Stress corrosion cracking behaviors of AZ91 magnesium alloy in deicer solutions using constant load

Materials Science and Engineering: A

Volumn 515, Issue 1-2, 2009, Pages 79-84

  Chen, Jian ^a   Ai, Meirong ^a   Wang, Jianqiu ^a   Han, En Hou ^a   Ke, Wei ^a  

^a INSTITUTE OF METAL RESEARCH   (China)

Author keywords

AZ91 magnesium alloy; Constant load; Hydrogen embrittlement; Stress corrosion cracking

Indexed keywords

CRACKS; HYDROGEN; HYDROGEN EMBRITTLEMENT; MAGNESIUM ALLOYS; RESIDUAL STRESSES; YIELD STRESS;

AS-CAST AZ91 MAGNESIUM ALLOYS; AZ91 ALLOY; AZ91 MAGNESIUM ALLOYS; CONSTANT LOADS; CRACKING BEHAVIOR; CRITICAL STRESS; DEICERS; STRESS THRESHOLDS;

STRESS CORROSION CRACKING;

EID: 65449160472     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2009.02.047     Document Type: Article

References (29)

1. Hartmann G., and Walter A.E. In: Kainer K.U. (Ed). Magnesium Alloys and Their Application (2000), Wiley-VCH, Weinhein 548-552
2. Mordike B.L., and Ebert T. Mater. Sci. Eng. A 302 1 (2001) 37-45
3. Winzer N., Atrens A., Song G.L., Ghali E., Dietzel W., Kainer K.U., Hort N., and Blawert C. Adv. Eng. Mater. 7 (2005) 659-693
4. Chen J., Wang J.Q., Han E.-H., and Ke W. Corrosion 63 7 (2007) 661-671
5. Chen J., Wang J.Q., Han E.-H., and Ke W. Corros. Sci. 49 3 (2007) 1625-1634
6. Chen J., Wang J.Q., Han E.-H., and Ke W. Mater. Sci. Forum 546-549 (2007) 537-542
7. Chen J., Wang J.Q., Han E.-H., and Ke W. Electrochem. Commun. 10 (2008) 577-581
8. Chen J., Wang J.Q., Han E.-H., and Ke W. Corros. Sci. 50 5 (2008) 1449-1459
9. J. Chen, J.Q. Wang, E.-H. Han, W. Ke, Corros. Eng. Sci. Tech. (accepted).
10. Chen J., Wang J.Q., Han E.-H., Dong J.H., and Ke W. Mater. Corros. 57 10 (2005) 789-793
11. Chen J., Wang J.Q., Han E.-H., Dong J.H., and Ke W. Electrochim. Acta 52 (2007) 3299-3309
12. Chen J., Wang J.Q., Han E.-H., Dong J.H., and Ke W. Corros. Sci. 50 5 (2008) 1292-1305
13. Chen J., Dong J.H., Wang J.Q., Han E.-H., and Ke W. Corros. Sci. 50 5 (2008) 3610-3614
14. Chen J., Wang J.Q., Han E.-H., and Ke W. Corros. Sci. 50 5 (2008) 2338-2341
15. Chen J., Wang J.Q., Han E.-H., and Ke W. Corros. Sci. 51 (2009) 477-484
16. Chen J., Wang J.Q., Han E.-H., and Ke W. Corros. Sci. (2009) 10.1016/j.corsci. 2009.02.020
17. Chen J., Wang J.Q., Han E.-H., and Ke W. Mater. Sci. Eng. A 488 1-2 (2008) 428-434
18. Wang J.Q., Chen J., Han E.-H., and Ke W. Mater. Trans. 49 5 (2008) 1052-1056
19. Chen J., Wang J.Q., Han E.-H., and Ke W. Mater. Sci. Eng. A 494 (2008) 257-262
20. Chakrapani D.G., and Pugh E.N. Corrosion 31 (1975) 247-252
21. Winzer N., Atrens A., Dietzel W., Song G.L., and Kainer K.U. Mater. Sci. Eng. A 466 (2007) 18-31
22. Winzer N., Atrens A., Dietzel W., Song G.L., and Kainer K.U. Mater. Sci. Eng. A 472 (2008) 97-106
23. N. Yang, Multiple deicers, Chinese Patent no. 1,563,248.
24. Gutman E.M., Solovioff G., and Eliezer D. Corros. Sci. 38 7 (1996) 1141-1145
25. Eliezer A., Gutman E.M., Abramov E., and Aghion E. Mater. Sci. Forum 289-292 (1998) 517-528
26. Bonora P.L., Andrei M., Eliezer A., and Gutman E. Corros. Sci. 44 (2002) 729-749
27. Nordien J.H., Ono S., Masuko N., and Nisancioglu K. J. Electrochem. Soc. 142 (1995) 3320-3322
28. Song G.L., Johannesson B., Hapugoda S., and StJohn D. Corros. Sci. 46 (2004) 955-977
29. Cheng Y.F., and Niu L. Electrochem. Commun. 9 (2007) 558-562