Volumn 58, Issue 3, 2002, Pages 267-275

Characteristics of near-neutral-pH stress corrosion cracks in an X-65 pipeline

Author keywords

Crack coalescence; Crack initiation; Crack morphology; Crack propagation; Near neutral pH stress corrosion cracking; Pipeline steel; Transgranular cracking

Indexed keywords

CRACKS; DISSOLUTION; HYDROGEN; PH EFFECTS; STEEL PIPE;

SPATIAL SEPARATION;

STRESS CORROSION CRACKING;

CORROSION; CRACKING; MORPHOLOGY; PH; PIPELINE; STRESS CORROSION CRACKING;

EID: 0036502938 PISSN: 00109312 EISSN: None Source Type: Journal
DOI: 10.5006/1.3279878 Document Type: Article

Times cited : (146)

References (26)

1
- 85031940773
- A review of stress corrosion cracking of high-pressure gas pipelines
- Paper no. 363 (Houston, TX: NACE International)
- (2000) CORROSION/2000
- Parkins, R.N.¹

2
- 0015383857
- (1972) Corrosion , vol.28 , pp. 313
- Sutcliffe, J.M.¹ Fessler, R.R.² Boyd, W.K.³ Parkins, R.N.⁴

3
- 0002500730
- (1996) J. Mech. Behavior of Mater , vol.7 , pp. 1
- Meletis, E.I.¹

4
- 0032066975
- (1998) Fatigue Fract. Eng. Mater. Struc , vol.21 , pp. 583
- Leis, N.¹ Parkins, R.N.²

5
- 0026878555
- (1992) Oil Gas J , vol.90 , Issue.24 , pp. 39
- Delanty, B.S.¹ O'Beirne, J.²

6
- 0028439127
- (1994) Corrosion , vol.50 , pp. 394
- Parkins, R.N.¹ Blanchard W.K., Jr.² Delanty, B.S.³

7
- 0003529062
- Report to TransCanada Pipelines. Ltd
- (1988) Investigations Relating to Environment Sensitive Fracture in the TransCanada Pipeline System
- Parkins, R.N.¹

8
- 0002912945
- Early stage of stress corrosion crack development of X-65 pipeline steel in near-neutral-pH solution
- ed. L. Collins (Montreal, Quebec: The Metallurgical Society of the Canadian Institute of Mining, Metallurgy and Petroleum)
- (1998) Materials for Resource Recovery and Transport , pp. 71
- Wang, Y.Z.¹ Revie, R.W.² Shehata, M.T.³

9
- 0002443533
- ASTM STP 1298, eds. W.A. Van Der Sluys, R.S. Piascik. R. Zawierucha (West Conshohocken, PA: ASTM)
- (1997) Effects of the Environment on Initiation of Crack Growth , pp. 34
- Leis, B.N.¹ Colwell, J.A.²

10
- 0003230889
- SCC susceptibility of X-70 steel in contact with various neutral-pH soil solutions
- paper no. 10 (Groningen, The Netherlands: Shell and Gasunie)
- (1999) EPRG/PRCI 12th Biennial Joint Tech Mtg
- Jack, T.R.¹ Wilmott, M.J.² Chen, W.³

11
- 34548172673
- Mechanistic aspects of stress corrosion crack initiation and early propagation
- Paper no. 143 (Houston, TX: NACE)
- (1999) CORROSION/99
- Wang, Y.-Z.¹ Revie, R.W.² Parkins, R.N.³

12
- 0002342328
- Mechanistic studies of near-neutral-pH SCC on underground pipelines
- eds. L. Collins. (Montreal, Quebec: The Metallurgical Society of the Canadian Institute of Mining, Metallurgy and Petroleum)
- (1998) Materials for Resource Recovery and Transport , pp. 31
- Beavers, J.A.¹ Durr, C.L.² Shademan, S.S.³

13
- 84994750430
- Effect of surface scratch roughness and orientation on the development of SCC of linepipe steel in near-neutral-pH evironment
- ed. J.R. Ellwood (Calgary, Canada: ASME)
- (2000) 2000 Int. Pipeline Conf , vol.2 , pp. 997
- He, D.¹ Chen, W.² Jack, T.R.³ King, F.⁴

14
- 84994718354
- Role of prior cyclic loading in the initiation of stress corrosion cracks on pipeline steels exposed to near-neutral-pH environment
- ed. J.R. Ellwood (Calgary, Canada: ASME)
- (2000) 2000 Int. Pipeline Conf , vol.2 , pp. 1005
- Wang, S.-H.¹ Chen, W.² King, F.³ Jack, T.R.⁴

15
- 0001222106
- (1999) Corrosion , vol.55 , pp. 297
- Zhang, X.-Y.¹ Lambert, S.B.² Sutherby, R.³ Plumtree, A.⁴

16
- 0000115387
- (1997) Corrosion , vol.53 , pp. 581
- Ahmed, T.M.¹ Lambert, S.B.² Sutherby, R.³ Plumtree, A.⁴

17
- 84994731748
- Mechanical factors affecting stress corrosion crack growth rates in buried pipelines
- ed. J.R. Ellwood (Calgary, Canada: ASME)
- (2000) 2000 Int. Pipeline Conf , vol.2 , pp. 961
- Lambert, S.B.¹ Beavers, J.A.² Dalanty, D.³ Sutherby R. Plumtree, A.⁴

18
- 0031622377
- The role of pressure and pressure fluctuations in the growth of SCC in linepipe steels
- Calgary, Canada: ASME
- (1998) Int. Pipeline Conf , vol.1 , pp. 409
- Wilmott, M.J.¹ Sutherby, R.L.²

19
- 84994745722
- Cracks during simulated hydrostatic testing
- ed. J.R. Ellwood (Calgary, Canada: ASME)
- (2000) 2000 Int. Pipeline Conf , vol.2 , pp. 743
- Brongers, M.P.H.¹ Beavers, J.A.² Jaske, C.E.³

20
- 0002267260
- Recent progress in the study of transgranular SCC in linepipe steels
- ed. T. Magnin (Nice, France: published for the European Federation of Corrosion by the Institute of Metals)
- (1996) Corrosion Deformation Interactions CDI '96 , pp. 282
- Zheng, W.¹ MacLeod, F.A.² Revie, R.W.³ Tyson, W.R.⁴ Shen, G.⁵ Kiff, D.⁶ Skaff, M.⁷ Wong, E.-W.⁸

21
- 84949522792
- Development of a predictive model for the initiation and early-stage growth of near-neutral-pH SCC of pipeline steels
- Paper no. 214 (Houston, TX: NACE)
- (2001) CORROSION/2001
- King, F.¹ Jack, T.R.² Chen, W.³ Wang, S.-H.⁴ Elboujdaini, M.⁵ Revie, W.⁶ Worthingham, R.⁷ Fessler, R.⁸ Dusek, P.⁹

22
- 0003726331
- Detailed characterization of SCC cracks from the Nordegg rupture site and their mechanistic implications
- Nova Research and Technology Corp. November
- (2000) Internal Report No. 01442
- King, F.¹ Given, R.² Chen, W.³

23
- 85040902117
- Dordrecht. The Netherlands: Kluwer Academic Publishers
- (1989) The Practical Use of Fracture Mechanics , pp. 282
- Droek, D.¹

24
- 0001381240
- New York. NY: Pergamon Press
- (1987) Stress Intensity Factors Handbook , vol.2 , pp. 863-867
- Murakami, Y.¹

25
- 84994711616
- Materials factors influencing the initiation of near-neutral-pH SCC on underground pipelines
- Calgary, Canada: ASME
- (2000) Int. Pipeline Conf , vol.2 , pp. 979
- Beavers, J.A.¹ Johnson, J.T.² Sutherby, R.L.³

26
- 0003304714
- SCC of pipeline steels in simulated groundwater: From mechanisms to a ranking test
- held Sept. 10-14 (London, U.K.: published for the European Federation of Corrosion by the Institute of Metals)
- (2000) EuroCorr 2000
- Le Friant, D.¹ Gayle, B.² Adam, C.³ Magnin, Th.⁴

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.