Challenges in modelling the evolution of stress corrosion cracks from pits

Author keywords

Finite element analysis; Modelling; Pitting; Stress corrosion cracking; X ray tomography

Indexed keywords

CRACKING (CHEMICAL); CRACKS; DIAGNOSTIC RADIOGRAPHY; FINITE ELEMENT METHOD; GROWTH KINETICS; IMAGING SYSTEMS; INDUSTRIAL APPLICATIONS; MARINE ENGINES; MATHEMATICAL TRANSFORMATIONS; PITTING; RESIDUAL STRESSES; STEAM TURBINES; TOMOGRAPHY;

EID: 60849108900     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfracmech.2008.09.004     Document Type: Article
Times cited : (104)

References (9)
  • 1
    • 0024301935 scopus 로고
    • Prediction of fatigue crack initiation life based on pit growth
    • Kondo Y. Prediction of fatigue crack initiation life based on pit growth. Corrosion 45 (1989) 7-11
    • (1989) Corrosion , vol.45 , pp. 7-11
    • Kondo, Y.1
  • 2
    • 60849117327 scopus 로고    scopus 로고
    • Wei RP. Material aging and reliability of engineered systems. In: Kane RD, editor. Proceedings of conference on environmentally assisted cracking: predictive methods for risk assessment and evaluation of material, equipment and structures, ASTM STP1401, 2000. p. 3-19.
    • Wei RP. Material aging and reliability of engineered systems. In: Kane RD, editor. Proceedings of conference on environmentally assisted cracking: predictive methods for risk assessment and evaluation of material, equipment and structures, ASTM STP1401, 2000. p. 3-19.
  • 5
    • 33746218004 scopus 로고    scopus 로고
    • A model to predict the evolution of pitting corrosion and the pit-to-crack transition incorporating statically distributed input parameters
    • Turnbull A., McCartney L.N., and Zhou S. A model to predict the evolution of pitting corrosion and the pit-to-crack transition incorporating statically distributed input parameters. Corros Sci 48 (2006) 2084-2105
    • (2006) Corros Sci , vol.48 , pp. 2084-2105
    • Turnbull, A.1    McCartney, L.N.2    Zhou, S.3
  • 6
    • 28544438825 scopus 로고    scopus 로고
    • Modelling of the evolution of stress corrosion cracks from corrosion pits
    • Turnbull A., McCartney L.N., and Zhou S. Modelling of the evolution of stress corrosion cracks from corrosion pits. Scripta Mater 54 (2006) 575-578
    • (2006) Scripta Mater , vol.54 , pp. 575-578
    • Turnbull, A.1    McCartney, L.N.2    Zhou, S.3
  • 7
    • 84876881542 scopus 로고    scopus 로고
    • Finite element analysis of the stress and strain associated with a corrosion pit in a cylindrical specimen under applied tensile loading
    • 034, 2006
    • Turnbull A, Crocker L. Finite element analysis of the stress and strain associated with a corrosion pit in a cylindrical specimen under applied tensile loading. NPL Report DEPC-MPE 034, 2006.
    • NPL Report DEPC-MPE
    • Turnbull, A.1    Crocker, L.2
  • 9
    • 33749547471 scopus 로고    scopus 로고
    • X-ray microtomography studies of localised corrosion and transitions to stress corrosion cracking
    • Connolly B.J., Horner D.A., Fox S.J., Davenport A.J., Padovani C., Zhou S., et al. X-ray microtomography studies of localised corrosion and transitions to stress corrosion cracking. Mater Sci Technol 22 9 (2006) 1076-1085
    • (2006) Mater Sci Technol , vol.22 , Issue.9 , pp. 1076-1085
    • Connolly, B.J.1    Horner, D.A.2    Fox, S.J.3    Davenport, A.J.4    Padovani, C.5    Zhou, S.6


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.