New electrical potential method for measuring crack growth in nonconductive materials

Measurement: Journal of the International Measurement Confederation

Volumn 36, Issue 2, 2004, Pages 121-129

  Nayeb Hashemi, H ^a   Swet, D ^a   Vaziri, A ^a  

^a Northeastern University   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ADHESIVE JOINTS; CARBON; CONDUCTIVE MATERIALS; CRACK INITIATION; ELECTRIC POTENTIAL; ELECTRIC RESISTANCE; PAINT; SCANNING ELECTRON MICROSCOPY;

CARBON PAINTS; CRACK GROWTH MEASUREMENT; DC ELECTRIC POTENTIAL TECHNIQUE;

MECHANICAL VARIABLES MEASUREMENT;

EID: 4644349695     PISSN: 02632241     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.measurement.2004.05.002     Document Type: Article

References (17)

1. Wahab M.M.A., Ashcroft I.A., Crocombe A.D., Shaw S.J. Prediction of fatigue thresholds in adhesively bonded joints using damage mechanics and fracture mechanics. J. Adhesion Sci. Technol. 15(7):2001;763-781.
2. Ashcroft I.A., Shaw S.J. Mode I fracture of epoxy bonded composite joints 2. Fatigue loading. Int. J. Adhesion Adhesives. 22(2):2002;151-167.
3. Cheuk P.T., Tang L., Wang C.H., Baker A., Chalkley P. Fatigue crack growth in adhesively bonded composite-metal double-lap joints. Compos. Struct. 57(1):2002;109-115.
4. Imanaka M., Ishii K., Nakayama H. Evaluation of fatigue strength of adhesively bonded single and single step double lap joints based on stress singularity parameters. Eng. Fract. Mech. 62(4):1999;409-424.
5. American Society for Testing and Materials, "Designation E647-95a: Standard Test Method for Measurement of Fatigue Crack Growth Rates", 1997 Annual Book of ASTM Specifications, vol. 3.01, ASTM, Easton, MD, 1997, pp. 565-599.
6. Chai H. Bond thickness effect in adhesive joints and its significance fr mode I interlaminar fracture of composites. Whitney J.M. Composite Materials: Testing and Design, Seventh Conference, ASTM STP 893. 1986;209-231 American Society for Testing and Materials, Philadelphia.
7. Plausinis D., Spelt J.K. Application of a new constant. G load-jig to creep crack growth in adhesive joints Int. J. Adhesion Adhesives. 15:1995;225-232.
8. Naito K., Fujii T. Static and fatigue crack growth of epoxy adhesives and fractal dimensions. Int. J. Adhesion Adhesives. 18:1998;199-213.
9. Liniecki A., Hsu T.R., Li W. Fatigue strength of adhesive bonded aluminum joints. J. Testing Evaluat. 23(6):1995;453-468.
10. Devries K.L., Gramoll K.C., Andersen G.P. Analysis of tensile test methods. Polym. Eng. Sci. 26(13):1986;962-968.
11. Joseph R., Bell J., McEvily A.J., Liang J.L. Fatigue crack growth in epoxy/aluminum and epoxy/steel joints. J. Adhesion. 41:1993;169-187.
12. A.S. Kobayashi, Experimental Techniques in Fracture Mechanics, Society of Experimental Stress Analysis Monograph, No. 1, 1973, Arnzallag, Claude, Automation in Fatigue and Fracture Testing and Analysis, ASTM PCN 04-012310-30.
13. Abou-Hamda M.M., Megahed M.M., Hammouda M.M.I. Fatigue crack growth in double cantilever beam specimen with an adhesive layer. Eng. Fract. Mech. 60(5-6):1998;605-614.
14. M.M. Abou-Hamda, M.M. Megahed, Elasto-plastic analysis of double cantilever beam specimen with an adhesive layer, Current Advances in Mechanical Design and Production, Sixth Cairo University International MDP Conference, Cairo, Egypt, 1996, pp. 465-479.
15. H. Nayeb-Hashemi, M.E. Taslim, J. Zotos, M.D. Cohen, Effect of mode II over-load on subsequent mode I crack growth, Proceedings International Conference and Exposition on Fatigue, Corrosion Cracking, Fracture Mechanics and Failure Analysis Conference, December 2-6, Salt Lake City, Utah, 1985, pp. 387-398.
16. Mostovoy S., Ripling E.J. Flow tolerance of a number of commercial and experimental adhesives. J. Adhesion Sci. Technol. 9B:1975;64-80.
17. Chow C.L., Woo C.W., Sykes J.L. On the Determination and application of COD to epoxy-bonded aluminum joints. J. Strain Anal. 14(2):1979;37-42.