Fatigue damage evolution in ductile single-phase face-centred cubic metals in the UHCF-regime

VHCF-4 - 4th International Conference on Very High Cycle Fatigue

Volumn , Issue , 2007, Pages 75-82

  Mughrabi, Hael ^a   Stanzl Tschegg, Stefanie ^b  

^a UNIVERSITY OF ERLANGEN NUREMBERG   (Germany)

^b UNIVERSITY OF NATURAL RESOURCES AND LIFE SCIENCES   (Austria)

Author keywords

Persistent slip bands; Surface fatigue damage; Ultrahigh Cycle Fatigue

Indexed keywords

CRACKS; EXPERIMENTS; FATIGUE CRACK PROPAGATION; FATIGUE OF MATERIALS; LAMINATES; LEAD; METALLIC COMPOUNDS; STRESS CONCENTRATION;

CUBIC METALS; CYCLIC SLIPS; EXPERIMENTAL EVIDENCES; FATIGUE BEHAVIOURS; FATIGUE DAMAGE EVOLUTIONS; FATIGUE LIFE DIAGRAMS; FATIGUE LIMITS; LOADING AMPLITUDES; LOCAL STRESS CONCENTRATIONS; NUMBER OF CYCLES; PERSISTENT SLIP BANDS; SURFACE FATIGUE DAMAGE; ULTRAHIGH CYCLE FATIGUE;

FATIGUE DAMAGE;

EID: 58349104990     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (23)

1. C. Bathias "There is no infinite fatigue life in metallic materials", Fatigue & Fract Engng Mater Struct 22 (1999), 559-565.
2. Y. Murakami, T. Nomoto, and T. Ueda, "Factors influencing the mechanism of superlong fatigue failure in steels", Fatigue & Fract Engng Mater Struct, 22 (1999) 581-590.
3. S. Nishijima and K. Kanazawa, "Stepwise S-N curve and fish-eye failure in gigacycle fatigue", Fatigue & Fract Engng Mater Struct, 22 (1999) 601-607.
4. T. Sakai, M. Takeda, K. Shiozawa, Y. Ochi, M. Nakajima, T. Nakamura, and N. Ogyma, "Experimental evidence of duplex S-N characteristics in wide life region for high strength steels", Proc. of FATIGUE 1999, Vol 1, eds. X.R. Wu and Z.G. Wang (Beijing: Higher Education Press and West Midlands: EMAS Ltd., 1999), 573-578.
5. H. Mughrabi, "On the life-controlling microstructural fatigue mechanisms in ductile metals and alloys in the gigacycle regime",. Fatigue & Fract Engng Mater Struct, 22 (1999) 633-641.
6. H. Mughrabi, "On multi-stage fatigue life diagrams and the relevant life-controlling mechanisms in ultrahigh-cycle fatigue", Fatigue & Fract Engng Mater Struct, 25 (2002) 755-764.
7. H. Mughrabi, "Specific features and mechanisms of fatigue in the ultrahigh-cycle regime", Proceedings of the Third International Conference on Very High Cycle Fatigue (VHCF-3), eds. T. Sakai and Y. Ochi., Ritsumeikan University, Kusatsu, Japan (Kyoto: The Society of Materials Science, Japan, 2004), 14-24. Updated version in: Int J Fatigue 28 (2006) 1501-1508.
8. th European Conference of Fracture (ECF 16) - Failure Analysis of Nano and Engineering Materials and Structures, Alexandropoulis, Greece, ed. E.E. Gdoutos (Springer, 2006) ISBN-101-4020-4971-4.
9. S. Stanzl-Tschegg, H. Mughrabi, and B. Schoenbauer, "Life time and cyclic slip of copper in the VHCF regime", Proceedings of International Conference on Fatigue Damage of Structural Materials, Hyannis, MA, USA, Sept. 2006, eds. M.R. Bache et al., Int. J. Fatigue, in press..
10. H. Mughrabi, "Fatigue mechanisms in the ultrahigh cycle regime", Proceedings of the Nineth International Fatigue Congress FATIGUE 2006, Atlanta, USA, eds. W.S. Johnson et al. (CD-ROM, 2006) Paper FT 193.
11. Q.Y. Wang, C. Bathias, N. Kawagoishi, and Q. Chen, "Effect of inclusion on subsurface crack initiation and gigacycle strength", Int J Fatigue 24 (2002) 1269-1274.
12. T. Billaudeau, and Y. Nadot, "Support for an environmental effect on fatigue mechanisms in the long life regime". Int J Fatigue 26 (2004) 839-847.
13. P. Paris P, I. Marines-Garcia, R.W. Hertzberg, and J.K. Donald, "The relationship of effective stress intensity, elastic modulus and Burgers vector on fatigue crack growth as associated with "fish-eye" gigacycle phenomena", Proceedings of the Third International Conference on Very High Cycle Fatigue (VHCF-3), eds. T. Sakai and Y. Ochi., Ritsumeikan University, Kusatsu, Japan (Kyoto: The Society of Materials Science, Japan, 2004) 1-13.
14. V.F. Terent'ev, "On the problem of the fatigue limit of metallic materials", Metal Science and Heat Treatment 46 (2004) 244-249.
15. H. Mughrabi and R. Wang, "Cyclic deformation of face-centred cubic polycrystals: a comparison with observations on single crystals", Deformation of Polycrystals: Mechanisms and Microstructures, Proceedings of 2nd Rise International Symposium on Metallurgy and Materials Science, eds. N. Hansen et al. (Roskilde: Risø National Laboratory, 1981) 87-98.
16. P. Lukáš, M. Klesnil, and J. Polák, "High cycle fatigue life of metals", Mater Sci Eng 15 (1974)239-245.
17. M. Klesnil and P. Lukáš, Fatigue of Metallic Materials (Prague: Academia, and Amsterdam: Elsevier, 1980).
18. W. Hessler, H. Milliner, B. Weiss, and R. Stickler, "Near-threshold behaviour of polycrystalline copper", Metal Science 15 (1981) 225-230.
19. S. Stanzl-Tschegg, to be presented at VHCF-4.
20. H. Mughrabi, R. Wang, K. Differt, and U. Essmann, "Fatigue crack initiation by cyclic slip irreversibilities in high-cycle fatigue", Fatigue mechanisms: Advances in Quantitative Measurement of Physical Damage, eds. J. Lankford et al. (Philadelphia: American Society for Testing and Materials, ASTM STP 811, 1983) 5-45.
21. J.C. Figueroa, and C. Laird, "Crack initiation mechanisms in copper polycrystals cycled under constant strain amplitudes and in step test", Mater Sci Eng 60 (1983) 45-58.
22. H. W. Höppel, L. Saitova, and M. Göken, to be presented at VHCF-4.
23. D. L. Davidson, Davidson, to be presented at VHCF-4.