Soluble polyphenylene homopolymers with controllable microstructure and properties: Optical and electrical characteristics of completely dehydrogenated poly(1,3-cyclohexadiene) as a π-conjugated polymer semiconductor

Polymer

Volumn 47, Issue 20, 2006, Pages 7123-7130

  Natori, I ^a   Natori, S ^b   Sato, H ^a  

^a TOKYO UNIVERSITY OF AGRICULTURE AND TECHNOLOGY   (Japan)

^b SEIKEI UNIVERSITY   (Japan)

Author keywords

Microstructure and properties; Poly(1,3 cyclohexadiene); Soluble polyphenylene

Indexed keywords

CURRENT VOLTAGE CHARACTERISTICS; ENERGY GAP; HOMOPOLYMERIZATION; MICROSTRUCTURE; OPTICAL PROPERTIES; SEMICONDUCTING POLYMERS;

CONJUGATED POLYMER SEMICONDUCTORS; HOMOPOLYMERS; MOLAR RATIOS; SOLUBLE POLYPHENYLENE;

POLYPROPYLENES;

ELECTRICAL PROPERTY; HOMOPOLYMER; MICROSTRUCTURAL PROPERTY; OPTICAL PROPERTY; POLYPHENYLENE; SOLUBILITY; TOUGHNESS;

EID: 33748583172     PISSN: 00323861     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.polymer.2006.07.069     Document Type: Article

References (35)

1. Kovacic P., and Jones M.B. Chem Rev 87 (1987) 357-379
2. Ivory D.M., Miller G.G., Sowa J.M., Shacklette L.W., Chance R.R., and Baughman R.H. J Chem Phys 71 (1979) 1506-1507
3. Grem G., Leditzky G., Ullrich B., and Leising G. Adv Mater 4 (1992) 36-37
4. Grem G., Leditzky G., Ullrich B., and Leising G. Synth Met 51 (1992) 383-389
5. Grem G., and Leising G. Synth Met 57 (1993) 4105-4110
6. Ried W., and Freitag D. Angew Chem Int Ed Engl 7 (1968) 835-844
7. Edwards A., Blumstengal S., Sokolik I., Dorsinville R., Yun H., Kwei T.K., et al. Appl Phys Lett 70 (1997) 298-300
8. Biyao W., and Yamamoto T. J Appl Polym Sci 89 (2003) 2210-2215
9. Marvel C.S., and Hartzell G.E. J Am Chem Soc 81 (1959) 448-452
10. Frey D.A., Hasegawa M., and Marvel C.S. J Polym Sci Part A Polym Chem 1 (1963) 2057-2065
11. Lefebver G., and Dawans F. J Polym Sci Part A Polym Chem 2 (1964) 3277-3295
12. Zhong X.F., and François B. Makromol Chem Rapid Commun 9 (1988) 411-416
13. Zhong X.F., and François B. Synth Met 29 (1989) 35-40
14. Zhong X.F., and François B. Synth Met 41-43 (1991) 955-958
15. Zhong X.F., and François B. Makromol Chem 192 (1991) 2277-2291
16. François B., Widawski G., Rawiso M., and Cesar B. Synth Met 69 (1995) 463-466
17. Si-Ahmed L., Nüesch F., Zuppiroli L., and François B. Macromol Chem Phys 99 (1998) 625-632
18. François B., Izzillo S., and Iratçabal P. Synth Met 102 (1999) 1211-1212
19. Mignard E., Tachon C., and François B. Synth Met 102 (1999) 1246-1247
20. Williamson D.T., Buchanan T.D., and Long T.E. Polym Prepr 43 2 (2002) 1201-1202
21. Mignard E., Hiorns R.C., and François B. Macromolecules 35 (2002) 6132-6141
22. Natori I., and Sato H. J Polym Sci Part A Polym Chem 44 (2006) 837-845
23. Cassidy P.E., and Marvel C.S. J Polym Sci Part A Polym Chem 3 (1965) 1533-1565
24. Mango L.A., and Lenz R.W. Makromol Chem 163 (1973) 13-36
25. François B., and Zhong X.F. Makromol Chem 191 (1990) 2743-2753
26. Natori I. Macromolecules 30 (1997) 3696-3697
27. Natori I., and Inoue S. Macromolecules 31 (1998) 982-987
28. Natori I., and Inoue S. Macromolecules 31 (1998) 4687-4694
29. Natori I., and Imaizumi K. Macromol Symp 157 (2000) 143-150
30. Natori I., Imaizumi K., Yamagishi H., and Kazunori M. J Polym Sci Part B Polym Phys 36 (1998) 1657-1668
31. Natori I., Natori S., and Sato H. Macromolecules 39 (2006) 3168-3174
32. Wu C.C., Strum J.C., Register R.A., Tian J., Dana E.P., and Thompson M.E. IEEE Trans Electron Devices 44 (1997) 1269-1281
33. Bao Z., Peng Z., Galvin M.E., and Chandross E.A. Chem Mater 10 (1998) 1201-1204
34. Meng H., Yu W., and Huang W. Macromolecules 32 (1999) 8841-8847
35. The solubility of PPH-1 for DMF was not so good [31]. Moreover, PPH-1 was too brittle to provide a good polymer film with enough thickness.