Oxidation-induced strength behavior of Ti3SiC2

Journal of Materials Processing Technology

Volumn 209, Issue 2, 2009, Pages 641-646

  Sarkar, D ^a   Padhiary, A ^a   Cho, S J ^b   Chu, M C ^b  

^a NATIONAL INSTITUTE OF TECHNOLOGY   (India)

^b Korea Research Institute of Standards and Science   (South Korea)

Author keywords

Flexural Strength; Oxidation; Ti3SiC2

Indexed keywords

BENDING STRENGTH; MECHANICAL PROPERTIES; OXIDATION; SCALE (DEPOSITS); SILICON CARBIDE; STRENGTH OF MATERIALS; THERMAL SPRAYING;

COEFFICIENT OF THERMAL EXPANSIONS; ELEVATED TEMPERATURES; FLEXURAL STRENGTH; FLEXURAL STRENGTHS; OXIDATION BEHAVIORS; OXIDE PHASES; OXIDE SCALES; STRENGTH BEHAVIORS; TI3SIC2;

THERMAL EXPANSION;

EID: 58149173506     PISSN: 09240136     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.jmatprotec.2008.02.060     Document Type: Article

References (19)

1. Bao Y.W., Zhou Y.C., Bu X.X., and Qiu Y. Evaluating elastic modulus and strength of hard coatings by relative method. Mater. Sci. Eng. A 458 (2007) 268-274
2. 2. J. Am. Ceram. Soc. 79 7 (1996) 1953-1956
3. Casas B., Ramis X., Anglada M., Salla J.M., and Llanes L. Oxidation-induced strength degradation of WC-Co hardmetals. Int. J. Refract. Metal Hard Mater. 19 (2001) 303-309
4. Chu M.C., Cho S.J., Yoon K.J., and Park H.M. Crack repairing in alumina by penetrating glass. J. Am. Ceram. Soc. 88 2 (2005) 491-493
5. Chu M.C., Cho S.J., Sarkar D., Basu B., Yoon G.J., and Park H.M. Oxidation-induced strengthening in ground SiC. J. Mater. Sci. 41 15 (2006) 4978-4980
6. Chu, M.C., Panigrahi, B.B., Balakkrishnan, A., Cho, S.J., Yoon, K.J., Kim, T.N., Lee, K.H., in press. Strengthening of alumina by a low thermal expansion glass at surface. Mater. Sci. Eng. A.
7. 2. Part II. Mechanical properties. J. Am. Ceram. Soc. 82 (1999) 2855-2859
8. 2 in the 25-1400 °C temperature range. J. Am. Ceram. Soc. 88 (12), 3489-3491.
9. 2 in argon and air by neutron diffraction. Physica B.
10. 2. J. Eur. Ceram. Soc. 5 (1989) 283
11. 2. J. Mater. Sci. 29 (1994) 3384
12. 2 in the 25-1300 °C temperature range. Acta Mater. 48 (2000) 453-459
13. 2-based structural ceramics. Arch. Metall. 42 (1997) 59
14. 2. J. Am. Ceram. Soc. 88 11 (2005) 3245-3248
15. 2. Ceram. Int. 33 (2007) 789-793
16. 2. J. Eur. Ceram. Soc. 26 13 (2006) 2441-2452
17. Sarkar D., Basu B., Chu M.C., and Cho S.J. Is glass infiltration beneficial to improve fretting wear properties for alumina?. J. Am. Ceram. Soc. 90 2 (2007) 523-532
18. 2 content and grain size on the thermo-mechanical properties of nano-ZTA. Ceram. Int. 33 2 (2007) 255-261
19. 2 induced by compression at temperatures below 1000 °C. Mater. Sci. Eng. A 408 (2005) 64-71