A pyrrole-containing surfactant as a tecton for nanocomposite SiO 2 films

Langmuir

Volumn 23, Issue 22, 2007, Pages 11273-11280

  Kaper, Helena ^a   Franke, Danielle ^a   Smarsly, Bernd M ^a,b   Faul, Charl F J ^c  

^a MAX PLANCK INSTITUTE OF COLLOIDS AND INTERFACES   (Germany)

^b JUSTUS LIEBIG UNIVERSITY   (Germany)

^c UNIVERSITY OF BRISTOL   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

DIFFERENTIAL SCANNING CALORIMETRY; NANOCOMPOSITES; OXIDE FILMS; POLYMERIZATION; POLYPYRROLES; SILICA;

BILAYER STRUCTURES; EVAPORATION-INDUCED SELF-ASSEMBLY (EISA);

SURFACE ACTIVE AGENTS;

EID: 35948988504     PISSN: 07437463     EISSN: None     Source Type: Journal    
DOI: 10.1021/la701911n     Document Type: Article

References (33)

1. Kato, T.; Mizoshita, N.; Kishimoto, K. Angew. Chem., Int. Ed. 2006, 45, 38.
2. Hamley, I. W. Soft Matter 2005, 1, 36.
3. Smarsly, B.; Antonietti, M. Eur. J. Inorg. Chem. 2006, 1111.
4. Davis, J. T. Angew. Chem., Int. Ed. 2004, 43, 668.
5. Zhang, S. G. Nat. Biotechnol. 2003, 21, 1171.
6. Sanchez, C.; Julian, B.; Belleville, P.; Popall, M. J. Mater. Chem. 2005, 15, 3559.
7. Ikkala, O.; ten Brinke, G. Chem. Commun. 2004, 2131.
8. Faul, C. F. J.; Antonietti, M. Adv. Mater. 2003, 15, 673.
9. Ward, M. D. Chem. Commun. 2005, 5838.
10. Hosseini, M. W. Chem. Commun. 2005, 5825.
11. Ozin, G. A.; Manners, I.; Fournier-Bidoz, S.; Arsenault, A. Adv. Mater. 2005, 17, 3011.
12. Lehn, J. M. Proc. Natl. Acad. Sci. U.S.A. 2002, 99, 4163.
13. Hawker, C. J.; Wooley, K. L. Science 2005, 309, 1200.
14. Chiang, C. K.; Fincher, C. R.; Park, Y. W.; Heeger, A. J.; Shirakawa, H.; Louis, E. J.; Gau, S. C.; Macdiarmid, A. G. Phys. Rev. Lett. 1977, 39, 1098.
15. Wei, Z. X.; Laitinen, T.; Smarsly, B.; Ikkala, O.; Faul, C. F. J. Angew. Chem., Int. Ed. 2005, 44, 751.
16. Ikeda, T.; Tsutsumi, O. Science 1995, 268, 1873.
17. Hartmann, M. Chem. Mater. 2005, 17, 4577.
18. Ruland, W.; Smarsly, B. J. Appl. Crystallogr. 2004, 37, 575.
19. Garnweitner, G.; Smarsly, B.; Assink, R.; Dunphy, D. R.; Scullin, C.; Brinker, C. J. Langmuir 2004, 20, 9811.
20. Kadam, J.; Faul, C. F. J.; Scherf, U. Chem. Mater. 2004, 16, 3867.
21. Zakrevskyy, Y.; Smarsly, B.; Stumpe, J.; Faul, C. F. J. Phys. Rev. E 2005, 71, 021701:1.
22. Ikegame, M.; Tajima, K.; Aida, T. Angew. Chem., Int. Ed. 2003, 42, 2154.
23. Franke, D.; Egger, C. C.; Smarsly, B.; Faul, C. F. J.; Tiddy, G. J. T. Langmuir 2005, 21, 2704.
24. Zhang, T. R.; Spitz, C.; Antonietti, M.; Faul, C. F. J. Chem. - Eur. J. 2005, 11, 1001.
25. For the slower cooling rate, the range investigated was from -40 to 170°C. This was done to reduce the time the samples were left at high temperatures so as to avoid possible polymerization.
26. Muller, A. Proc. R. Soc. London, Ser. A 1932, 138, 514.
27. Brinker, C. J.; Lu, Y. F.; Sellinger, A.; Fan, H. Y. Adv. Mater. 1999, 11, 579.
28. Ogawa, M. Langmuir 1997, 13, 1853.
29. The Aldrich Library of Infrared Spectra, 3rd ed.; 1981.
30. Wang, T. W.; Kaper, H.; Antonietti, M.; Smarsly, B. Langmuir 2007, 23 (3), 1489.
31. Kaper, H.; Smarsly, B. Z. Phys. Chem. 2006, 220 (10-11), 1455.
32. Sel, O.; Kuang, D. B.; Thommes, M.; Smarsly, B. Langmuir 2006, 22, 2311.
33. Kuang, D. B.; Brezesinski, T.; Smarsly, B. J. Am. Chem. Soc. 2004, 126, 10534.