Corrosion fatigue behavior of extruded magnesium alloy AZ31 in sodium chloride solution

International Journal of Fatigue

Volumn 30, Issue 7, 2008, Pages 1181-1188

  Nan, Z Y ^a   Ishihara, S ^a   Goshima, T ^a  

^a UNIVERSITY OF TOYAMA   (Japan)

Author keywords

Corrosion fatigue; Corrosion pit; Crack initiation; Crack propagation; Magnesium alloy

Indexed keywords

CORROSION FATIGUE; CRACK INITIATION; FAILURE ANALYSIS; FATIGUE CRACK PROPAGATION; SODIUM CHLORIDE; STRESS ANALYSIS;

CORROSION PITS; EXTRUDED MAGNESIUM; FATIGUE BEHAVIOR; SODIUM CHLORIDE SOLUTIONS;

MAGNESIUM ALLOYS;

EID: 41549149062     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2007.09.005     Document Type: Article

References (18)

1. Kojima Y. Handbook advanced magnesium technology (2000), Kallos Publishing Co. Ltd., Tokyo
2. Goodenberger D.L., and Stephens R.I. Fatigue of AZ91E-T6 cast magnesium alloy. J Eng Mater Technol 115 (1993) 391-397
3. Kobayashi Y, Takano K, Ishikawa K. Fatigue crack propagation of AZ31 magnesium alloy. In: Program of the 96th conference of Japan Institute of Light Metal 1999. p. 81-2.
4. Hilpert M., and Wagner L. Corrosion fatigue behavior of the high-strength magnesium alloy AZ80. J Mater Eng Perform 9 4 (2000) 402-407
5. Eisenmeier G., Holzwarth B., Höppel H.W., and Mughrabi H. Cyclic deformation and fatigue behaviour of the magnesium alloy AZ91. Mater Sci Eng A 319 (2001) 578-582
6. Shih T.S., Liu W.S., and Chen Y.J. Fatigue of as-extruded AZ61A magnesium alloy. Mater Sci Eng A 325 (2002) 152-162
7. Kobayashi Y, Takano K, Ishikawa K. Fatigue crack propagation of AZ91D and AM60B magnesium alloys. In: Program of the 94th conference of Japan Institute of Light Metal 1998. p. 267-8.
8. Sajuri Z.B., Umehara T., and Mutoh Y. Effect of environment on fatigue behavior of AZ61 magnesium alloy. In: Blom A.F. (Ed). Proceedings of the eighth international fatigue conferences. Fatigue (2002), EMAS, West Midlands, (UK) 3301-3308
9. Nan Z.Y., Ishihara S., Goshima T., and Nakanishi R. Fatigue behavior of AZ31 extruded magnesium alloy in laboratory air. Trans Jpn Soc Mech Eng A 70 696 (2004)
10. Nan Z.Y., Ishihara S., Goshima T., and Nakanishi R. Scanning probe microscope observations of fatigue process in magnesium alloy AZ31 near the fatigue limit. Scr Mater 50 4 (2004) 429-434
11. Nan Z.Y., Ishihara S., and Goshima T. On the sharp bend in the S-N curve of the AZ31 extruded magnesium alloy. In: Nilsson F. (Ed). The 15th European conference of fracture (2004), Stockholm, Sweden
12. Ishihara S., Saka S., Nan Z.Y., Goshima T., and Sunada S. Prediction of corrosion fatigue lives of aluminum alloy on the basis of corrosion pit growth law. Fatigue Fract Eng Mater Struct 29 (2006) 472-480
13. Ishihara S., Goshima T., McEvily A.J., Sunada S., and Nomata S. Corrosion-pit-growth behaviour during the corrosion fatigue process in aluminum. In: Ravi-Chandar K., Karihaloo B.L., Kishi T., Ritchie R.O., Yokobori Jr. A.T., and Yokobori T. (Eds). Proceedings of the 10th international conference on fracture (2001), Honolulu, USA [CD-ROM]
14. Ishihara S, Goshima T, Chiba H, Nomata S, Sunada S, McEvily AJ. Effect of stress amplitude on the corrosion-pit-growth behavior of pure aluminum in a sodium chloride solution. In: Matsumura M, Nagano H, Nakasa K, Isomoto Y, editors. Proceedings of the second international conference on environment sensitive cracking and corrosion damage, Hiroshima, Japan; 2001. p. 354-61.
15. Wei R.P. Corrosion/corrosion fatigue and life-cycle management. Mater Sci Res Int 7 3 (2001) 147-156
16. Murakami Y., and Endo M. Experimental evidences and applications. Proceedings of the theoretical concepts and numerical analysis of fatigue (1992), Engineering Materials Advisory Services Ltd., Cradley Heath, Birmingham, (UK). Warley 51-71
17. Ishihara S., McEvily A.J., and Shiozawa K. A fatigue-crack-growth-based analysis of two-sterp corrosion fatigue tests. Fatigue Fract Eng Mater Struct 18 (1995) 1311-1321
18. Nishitani H. Fatigue strength (1985), Ohmsha Publishing Co. Ltd., Tokyo