Evaluation of fatigue strength of adhesively bonded single and single step double lap joints based on stress singularity parameters

Engineering Fracture Mechanics

Volumn 62, Issue 4-5, 1999, Pages 409-424

  Imanaka, M ^a   Ishii, K ^b   Nakayama, H ^c  

^a OSAKA KYOIKU UNIVERSITY   (Japan)

^b OSAKA SANGYO UNIVERSITY   (Japan)

^c Sch Juridical Person Osaka S   (Japan)

Author keywords

Adhesive bonded joints; Cracked lap joint; Fatigue strength; Life prediction; Single lap joint; Single step double lap joint; Stress singularity parameter

Indexed keywords

ADHESIVE JOINTS; INTERFACES (MATERIALS); STRENGTH OF MATERIALS; STRESS CONCENTRATION;

ADHESIVE BONDED JOINTS; STRESS SINGULARITY PARAMETER;

FATIGUE OF MATERIALS;

EID: 0032657044     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/s0013-7944(98)00111-8     Document Type: Article

References (18)

1. Liee D.G., Kim K.S., IM Y.T. An experimental study of fatigue strength for adhesively bonded tubular single joints. J. Adhes. 35:1991;39-53.
2. Schmuser D.W. A fracture mechanics approach to characterizing cyclic debonding of varied thickness adhesive joints to electroprimed steel surfaces. J. Adhes. 36:1991;1-23.
3. Gilchrist M.D., Smith R.A. Fatigue growth of cohesive defects in T-peel joints. J. Adhes. 42:1993;179-190.
4. Joseph R., Bell J.P., Mcevily A.J., Liang J.L. Fatigue crack growth in epoxy/aluminum and epoxy/steel joints. J. Adhes. 41:1993;169-187.
5. Kinloch A.J., Osiyemi S.O. Predicting the fatigue life of adhesively-bonded joints. J. Adhes. 43:1993;79-90.
6. Aglan H. Fatigue lifetime assessment of adhesive joints by ultrasonic and thermal wave imaging. J. Adhes. Sci. Technol. 8:1994;101-115.
7. Liniecki A., Hsu T.R., Li W. Fatigue strength of adhesive bonded aluminum joints. J. Test. Eval. 23:1995;453-468.
8. Miyazaki K., Fujii T. Fatigue crack propagation of rubber toughened epoxy adhesive under mode 1 loading (Effect of rubber content and adhesive thickness on fatigue crack growth. Trans. Jpn Mech. Engng. Ser. A. 61:1995;1212-1217. (in Japanese).
9. Imanaka M., Iwata T. Fatigue failure criterion of adhesively-bonded joints under combined stress conditions. J. Adhes. 59:1996;111-126.
10. Imanaka M., Iwata T. Effect of adhesive layer thickness on fatigue strength of adhesively bonded butt, scarf and butterfly type butt joints. Int. J. Fract. 80:1996;R69-R76.
11. Hattori T., Sakata S., Hatsuda T., Murakami G. A stress singularity parameter approach for evaluating adhesive strength. JSME Int. J. Ser. 1. 31:1988;718-723.
12. Hattori T. A stress-singularity-parameter approach for evaluating the adhesive strength of single-lap joints. JSME Int. J. Ser. 1. 34:1991;326-331.
13. Yuuki R. Mechanics of interface. 1993;Baifuukan. (in Japanese).
14. Adams R.D., Wake W.C. Structural adhesive joints in engineering. 1986;Elsevier Applied Science, London.
15. Chen D.H., Nisitani H. Stress fields near the corner of jointed dissimlar materials. Trans. Jpn Soc. Mech. Engng. Ser. A. 57:1991;366-372. (in Japanese).
16. Chen D.H., Nisitani H. Singular stress fields near a corner of jointed dissimilar materials. Trans. Jpn Soc. Mech. Engng. Ser. A. 57:1991;2509-2515. (in Japanese).
17. Nielsen L.E. Mechanical properties of polymers and composites. 1965;Marcel Dekker, New York.
18. Taylor D. Fatigue thresholds. 1989;Butterworths, London.