Support for an environmental effect on fatigue mechanisms in the long life regime

International Journal of Fatigue

Volumn 26, Issue 8, 2004, Pages 839-847

  Billaudeau, T ^a   Nadot, Y ^a  

^a CNRS   (France)

Author keywords

Casting defects; Environment; Fatigue life assessment; Giga cycle fatigue; High cycle fatigue; Nodular cast irona

Indexed keywords

CASTING; CRACK INITIATION; ENVIRONMENTAL IMPACT; FRACTURE; LOADS (FORCES); NODULAR IRON; PARAMETER ESTIMATION; STATISTICAL METHODS; TENSILE STRENGTH; THRESHOLD ELEMENTS;

CASTING DEFECTS; FATIGUE LIFE ASSESSMENT; GIGA CYCLE FATIGUE; HIGH CYCLE FATIGUE;

CRACKS;

EID: 2342632482     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2004.01.005     Document Type: Article

References (20)

1. Sakai T, Takeda M, Shiosawa K, Ochi Y, Nakajima M, Nakamura T, Oguma N. Experimental evidence of duplex S-N characteristics in wide life region for high strength steels. In: Wu XR, Wang ZG, editors. Proceedings of the 7th Int. Conf. Fatigue Congress, Beijing, China. Higher Education Press/EMAS; 1999. p. 573-8.
2. Bathias C. There is no infinite fatigue life in metallic materials. Fatigue Fract Engng Mater Struct. 22:1999;559-565.
3. Murakami Y., Nomoto T., Ueda T. Factors influencing the mechanism of superlong fatigue failure in steels. Fatigue Fract Engng Mater Struct. 22:1999;581-590.
4. Billaudeau T., Nadot Y. Fatigue crack initiation for defect materials under multiaxial loading. Proceedings of the Sixth International Conference on Biaxial/Multiaxial Fatigue & Fracture :2001;771-778 Instituto Superior Tecnico, Lisboa, Portugal.
5. Nadot Y., Mendez J., Ranganathan N., Béranger A.S. Fatigue life assessment of nodular cast iron containing casting defects. Fatigue Fract Engng Mater Struct. 22:1999;289-300.
6. Nadot Y., Ranganathan N., Mendez J., Béranger A.S. A study of natural cracks initiated on casting defects by crack front marking. Scripta Mater. 37:(5):1997;549-553.
7. Henaff G., Petit J. A logical framework for the analysis of fatigue crack propagation enhancement by ambient atmosphere. Physicochem Mech Mater. 32:(2):1996;69-88.
8. Birnbaum H.K., Sofronis P. Hydrogen-enhanced localized plasticity. Mater Sci Eng. A176:1994;191-202.
9. Mayer H., Stanzl-Tschegg S. Environmental influences at very high frequency. Proceedings of the International Conference on Fatigue in the Very High Cycle Regime :2001;267-274 Universitaet fur Bodenkultur Wien, Vienna, Austria.
10. 7 cycles). Fatigue Fract Engng Mater Struct. 23:2000;893-910.
11. Levan A., Royer J. Part-circular surface cracks in round bars under tension, bending and twisting. Int J Fract. 61:1993;71-99.
12. Rooke DP, Cartwright DJ. Compendium of stress intensity factors. Her Majesty's Stationary Office; 1976 [ISBN: 0117713368].
13. Petit J., De Fouquet J., Henaff G. Influence of ambiant atmosphere on fatigue crack growth behaviour of metals. Carpinteri A. Handbook of fatigue crack propagation in metallic structures. 1994;1159-1204 Elsevier.
14. Lindley T., Pineau A. Short crack effect in fracture and fatigue. Science et Genie des Matériaux. 2:1995;187.
15. Miller K.J., O'Donnell W.J. The fatigue limit and its elimination. Fatigue Fract Engng Mater Struct. 22:1999;545-557.
16. Mughrabi H. On the life-controlling microstructural fatigue mechanisms in ductile metals and alloys in the gigacycle regime. Fatigue Fract Engng Mater Struct. 22:1999;633-641.
17. Mughrabi H. On "multi-stage" fatigue life diagrams and the relevant life-controlling mechanisms. Proceedings of the International Conference on Fatigue in the Very High Cycle Regime :2001;35-49 Universitat fur Bodenkultur Wien, Vienna, Austria.
18. Nishijama S., Kanazawa K. Stepwise S-N curve and fish-eye failure in gigacycle fatigue. Fatigue Fract Engng Mater Struct. 22:1999;601-607.
19. Murakami Y., Nomoto T., Ueda T. Factors influencing the mechanisms of superlong fatigue failure in steels. Fatigue Fract Engng Mater Struct. 22:1999;581-590.
20. Huneau B. Influence de l'air ou de milieux salins avec polarisation cathodique sur les processus d'endommagement par fatigue d'un acier à haute limite d'élasticité. PhD thesis, ENSMA, 2000 [in French].