The role of residual stress in neutral pH stress corrosion cracking of pipeline steels - Part II: Crack dormancy

Acta Materialia

Volumn 55, Issue 1, 2007, Pages 43-53

  Chen, W ^a   Van Boven, G ^a   Rogge, R ^b  

^a UNIVERSITY OF ALBERTA   (Canada)

^b NATIONAL RESEARCH COUNCIL CANADA   (Canada)

Author keywords

Corrosion; Ferritic steels; Neutron diffraction; Residual stresses; Stress corrosion cracking

Indexed keywords

CRACKS; DISSOLUTION; NEUTRON DIFFRACTION; PH EFFECTS; PLASTIC DEFORMATION; RESIDUAL STRESSES; STRESS CORROSION CRACKING;

FERRITIC STEELS; MECHANICAL DRIVING FORCE; ROOM TEMPERATURE;

STEEL PIPE;

EID: 33751434623     PISSN: 13596454     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.actamat.2006.07.021     Document Type: Article

References (29)

1. Parkins R.N. A review of stress corrosion cracking of high pressure gas pipelines. Proceedings of corrosion 2000. Paper 00363 (2000), NACE International, Houston (TX)
2. Parkins RN. Investigations relating to environment sensitive fracture in the TransCanada Pipeline System. Report to TCPL; 1988.
3. Parkins R.N., Blanchard Jr. W.K., and Delanty B.S. Corrosion 50 (1993) 395
4. Parkins R.N., Blanchard W.K., and Delanty B.S. Stress corrosion cracking: a summary. Corrosion 50 (1994) 394
5. Van Boven G, Chen W, Rogge R, Sutherby RL. Acta Mater [accepted for publication].
6. King F, Given R, Chen W. Detailed characterization of SCC cracks from the Nordegg rupture site and their mechanistic implications. Internal Report #01442, Nova Research & Technology Corp., November; 2000.
7. Watson MK, Evitts RW, Wilmott MJ. Corrosion/96, Paper No. 251.
8. Chen W., King F., and Vokes E.D. Corrosion 58 3 (2002) 267
9. Chu R., Chen W., Wang S.-H., King F., Jack T.R., and Fessler R.R. Corrosion 60 3 (2004) 275
10. Chen W, Sutherby RL. Environmental effect of crack growth rate of pipeline steel in near-neutral pH soil environments. In: Proceedings of IPC 2004, international pipeline conference, October 4-8, Calgary, Alta., Canada; 2004. Paper No. IPC04-0449.
11. Eadie, unpublished results.
12. Beavers JA, Johnson JT, Sutherby RL. Materials factors influencing the initiation of near-neutral pH SCC on underground pipelines. In: Proceedings of 3th international pipeline conference, vol. 2, October 1-5, Calgary, Canada; 2000. p. 979-88.
13. Wang S., and Chen W. Corrosion 58 6 (2002) 526
14. Chen W., Wang S.-H., Chu R., King F., Jack T.R., and Fessler R.R. Metall Mater Trans A 34 (2003) 2601
15. Chen W, Eadie RL, Sutherby RL. Environmental effects on near-neutral pH stress corrosion cracking in pipelines. In: Second international conference on environment-induced cracking of metals, September 19-23, The Banff Centre, Banff, Alta., Canada; 2004.
16. Wang S., Zhang Y.G., and Chen W. J Mater Sci 36 (2001) 1931
17. Wang S., and Chen W. Mater Sci Eng A 301 (2001) 147
18. Tanaka K. Mechanics and micromechanics of fatigue crack propagation, ASTM STP 1020 (1989), American Society for Testing and Materials, Philadelphia (PA) p. 151-83
19. Tanaka K., and Nakai Y. Fatigue Eng Mater Struct 6 (1983) 315
20. El Haddad M.H., Topper T.H., and Smith K.N. Eng Fracture Mech 11 (1979) 573
21. Anderson T.L. Fracture mechanics: fundamentals and applications. 2nd ed. (1995), CRC Press, Boca Raton (FL)
22. Lambert SB, Beavers JA, Delanty B, Sutherby R, Plumtree A. Mechanical factors affecting stress corrosion crack growth rates in buried pipelines. In: 2000 International pipeline conference, vol. 2. p. 961.
23. Leis B.N., and Colwell J.A. Initiation of stress-corrosion cracking on gas transmission piping. Effects of the environment on the initiation of crack growth, Orlando, FL, 20-21 May 1996 (1997), American Society for Testing and Materials, Philadelphia (PA) 34-58
24. Chen W., and Zheng W. Progress in understanding of pipeline SCC: initiation and propagation. In: Chen W. (Ed). Pipelines for the 21st century (2005), Canadian Institute of Mines, Metallurgy and Petroleum 419-436
25. Qin Z., Demko B., Noel J., Shoesmith D., and King F. Corrosion 60 (2004) 906
26. Been J, Lu H, King F, Jack T, Sutherby R. The role of hydrogen in EAC of pipeline seels in near-neutral pH environments. EICM 2, Banff, AB, Canada, October; 2004.
27. Kushida T, Nose K, Asahi H, Kimura M, Yamane Y, Endo S, et al. Effects of metallurgical factors and test conditions on near-neutral pH SCC of pipeline steels. Corrosion 2001. Paper No. 01213.
28. Elboujdaini M, Wang YZ, Revie RW, Parkins RN, Shehata MT. Stress corrosion crack initiation processes: pitting and microcrack coalescence. NACE international corrosion 2000. Paper No. 00379 2000.
29. He D, Jack TR, King F, Chen W. Effect of surface scratch roughness and orientation on SCC of line pipe steel in neutral pH environment. In: 2000 International pipeline conference, vol. 2. p. 997-1004.