Investigation of stress corrosion cracking behaviors of an AZ91 magnesium alloy in 0.1 kmol/m3 Na2so4 solution using slow strain rate test

Materials Transactions

Volumn 49, Issue 5, 2008, Pages 1052-1056

  Wang, Jianqiu ^a   Chen, Jian ^a   Han, Enhou ^a   Ke, Wei ^a  

^a INSTITUTE OF METAL RESEARCH   (China)

Author keywords

AZ91 magnesium alloy; Hydrogen embrittlement; Slow strain rate test; Stress corrosion cracking

Indexed keywords

ALLOYS; CORROSION; CRACK DETECTION; CRACKING (CHEMICAL); LIGHT METALS; MAGNESIUM; MAGNESIUM ALLOYS; MAGNESIUM PRINTING PLATES; RESIDUAL STRESSES;

AS-CAST; AZ91 MAGNESIUM ALLOYS; STRESS CORROSION; STRESS CORROSION CRACKING (SCC);

STRESS CORROSION CRACKING;

EID: 46649105733     PISSN: 13459678     EISSN: None     Source Type: Journal    
DOI: 10.2320/matertrans.MC200711     Document Type: Article

References (12)

1. R. Glicksman: J. Electrochem. Soc. 106 (1959) 457.
2. R. Tunold, H. Holtan, M. Berge, A. Lasson and R. Hansen: Corros. Sci. 17 (1977) 353.
3. J. Chen, J. Wang, E. Han, J. Dong and W. Ke: Electrochim. Acta 52 (2007) 3299-3309.
4. J. Chen, J. Wang, E. Han, J. Dong and W, Ke: Mater. Corros. 57 (2006) 789-793.
5. J. Chen, J. Wang, E. Han, J. Dong and W. Ke: Corros. Sci. in revision.
6. J. Chen, J. Wang, E. Han, J. Dong and W. Ke: Corros. Sci. under review.
7. N. Winzer, A. Atrens, W. Dietzel, G. Song and K. Kainer: Mater. Sci. Eng. A 466 (1-2) (2007) 18-31.
8. J. Chen, J. Wang, E. Han and W. Ke: Mater. Sci. Eng. A (2007), doi: 10.1016/j.mesa.2007.11.035.
9. O. Lunder, J. Lein, T. Aune and K. Nisancioglu: Corrosion 45 (1989) 741.
10. G. Song, A. Atrens and M. Dargusch: Corros. Sci. 41 (1999) 741-748.
11. A. Atrens, N. Winzer, G. Song, W. Dietzel and C. Blawert: Adv. Eng. Mater. 8 (2006) 750.
12. Y. Cheng and L. Niu: Electrochem. Comm. 9 (2007) 558-562.