Role of core support material in veneer failure of brittle layer structures

Journal of Biomedical Materials Research - Part B Applied Biomaterials

Volumn 82, Issue 1, 2007, Pages 115-121

  Hermann, Ilja ^a   Bhowmick, Sanjit ^a   Lawn, Brian R ^a  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

Author keywords

Alumina; Cone cracks; Cyclic fatigue; Dental crowns; Residual stress; Slow crack growth; Zirconia

Indexed keywords

ALUMINA; GLASS; GRAFT VS. HOST REACTIONS; RESIDUAL STRESSES; THERMAL EXPANSION; VIDEO CAMERAS; ZIRCONIA;

CYCLIC FATIGUE; DENTAL CROWNS; SLOW CRACK GROWTH;

DENTAL COMPOSITES;

ALUMINUM OXIDE; GLASS; ZIRCONIUM OXIDE;

ARTICLE; CERAMIC PROSTHESIS; DENTIN; MECHANICAL STRESS; PHYSICAL MOBILITY; PROSTHESIS FAILURE; RIGIDITY; STRENGTH; TOOTH CROWN; VIDEORECORDING;

ALUMINUM OXIDE; DENTAL RESTORATION FAILURE; DENTAL VENEERS; GLASS; HEAT; MATERIALS TESTING; STRESS, MECHANICAL; ZIRCONIUM;

EID: 34347339409     PISSN: 15524973     EISSN: 15524981     Source Type: Journal    
DOI: 10.1002/jbm.b.30712     Document Type: Article

References (18)

1. Frank FC, Lawn BR. On the theory of Hertzian fracture. Proc R Soc London A 1967;299:291-306.
2. Lawn BR. Indentation of ceramics with spheres: A century after Hertz. J Am Ceram Soc 1998;81:1977-1994.
3. Zhang Y, Bhowmick S, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: Monoliths. J Mater Res 2005;20:2021-2029.
4. Bhowmick S, Zhang Y, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: Bilayer structures. J Mater Res 2005;20:2792-2800.
5. Zhang Y, Kwang J-K, Lawn BR. Deep penetrating conical cracks in brittle layers from hydraulic cyclic contact. J Biomed Mater Res B Appl Biomater 2005;73:186-193.
6. Hermann I, Bhowmick S, Zhang Y, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: Trilayer structures. J Mater Res 2006;21:512-521.
7. McLean JW. The Science and Art of Dental Ceramics, Vol. 1: The Nature of Dental Ceramics and Their Clinical Use. Chicago: Quintessence; 1979.
8. Lee KS, Jung Y-G, Peterson IM, Lawn BR, Kim DK, Lee SK. Model for cyclic fatigue of quasiplastic ceramics in contact with spheres. J Am Ceram Soc 2000;83:2255-2262.
9. Lawn BR, Deng Y, Miranda P, Pajares A, Chai H, Kim DK. Overview: Damage in brittle layer structures from concentrated loads. J Mater Res 2002;17:3019-3036.
10. Taskonak B, Mecholsky JJ, Anusavice KJ. Residual stresses in bilayer dental ceramics. Biomaterials 2005;26:3235-3241.
11. Chai H, Lawn BR. Role of adhesive interlayer in transverse fracture of brittle layer structures. J Mater Res 2000;15:1017-1024.
12. Chai H, Lawn BR, Wuttiphan S. Fracture modes in brittle coatings with large interlayer modulus mismatch. J Mater Res 1999;14:3805-3817.
13. Schwarzer N, Chudoba T, Pharr GM. On the evaluation of stress in coated materials during nanoindentation with sharp indenters. Surf Coat Technol 2006;200:4220-4226.
14. Jung YG, Wuttiphan S, Peterson IM, Lawn BR. Damage modes in dental layer structures. J Dent Res 1999;78:887-897.
15. Deng Y, Miranda P, Pajares A, Guiberteau F, Lawn BR. Fracture of ceramic/ceramic/polymer trilayers for biomechanical applications. J Biomed Mater Res A 2003;67:828-833.
16. Miranda P, Pajares A, Guiberteau F, Deng Y, Zhao H, Lawn BR. Designing damage-resistant brittle-coating structures. II. Trilayers. Acta Mater 2003;51:4357-4365.
17. Chevalier J. What future for zirconia as a biomaterial? Biomaterials 2006;27:535-543.
18. Willmann G. Improving bearing surfaces of artificial joints. Adv Eng Mater 2001;3:135-141.