Fatigue testing of a NiTi rotary instrument. Part 2: Fractographic analysis

Author keywords

Breakage; Corrosion fatigue; Failure; Nickel titanium; Root canal preparation; Strain life analysis

Indexed keywords

DENTAL ALLOY; NICKEL; TITANIUM; TITANIUM NICKELIDE; UNCLASSIFIED DRUG; WATER;

EID: 34547312762     PISSN: 01432885     EISSN: 13652591     Source Type: Journal    
DOI: 10.1111/j.1365-2591.2007.01256.x     Document Type: Article
Times cited : (59)

References (21)
  • 3
    • 0003932898 scopus 로고    scopus 로고
    • ASM International (. Materials Park, OH: ASM International.
    • ASM International (1996) ASM Handbook, Vol. 19: Fatigue and Fracture. Materials Park, OH : ASM International.
    • (1996) ASM Handbook, Vol. 19: Fatigue and Fracture.
  • 4
    • 22544455071 scopus 로고    scopus 로고
    • Decrease in the fatigue resistance of nickel-titanium rotary instruments after clinical use in curved root canals
    • Bahia MG, Buono VT (2005) Decrease in the fatigue resistance of nickel-titanium rotary instruments after clinical use in curved root canals. Oral Surgery Oral Medicine Oral Pathology Oral Radiology and Endodontics 100, 249 55.
    • (2005) Oral Surgery Oral Medicine Oral Pathology Oral Radiology and Endodontics , vol.100 , pp. 249-55
    • Bahia, M.G.1    Buono, V.T.2
  • 8
    • 34547239216 scopus 로고    scopus 로고
    • Fatigue testing of a NiTi rotary instrument. Part1: Strain-life relationship
    • in press.
    • Cheung GSP, Darvell BW (2007) Fatigue testing of a NiTi rotary instrument. Part1: strain-life relationship. International Endodontic Journal, in press.
    • (2007) International Endodontic Journal
    • Cheung, G.S.P.1    Darvell, B.W.2
  • 10
    • 0001884238 scopus 로고
    • Ti-Ni shape memory alloys
    • In: Boyer, R., Welsch, G., Collings, E.W., eds. Materials Park, OH: ASM International, pp.
    • Duerig TW, Pelton AR (1994) Ti-Ni shape memory alloys. In : Boyer R, Welsch G, Collings EW, eds. Materials Properties Handbook: Titanium Alloys. Materials Park, OH : ASM International, pp. 1035 48.
    • (1994) Materials Properties Handbook: Titanium Alloys. , pp. 1035-48
    • Duerig, T.W.1    Pelton, A.R.2
  • 14
    • 0033527928 scopus 로고    scopus 로고
    • Fatigue-crack propagation in nitinol, a shape-memory and superelastic endovascular stent material
    • McKelvey AL, Ritchie RO (1999) Fatigue-crack propagation in nitinol, a shape-memory and superelastic endovascular stent material. Journal of Biomedical Materials Research 47, 301 8.
    • (1999) Journal of Biomedical Materials Research , vol.47 , pp. 301-8
    • McKelvey, A.L.1    Ritchie, R.O.2
  • 16
    • 5444247733 scopus 로고    scopus 로고
    • Factors influencing defects of rotary nickel-titanium endodontic instruments after clinical use
    • Parashos P, Gordon I, Messer HH (2004) Factors influencing defects of rotary nickel-titanium endodontic instruments after clinical use. Journal of Endodontics 30, 722 5.
    • (2004) Journal of Endodontics , vol.30 , pp. 722-5
    • Parashos, P.1    Gordon, I.2    Messer, H.H.3
  • 17
    • 22544487199 scopus 로고    scopus 로고
    • Defects in ProTaper S1 instruments after clinical use: Longitudinal examination
    • Peng B, Shen Y, Cheung GSP, Xia TJ (2005) Defects in ProTaper S1 instruments after clinical use: longitudinal examination. International Endodontic Journal 38, 550 7.
    • (2005) International Endodontic Journal , vol.38 , pp. 550-7
    • Peng, B.1    Shen, Y.2    Cheung, G.S.P.3    Xia, T.J.4
  • 19
    • 1942503388 scopus 로고    scopus 로고
    • Comparative investigation of two rotary nickel-titanium instruments: ProTaper versus RaCe. Part 2. Cleaning effectiveness and shaping ability in severely curved root canals of extracted teeth
    • Schäfer E, Vlassis M (2004) Comparative investigation of two rotary nickel-titanium instruments: ProTaper versus RaCe. Part 2. Cleaning effectiveness and shaping ability in severely curved root canals of extracted teeth. International Endodontic Journal 37, 239 48.
    • (2004) International Endodontic Journal , vol.37 , pp. 239-48
    • Schäfer, E.1    Vlassis, M.2
  • 20
    • 33644645409 scopus 로고    scopus 로고
    • Failure mechanism of ProTaper nickel-titanium rotary instruments during clinical use: Fractographic analysis
    • Spanaki-Voreadi AP, Kerezoudis NP, Zinelis S (2006) Failure mechanism of ProTaper nickel-titanium rotary instruments during clinical use: fractographic analysis. International Endodontic Journal 39, 171 8.
    • (2006) International Endodontic Journal , vol.39 , pp. 171-8
    • Spanaki-Voreadi, A.P.1    Kerezoudis, N.P.2    Zinelis, S.3
  • 21
    • 0036635798 scopus 로고    scopus 로고
    • The effect of rotational speed and the curvature of root canals on the breakage of rotary endodontic instruments
    • Zelada G, Varela P, Martín B, Bahíllo JG, Magán F, Ahn S (2002) The effect of rotational speed and the curvature of root canals on the breakage of rotary endodontic instruments. Journal of Endodontics 28, 540 2.
    • (2002) Journal of Endodontics , vol.28 , pp. 540-2
    • Zelada, G.1    Varela, P.2    Martín, B.3    Bahíllo, J.G.4    Magán, F.5    Ahn, S.6


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.