Part II. Effects of grain-boundary structure on the path of cracking in polycrystals

Materials Science and Engineering: A

Volumn 507, Issue 1-2, 2009, Pages 61-65

  Kane, William M ^a   McMahon, C J ^a  

^a UNIVERSITY OF PENNSYLVANIA   (United States)

Author keywords

Bicrystals; Dynamic embrittlement; High temperature brittle fracture; IN718; Intergranular fracture; Polycrystals; Superalloys

Indexed keywords

BICRYSTALS; CRACKS; EMBRITTLEMENT; GRAIN BOUNDARIES; NICKEL ALLOYS; POLYCRYSTALS; SUPERALLOYS;

CRACKING SUSCEPTIBILITY; DYNAMIC EMBRITTLEMENT; GRAIN BOUNDARY STRUCTURE; HIGH-TEMPERATURE BRITTLE FRACTURE; HIGHEST TEMPERATURE; INTERGRANULAR CRACK; INTERGRANULAR FRACTURE; LOW ANGLE BOUNDARIES; NICKELBASE SUPERALLOY; TRIPLE JUNCTION;

BRITTLE FRACTURE;

EID: 61649128770     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2008.07.015     Document Type: Article

References (6)

1. Bika D., Pfaendtner J.A., Menyhard M., and McMahon Jr. C.J. Acta Metall. Mater. 43 (1995) 1909
2. Pfaendtner J.A., and McMahon Jr. C.J. Acta Mater. 49 (2001) 3369
3. Krupp U., Kane W.M., Liu X., Duber O., Laird C., and McMahon Jr. C.J. Mater. Sci. Eng. A 349 (2003) 213
4. Muthiah R.C., Pfaendtner J.A., Ishikawa S., and McMahon Jr. C.J. Acta Mater. 47 (1999) 2797
5. Muthiah R.C., Pfaendtner J.A., McMahon Jr. C.J., Xu Y., and Bassani J.L. Mater. Sci. Eng. A 234-236 (1997) 1033-1036
6. Bika D., and McMahon Jr. C.J. Acta Metall. Mater. 43 (1995) 1895