Temperature dependence of blistering and deuterium retention in tungsten exposed to high-flux and low-energy deuterium plasma

Fusion Engineering and Design

Volumn 83, Issue 7-9, 2008, Pages 1044-1048

  Shu, W M ^a   Isobe, K ^a   Yamanishi, T ^a  

^a JAPAN ATOMIC ENERGY AGENCY   (Japan)

Author keywords

Blistering; Deuterium; Plasma; Retention; Tungsten; Vacancy

Indexed keywords

DESORPTION; FOCUSED ION BEAMS; HYDROGEN; PLASMAS; SURFACE CHEMISTRY; TEMPERATURE DISTRIBUTION; THERMAL DESORPTION; TUNGSTEN; VACANCIES;

BLISTERING; DEUTERIUM PLASMAS; DEUTERIUM RETENTIONS; EXPOSURE TEMPERATURES; RETENTION; TEMPERATURE DEPENDENCES; TEMPERATURE RANGES;

DEUTERIUM;

EID: 56949094303     PISSN: 09203796     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.fusengdes.2008.05.006     Document Type: Article

References (15)

1. Federici G., Skinner C.H., Brooks J.N., Coad J.P., Grisolia C., Haasz A.A., et al. Plasma-material interactions in current tokamaks and their implications for next step fusion reactors. Nucl. Fusion 41 (2001) 1967-2137
2. 3 tungsten in a high ion flux, low ion energy, low carbon impurity plasma environment for the International Thermonuclear Experimental Reactor. J. Nucl. Mater. 264 (1999) 89-98
3. Wang W., Roth J., Lindig S., and Wu C.H. Blister formation of tungsten due to ion bombardment. J. Nucl. Mater. 299 (2001) 124-131
4. Venhaus T., Causey R., Doerner R., and Abeln T. Behavior of tungsten exposed to high fluences of low energy hydrogen isotopes. J. Nucl. Mater. 290-293 (2001) 505-508
5. Shu W.M., Wakai E., and Yamanishi Y. Blister bursting and deuterium bursting release from tungsten exposed to high fluences of high flux and low energy deuterium plasma. Nucl. Fusion 47 (2007) 201-209
6. Shu W.M., Luo G.-N., and Yamanishi T. Mechanisms of retention and blistering in near-surface region of tungsten exposed to high flux deuterium plasmas of tens of eV. J. Nucl. Mater. 367-370 (2007) 1463-1467
7. Shu W.M., Kawasuso A., and Miwa Y. Microstructure dependence of deuterium retention and blistering in the near-surface region of tungsten exposed to high flux deuterium plasmas of 38 eV at 315 K. Phys. Scr. T128 (2007) 96-99
8. Scherzer B.M.U. Development of surface topography due to gas ion implantation. In: Behrisch R. (Ed). Sputtering by Particle Bombardment II (1983), Springer-Verlag 271-355
9. van Veen A., Filius H.A., de Vries J., Bijerk K.R., Rozing G.J., and Segers D. Hydrogen exchange with voids in tungsten observed with TDS and PA. J. Nucl. Mater. 155-157 (1988) 1113-1117
10. Pick M.A., and Sonnenberg K. A model for atomic hydrogen-metal interactions-application to recycling, recombination and permeation. J. Nucl. Mater. 131 (1985) 208-220
11. + irradiation on D trapping in single crystal tungsten. J. Nucl. Mater. 337-339 (2005) 629-633
12. Alimov V.Kh., Roth J., and Mayer M M. Depth distribution of deuterium in single- and polycrystalline tungsten up to depths of several micrometers. J. Nucl. Mater. 337-339 (2005) 619-623
13. Fukai Y., and Okuma N. Formation of superabundant vacancies in Pd hydride under high hydrogen pressures. Phys. Rev. Lett. 73 (1994) 1640-1643
14. Fukai Y., Ishii Y., Goto Y., and Watanabe K. Formation of superabundant vacancies in Pd-H alloys. J. Alloys Comp. 313 (2000) 121-132
15. Garner F.A., Simonen E.P., Oliver B.M., Greenwood L.R., Grossbeck M.L., Wolfer W.G., et al. Retention of hydrogen in fcc metals irradiated at temperatures leading to high densities of bubbles or voids. J. Nucl. Mater. 356 (2006) 122-135