SCOPUS 정보 검색 플랫폼

International Journal of Adhesion and Adhesives

Volumn 22, Issue 2, 2002, Pages 151-167

Mode I fracture of epoxy bonded composite joints 2. Fatigue loading

(2) Ashcroft, I A a Shaw, S J b

a LOUGHBOROUGH UNIVERSITY (United Kingdom)

b DEFENCE SCIENCE AND TECHNOLOGY LABORATORY (United Kingdom)

Author keywords

A. Epoxides; B. Composites; C. Fracture mechanics; D. Fatigue; E. Environmental issues

Indexed keywords

BONDING; CARBON FIBER REINFORCED PLASTICS; CRACK PROPAGATION; DEGRADATION; ENVIRONMENTAL IMPACT; FATIGUE OF MATERIALS; FRACTURE; FRACTURE MECHANICS; STRAIN;

FATIGUE LOADING;

JOINTS (STRUCTURAL COMPONENTS);

EID: 0036193768 PISSN: 01437496 EISSN: None Source Type: Journal
DOI: 10.1016/S0143-7496(01)00050-1 Document Type: Article

Times cited : (112)

References (53)

1
- 0034825403
- Mode I fracture of epoxy bonded composite joints: Part 1. Quasi-static loading
- (2001) Int J Adhesion Adhesives , vol.21 , pp. 87-99
- Ashcroft, I.A.¹ Hughes, D.J.² Shaw, S.J.³

2
- 0034988975
- Effect of temperature in the quasi-static strength and fatigue resistance of bonded composite double lap joints
- (2001) J Adhesion , vol.75 , pp. 61-88
- Ashcroft, I.A.¹ Hughes, D.J.² Shaw, S.J.³ Abdel-Wahab, M.⁴ Crocombe, A.⁵

3
- 0003420977
- Englewood Cliffs, NJ: Prentice Hall
- (1990) Fundamentals of metal fatigue analysis
- Bannantine, J.A.¹ Comer, J.J.² Handrock, J.L.³

4
- 84963145351
- A backface strain technique for detecting fatigue crack initiation in adhesive joints
- (1995) J Adhesion , vol.49 , pp. 23-36
- Zhang, Z.¹ Shang, J.K.² Lawrence, F.V.³

5
- 0008667873
- Fatigue behaviour of adhesive bonded joints
- (1987) J Adhesion , vol.21 , pp. 115-128
- Chen, N.N.S.¹ Niem, P.I.F.² Lee, R.C.³

6
- 0026464425
- Fatigue life evaluation of structural adhesives for automotive applications
- (1992) Int J Adhesion Adhesives , vol.12 , pp. 9-18
- Harris, J.A.¹ Fay, P.A.²

7
- 0004258865
- Academic Press: New York
- (1980) Fatigue of engineering plastics
- Hertzberg, R.W.¹ Manson, J.A.²

8
- 0022215212
- Repeatability of mixed-mode adhesive debonding
- Philadelphia: American Society for Testing and Materials
- ASTM STP , vol.876 , pp. 267-281
- Everett, R.¹ Johnson, W.S.²

9
- 0019262571
- Fatigue crack growth in structural adhesives
- (1980) J Adhesion , vol.11 , pp. 125-143
- Jablonski, D.A.¹

10
- 0042034503
- Similarity concepts in the fatigue fracture of adhesively bonded joints
- (1987) J Adhesion , vol.21 , pp. 1-24
- Lin, C.¹ Liechti, K.M.²

11
- 0001398915
- Fatigue performance of two structural adhesives
- (1988) J Adhesion , vol.26 , pp. 273-291
- Luckyram, J.¹ Vardy, A.E.²

12
- 0028516389
- Fatigue behaviour of joints bonded with either filled, or filled and toughened, adhesive
- (1994) Int J Fatigue , vol.16 , pp. 469-477
- Xu, X.X.¹ Crocombe, A.D.² Smith, P.A.³

13
- 0031207892
- Observations of fatigue crack initiation and propagation in an epoxy adhesive
- (1997) Int J Adhesion Adhesives , vol.17 , pp. 183-195
- Dessureault, M.¹ Spelt, J.K.²

14
- 0023173974
- Stress ratio effect on cyclic debonding in adhesively bonded composite joints
- (1987) Compos Struct , vol.8 , pp. 31-45
- Mall, S.¹ Ramamurthy, G.² Rezaizdeh, M.A.³

15
- 0008641819
- The fatigue performance of adhesively bonded thick adherend steel joints
- Cambridge, UK
- (1996) Proceedings of the European Adhesion Conference , vol.1 , pp. 319-324
- Knox, E.M.¹ Tan, K.T.T.² Cowling, M.J.³ Hashim, S.A.⁴

16
- 0004031078
- London: Butterworths
- (1989) Fatigue thresholds
- Taylor, D.¹

17
- 84950007515
- Effect of adherend thickness and mixed mode loading on debond growth in adhesively bonded composite joints
- (1987) J Adhesion , vol.23 , pp. 263-288
- Mangalgiri, P.D.¹ Johnson, W.S.² Everett, R.A.³

18
- 4243584161
- Ph.D. thesis, Imperial College, London
- (1995) The fatigue performance of adhesively bonded metal joints
- Jethwa, J.K.¹

19
- 85165996794
- Characterization of matrix toughness effect on cyclic delamination growth in graphite fiber composites
- Philadelphia: American Society for Testing and Materials
- (1989) ASTM STP , vol.1012 , pp. 296-310
- Mall, S.¹ Yun, K.T.² Kochar, N.K.³

20
- 0023164419
- Delamination fatigue crack growth in unidirectional graphite/epoxy laminates
- (1987) J Reinforced Plast Compos , vol.6 , pp. 36-52
- Gustafson, C.G.¹ Hojo, M.²

21
- 0004214578
- London, UK: Edward Arnold
- (1984) Fracture mechanics
- Ewalds, H.L.¹

22
- 0008658098
- Effect of adhesive ductility on cyclic debond mechanism in composite-to-composite bonded joints
- (1987) J Adhesion , vol.23 , pp. 215-231
- Mall, S.¹ Yun, K.T.²

23
- 0030358265
- Fatigue crack growth rates in adhesive joints at different frequencies
- (1996) J Adhesion , vol.58 , pp. 191-204
- Xu, X.X.¹ Crocombe, A.D.² Smith, P.A.³

24
- 0022918661
- Characterization of mode I and mixed mode failure of adhesive bonds between composite adherends
- Philadelphia: American Society for Testing and Materials
- (1986) ASTM STP , vol.893 , pp. 322-334
- Mall, S.¹ Johnson, W.S.²

25
- 0029249568
- A new test method for determining the adhesive fracture energy when bonding thin or coated substrates
- (1995) J Mater Sci Lett , vol.14 , pp. 155-157
- Jethwa, J.K.¹ Kinloch, A.J.² Wallington, G.³

26
- 0000458697
- Flaw tolerance of a number of commercial and experimental adhesives
- (1975) Adhesion Sci Technol , vol.9 B , pp. 513-562
- Mostovoy, S.¹ Ripling, E.J.²

27
- 84950182119
- Predicting the fatigue life of adhesively bonded joints
- (1993) J Adhesion , vol.43 , pp. 79-90
- Kinloch, A.J.¹ Osiyemi, S.²

28
- 0031677106
- The fatigue and durability behaviour of automotive adhesives. Part III: Predicting the service life
- (1998) J Adhesion , vol.66 , pp. 39-59
- Curley, A.J.¹ Jethwa, J.K.² Kinloch, A.J.³ Taylor, A.C.⁴

29
- 0003420206
- Ph.D. thesis, Imperial College, London
- (1999) The durability of structural adhesive joints
- Little, M.S.G.¹

30
- 0025462281
- Technique and apparatus for automatic monitoring of crack propagation along glue lines
- (1990) J Mater Sci , vol.25 , pp. 3079-3082
- Pankevicius, E.R.¹ Spicer, M.²

31
- 0022305351
- Krak-gages for automated fatigue crack growth rate testing: A review
- Philadelphia: American Society for Materials and Testing
- (1985) ASTM STP , vol.877 , pp. 177-196
- Liaw, P.K.¹ Logsdon, W.A.² Roth, L.D.³ Hartmann, H.R.⁴

32
- 0020500645
- Corrosion fatigue crack propagation testing with the krak-gage in salt water
- (1983) Eng Fract Mech , vol.1 , pp. 121-1131
- Liaw, P.K.¹ Hartmann, H.R.² Helm, E.J.³

33
- 0000357002
- (1920) Phil Trans Roy Soc , vol.A221 , pp. 163
- Griffith, A.A.¹

34
- 0003831782
- European Structural Integrity Society: Polymers and Composites Task Group
- (1992) Protocols for interlaminar fracture testing of composites
- Davies, P.¹

35
- 33845257283
- Corrections needed in double-cantilever beam tests for assessing the interlaminar failure of fibre-composites
- (1989) J Mater Sci Lett , vol.8 , pp. 125
- Hashemi, S.¹ Kinloch, A.J.² Williams, J.G.³

36
- 0000514565
- Use of crack-line-loaded specimens for measuring plane strain fracture toughness
- (1967) J Mater , vol.2 , pp. 661-681
- Mostovoy, S.¹ Crosley, P.B.² Ripling, E.J.³

37
- 0027148778
- A closed form solution for the energy release rate of the double cantilever beam specimen with an adhesive layer
- (1993) J Compos Mater , vol.27 , pp. 383-407
- Penado, F.E.¹

38
- 0026652164
- A simplified improved beam analysis of the DCB specimen
- (1992) Compos Sci Technol , vol.43 , pp. 329-338
- Olsson, R.¹

39
- 0023330852
- Large displacement and end block effects in the 'DCB' interlaminar test in modes I and II
- (1987) J Compos Mater , vol.21 , pp. 331-347
- Williams, J.G.¹

40
- 0003965621
- Mixed -mode delamination growth in carbon-fibre composites under fatigue loading
- (1996) DRA Technical Report DRA/SMC/CR961052/1.0
- Singh, S.¹ Greenhalgh, E.²

41
- 0004289081
- Barking, UK: Applied Science Publishers
- (1983) Fracture behaviour of polymers
- Kinloch, A.J.¹ Young, R.J.²

42
- 0021607182
- Chichester, UK: Ellis Horwood
- (1984) Fracture mechanics of polymers
- Williams, J.G.¹

43
- 0022756061
- (1986) J Mater Sci , vol.21 , pp. 2462
- Yee, A.F.¹ Pearson, R.A.²

44
- 0023847002
- Failure mechanisms in toughened epoxy resins - A review
- (1988) Compos Sci Technol , vol.31 , pp. 179-223
- Garg, A.C.¹ Mai, Y.W.²

45
- 4243920305
- Ph.D. thesis, Imperial College, London
- (1999) The fatigue behaviour of toughened epoxy polymers
- Oba, T.¹

46
- 0342420600
- The effect of environment on the fatigue of bonded composite joints. Part 1: Testing and fractography
- (2001) Composites: Part A , vol.32 , pp. 45-58
- Ashcroft, I.A.¹ Abdel-Wahab, M.M.² Crocombe, A.D.³ Hughes, D.J.⁴ Shaw, S.J.⁵

47
- 0010052526
- Fracture mechanics for structural adhesive bonds - Final report
- Air Force Materials Laboratory
- (1977) AFML TR-77-163
- Brussat, T.R.¹ Chiu, S.T.²

48
- 0001922359
- The effect of geometry on the fracture of adhesive joints
- (1994) Int J Adhesion Adhesives , vol.14 , pp. 5-13
- Papini, M.¹ Fernlund, G.² Spelt, J.K.³

49
- 0023455220
- Stress analysis of the cracked-lap-shear specimen: An ASTM round robin
- (1987) J Test Eval , vol.15 , pp. 303-324
- Johnson, W.S.¹

50
- 0008658099
- Characterization of mode I and mixed-mode failure of adhesive bonds between composite adherends
- National Aeronautics and Space Administration
- (1985) NASA-TM-86355
- Mall, S.¹ Johnson, W.S.²

51
- 0342420609
- The effect of environment on the fatigue of bonded composite joints. Part 2: Fatigue threshold prediction
- (2001) Composites: Part A , vol.32 , pp. 59-69
- Abdel-Wahab, M.M.¹ Ashcroft, I.A.² Crocombe, A.D.³ Hughes, D.J.⁴ Shaw, S.J.⁵

52
- 0038122982
- Prediction of fatigue thresholds in adhesively bonded joints using damage mechanics and fracture mechanics
- (2001) J Adhesion Sci Technol , vol.15 , pp. 763-782
- Abdel-Wahab, M.M.¹ Ashcroft, I.A.² Crocombe, A.D.³ Shaw, S.J.⁴

53
- 0029208766
- Finite element analysis of crack growth in adhesively bonded joints
- (1995) Int J Adhesion Adhesives , vol.15 , pp. 33-41
- Pradhan, S.C.¹ Iyengar, N.G.R.² Kishore, N.N.³

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.