; WATER;

ARTICLE; ATOMIC FORCE MICROSCOPY; CHEMISTRY; MICELLE; TRANSMISSION ELECTRON MICROSCOPY;

ETHANOL; MICELLES; MICROSCOPY, ATOMIC FORCE; MICROSCOPY, ELECTRON, TRANSMISSION; POLYSTYRENES; POLYVINYLS; WATER;

EID: 77954551012     PISSN: 07437463     EISSN: 15205827     Source Type: Journal    
DOI: 10.1021/la904623e     Document Type: Article

References (34)

1. Pietsch, C.; Hoogenboom, R.; Schubert, U. S. Angew. Chem., Int. Ed. 2009, 48, 5653-5656.
2. Mendes, P. M. Chem. Soc. Rev. 2008, 37, 2512-2529.
3. Tokarev, I.; Minko, S. Soft Matter 2009, 5, 511-524.
4. Tokarev, I.; Motornov, M.; Minko, S. J. Mater. Chem. 2009, 19, 6932-6948.
5. Albrecht, K.; Mourran, A.; Moeller, M. Adv. Polym. Sci. 2006, 200, 57-70.
6. Webber, G. B.; Wanless, E. J.; Bütün, V.; Armes, S. P.; Biggs, S. Nano Lett. 2002, 2, 1307-1313.
7. Xu, C.; Fu, X. F.; Fryd, M.; Xu, S.; Wayland, B. B.; Winey, K. I.; Composto, R. J. Nano Lett. 2006, 6, 282-287.
8. Li, X.; Peng, J.; Kang, J. H.; Choy, J. H.; Steinhart, M.; Knoll, W.; Kim, D. H. Soft Matter 2008, 4, 515-521.
9. Chai, J.; Wang, D.; Fan, X. N.; Buriak, J. M. Nat. Nanotechnol. 2007, 2, 500-506.
10. Chai, J.; Buriak, J. M. ACS Nano 2008, 2, 489-501.
11. Albrecht, K.; Mourran, A.; Moeller, M. Adv. Polym. Sci. 2006, 200, 57-70.
12. Krishnamoorthy, S.; Hinderling, C.; Heinzelmann, H. Mater. Today 2006, 9, 40-47.
13. Sohn, B. H.; Yoo, S. I.; Seo, B. W.; Yun, S. H.; Park, S. M. J. Am. Chem. Soc. 2001, 123, 12734-12735.
14. Boontongkong, Y.; Cohen, R. E. Macromolecules 2002, 35, 3647-3652.
15. Bennett, R. D.; Miller, A. C.; Kohen, N. T.; Hammond, P. T.; Irvine, D. J.; Cohen, R. E. Macromolecules 2005, 38, 10728-10735.
16. Miller, A. C.; Bennett, R. D.; Hammond, P. T.; Irvine, D. J.; Cohen, R. E. Macromolecules 2008, 41, 1739-1744.
17. Xu, C.; Wayland, B. B.; Fryd, M.; Winey, K. I.; Composto, R. J. Macromolecules 2006, 39, 6063-6070.
18. Park, J. Y.; Sun, Y.; Goldman, Y. E.; Composto, R. J. Macromolecules 2009, 42, 1017-1023.
19. Kastle, G.; Boyen, H. G.; Weigl, F.; Lengl, G.; Herzog, T.; Ziemann, P.; Riethmuller, S.; Mayer, O.; Hartmann, C.; Spatz, J. P.; Möller, M.; Ozawa, M.; Banhart, F.; Garnier, M. G.; Oelhafen, P. Adv. Funct. Mater. 2003, 13, 853-861.
20. Qiao, Y. H.; Wang, D.; Buriak, J. M. Nano Lett. 2007, 7, 464-469.
21. Wang, Y.; Becker, M.; Wang, L.; Liu, J.; Scholz, R.; Peng, J.; Gösele, U.; Christiansen, S. H.; Kim, D. H.; Steinhart, M. Nano Lett. 2009, 9, 2384-2389.
22. Wang, Y.; Liu, J. Q.; Christiansen, S.; Kim, D. H.;Gösele, U.; Steinhart, M. Nano Lett. 2008, 8, 3993-3997.
23. Li, X.; Tian, S. J.; Ping, Y.; Kim, D. H.; Knoll, W. Langmuir 2005, 21, 9393-9397.
24. Cong, Y.; Zhang, Z. X.; Fu, J.; Li, J.; Han, Y. C. Polymer 2005, 46, 5377-5384.
25. Meister, A.; Krishnamoorthy, S.; Hinderling, C.; Pugin, R.; Heinzelmann, H. Microelectron. Eng. 2006, 83, 1509-1512.
26. Wang, L.; Montagne, F.; Hoffmann, P.; Pugin, R. Chem. Commun. 2009, 25, 3798-3800.
27. Ganta, S.; Devalapally, H.; Shahiwala, A.; Amiji, M. A. J. Controlled Release 2008, 126, 187-204.
28. Krishnamoorthy, S.; Pugin, R.; Brugger, J.; Heinzelmann, H.; Hinderling, C. Adv. Funct. Mater. 2006, 16, 1469-1475.
29. Virgili, J. M.; Hexemer, A.; Pople, J. A.; Balsara, N. P.; Segalman, R. A. Macromolecules 2009, 42, 4604-4613.
30. As measured from the AFM image of the as-coated PS-b-P2VP film, the average diameter of micelles is around 53 nm, and the PS-b-P2VP used here has a symmetric structure; therefore, the volume of the core can be estimated as half of the whole size of the micelle. As a result, it is reasonable to estimate the thickness of the PS corona is ca. 5 nm.
31. Loxley, A.; Vincent, B. Colloid Polym. Sci. 1997, 275, 1108-1114.
32. Fernández-Nieves, A.; Fernández-Barbero, A.; Vincent, B.; de las Nieves, F. J. Macromolecules 2000, 33, 2114-2118.
33. Krishnamoorthy, S.; Pugin, R.; Brugger, J.; Heinzelmann, H.; Hoogerwerf, A. C.; Hinderling, C. Langmuir 2006, 22, 3450-3452.
34. Fleer, G. I.; Cohen Stuart, M. A.; Scheutjens, J. M. H.; Cosgrove, T.; Vincent, B. Polymer at Interfaces; Chapman & Hall: London, 1993.