Bending fatigue characteristics of nanohoneycomb structures

Composite Structures

Volumn 82, Issue 1, 2008, Pages 28-35

  Jeon, J H ^a   Lee, P S ^a   Lee, K H ^a   Park, H C ^a   Hwang, W ^a  

^a Pohang University of Science and Technology (POSTECH)   (South Korea)

Author keywords

AAO; Nano UTM; Nanohoneycomb; Three point bending fatigue

Indexed keywords

BEAMS AND GIRDERS; BENDING (DEFORMATION); CYCLIC LOADS; FATIGUE OF MATERIALS;

ANODIC ALUMINUM OXIDE; NANO-UNIVERSAL TESTING MACHINE; NANOHONEYCOMB STRUCTURES; THREE-POINT BENDING FATIGUE;

HONEYCOMB STRUCTURES;

BENDING PROPERTY; COMPOSITE; COMPOSITE PROPERTY; FATIGUE; LOADING (TESTING); METAL; OXIDE; STRUCTURAL PROPERTY;

EID: 34548683675     PISSN: 02638223     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compstruct.2006.11.007     Document Type: Article

References (12)

1. Hynes A.M., et al. Recent advances in silicon etching for MEMS using the ASE process. Sensors Actuators A - Phys 74 (1999) 13-17
2. Gad-el-Hak M., et al. The MEMS handbook (2002), CRC Press [Chapter 17]
3. Masuda H., et al. Ordered metal nanohole arrays made by a two-step replication of honeycomb structures of anodic alumina. Science 268 (1995) 1466-1468
4. Nielsch K., et al. Hexagonally ordered 100 nm period nickel nanowire arrays. Appl Phys Lett 79 (2001) 1360-1362
5. Karmhag R., et al. Oxidation kinetics of nickel particles: comparison between free particles and particles in an oxide matrix. Solar Energy 68 (2000) 329-333
6. Che G., et al. Carbon nanotube membranes for electrochemical energy storage and production. Nature 393 (1998) 346-349
7. Che G., et al. Chemical vapor deposition based synthesis of carbon nanotubes and nanofibers using a template method. Chem Mater 10 (1998) 260-267
8. Zhang Z.B., et al. Processing and characterization of single-crystalline ultrafine bismuth nanowires. Chem Mater 11 (1999) 1659-1665
9. Sauer G., et al. Highly ordered monocrystalline silver nanowire arrays. J Appl Phys 91 (2002) 3243-3247
10. Jee S.E., et al. Fabrication of microstructures by wet etching of anodic aluminum oxide substrates. Chem Mater 17 (2005) 4049-4052
11. Hwang W., et al. Single- and multi-stress level fatigue life prediction of glass/epoxy composites. J Adv Mater 26 4 (1995) 3-9
12. Kim D.H., et al. Fatigue characteristics of surface antenna structure designed for satellite communication. J Reinf Plast Compos 24 1 (2005) 35-51