J-Resistance curve testing of HY80 steel using SE(B) specimens and normalization method

Engineering Fracture Mechanics

Volumn 74, Issue 14, 2007, Pages 2263-2281

  Zhu, Xian Kui ^a   Joyce, James A ^b  

^a BATTELLE MEMORIAL INSTITUTE   (United States)

^b UNITED STATES NAVAL ACADEMY   (United States)

Author keywords

Elastic compliance method; Fracture testing; Fracture toughness; HY80 steel; J R curve; Normalization method; SE(B) specimen; Shallow crack

Indexed keywords

CRACK TIPS; ELASTICITY; FRACTURE TOUGHNESS; STANDARDS; STEEL TESTING;

ELASTIC COMPLIANCE METHOD; NORMALIZATION METHOD; RESISTANCE CURVE TEST METHOD;

FRACTURE TESTING;

CRACK TIPS; ELASTICITY; FRACTURE TESTING; FRACTURE TOUGHNESS; STANDARDS; STEEL TESTING;

EID: 34047224168     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfracmech.2006.10.018     Document Type: Article

References (28)

1. ASTM E 1820-01. Standard test method for measurement of fracture toughness. Annual book of ASTM standards vol. 03.01 (2005), American Society for Testing and Materials, West Conshohocken, PA
2. Joyce JA. J-Resistance curve testing of short crack bend specimens using unloading compliance. In: Fracture mechanics: twenty-second symposium, vol. I, ASTM STP 1131; 1992. p. 904-24.
3. Joyce JA, Hackett EM, Roe C. Effect of crack depth and mode of loading on the J-R curve behavior of a high-strength steel. In: Constraint effects in fracture, ASTM STP 1171; 1993. p. 239-63.
4. Joyce J.A., and Link R.E. Application of two parameter elastic-plastic fracture mechanics to analysis of structures. Engng Fract Mech 57 (1997) 431-446
5. Bakker A. A DC potential drop procedure for crack initiation and R-curve measurements during ductile fracture tests. In: Elastic-plastic fracture test methods: the user's experience, ASTM STP 586; 1985. p. 394-410.
6. Marscahll CW, Held PR, Landow MP, Mincer PN. Use of the direct-current electric potential method to monitor large amounts of crack growth in highly ductile metals. In: Fracture mechanics: twenty-first symposium, ASTM STP 1074; 1990. p. 581-93.
7. Herrera R., and Landes J.D. Direct J-R curve analysis of fracture toughness test. J Test Eval 16 (1988) 427-449
8. Herrera R, Landes JD. Direct J-R curve analysis: a guide to the methodology. In: Fracture mechanics: twenty-first symposium, ASTM STP 1074; 1990. p. 24-43.
9. Orange TW. Methods and models for R-curve instability calculations. In: Fracture mechanics: twenty-first symposium, ASTM STP 1074; 1990. p. 545-59.
10. Landes J.D., Zhou Z., Lee K., and Herrera R. Normalization method for developing J-R curves with the LMN function. J Test Eval 19 (1991) 305-311
11. Joyce J.A. Analysis of a high rate round robin based on proposed annexes to ASTM E 1820. J Test Eval 29 (2001) 329-351
12. Ernst HA, Paris PC, Landes JD. Estimations on J-integral and tearing modulus T from a single specimen test record. In: Fracture mechanics: thirteenth conference, ASTM STP 743; 1981. p. 476-502.
13. Sharobeam M.H., and Landes J.D. The load separation criterion and methodology in ductile fracture mechanics. Int J Fract 47 (1991) 81-104
14. Joyce JA, Ernst H, Paris PC. Direct J-R curve analysis: a guide to the methodology. In: Fracture mechanics: twelfth national symposium, ASTM STP 700; 1980. p. 222-36.
15. Scibetta M., Lucon E., Schuurmans J., and van Walle E. Numerical simulations to support the normalization data reduction technique. Engng Fract Mech 73 (2006) 524-534
16. Dzugan J., and Viehrig H.W. Application of the normalization method for the determination of J-R curves. Mater Sci Engng A 387-389 (2004) 307-311
17. Joyce J.A., and Joyce P.J. Toughness characterization of a metal filled polytetrafluoro-ethylene using the J-integral. Engng Fract Mech 71 (2004) 2513-2531
18. Zhu X.K., and Jang S.K. J-R curves corrected by load-independent constraint parameter in ductile crack growth. Engng Fract Mech 68 (2001) 285-301
19. Zhu X.K., and Leis B.N. Application of constraint corrected J-R curves to fracture analysis of pipelines. J Press Vess Technol 128 (2006) 581-589
20. Shen G, Tyson WR, Glover A, Horsley D. Constraint effects on linepipe toughness. In: Proceedings of the 4th international conference on pipeline technology, vol. 2, Ostend, Belgium; May 9-13, 2004. p. 703-20.
21. Sreenivasan P.R., and Mannan S.L. Plastic η-factor for three-point bend specimens: analysis of instrumented Charpy impact test results for AISI 308 weld and AISI 316 stainless steels. Int J Fract 101 (2000) 215-228
22. c determination for shallow notch welded bend specimens. Fatigue Fract Engng Mater Struct 10 (1987) 479-493
23. Link RE, Joyce JA. Experimental investigation of fracture toughness scaling models. In: Constraint effects in fracture theory and applications, vol. 2, ASTM STP 1244; 1995. p. 286-315.
24. Schindler HJ, Veidt M. Fracture toughness evaluation from instrumented sub-size Charpy-type tests. In: Small specimen test techniques, ASTM STP 1329; 1998. p. 48-62.
25. Wu S.X., Mai Y.W., and Cotterell B. Plastic η-factor of fracture specimens with deep and shallow cracks. Int J Fract 45 (1990) 1-18
26. Kirk M.T., and Dodds R.H. J and CTOD estimation equations for shallow cracks in single edge notch bend specimens. J Test Eval 21 (1993) 228-238
27. p-factor for structures with different geometries. Int J Fract 69 (1995) 251-267
28. Wallin K., and Laukkanen A. Improved crack growth corrections for J-R curve testing. Engng Fract Mech 71 (2004) 1601-1614