Volumn 50, Issue 8, 2008, Pages 2338-2341
|
|
In situ observation of crack initiation and propagation of the charged magnesium alloy under cyclic wet-dry conditions
a
a
|
|
Author keywords
A. Magnesium; B. Environmental scanning electron microscope
|
|
Indexed keywords
ALLOYS;
CRACK INITIATION;
CRACK PROPAGATION;
CURING;
DRYING;
FRACTURE FIXATION;
HYDROGEN;
LIGHT METALS;
MAGNESIUM;
MAGNESIUM ALLOYS;
MAGNESIUM PRINTING PLATES;
NONMETALS;
SCANNING ELECTRON MICROSCOPY;
STRESS CORROSION CRACKING;
A. MAGNESIUM;
B. ENVIRONMENTAL SCANNING ELECTRON MICROSCOPE;
CORROSION REACTIONS;
CRACK INITIATION AND PROPAGATION;
CRACK LENGTHS;
CRACKING PROCESSES;
CYCLIC WET-DRY CONDITIONS;
ENVIRONMENTAL SCANNING ELECTRON MICROSCOPE;
IN-SITU;
IN-SITU OBSERVATIONS;
WET-DRY CYCLING;
WETTING TIME;
WATER VAPOR;
CRACKS;
CURING;
DRYING;
FRACTURE;
HYDROGEN;
LIGHT METALS;
MAGNESIUM COMPOUNDS;
NONMETALS;
PRINTING PLATES;
SCANNING ELECTRON MICROSCOPY;
STRESS CORROSION;
|
|
EID: 50349092269
PISSN: 0010938X
EISSN: None
Source Type: Journal
DOI: 10.1016/j.corsci.2008.05.013 Document Type: Article |
|
Times cited : (20)
|
|
References (17)
|