Crack opening displacements of Vickers indentation cracks

Engineering Fracture Mechanics

Volumn 72, Issue 5, 2005, Pages 647-659

  Fett, Theo ^a   Kounga Njiwa, A B ^b   Rodel J ^b  

^a KARLSRUHE INSTITUTE OF TECHNOLOGY   (Germany)

^b DARMSTADT UNIVERSITY OF TECHNOLOGY   (Germany)

Author keywords

Crack opening profile; Crack tip toughness; Residual stresses; Vickers crack

Indexed keywords

CHEMICAL OXYGEN DEMAND; CRACK INITIATION; TOUGHNESS;

R-CURVE BEHAVIORS; VICKERS INDENTATION CRACKS;

FRACTURE;

FRACTURE MECHANICS;

EID: 10644281282     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfracmech.2004.07.003     Document Type: Article

References (27)

1. J. Rödel J.F. Kelly B.R. Lawn In situ measurements of bridged crack interfaces in the scanning electron microscope J. Am. Ceram. Soc. 73 1990 3313-3318
2. T. Fett D. Munz J. Seidel M. Stech J. Rödel Correlation between long and short crack R-curves in alumina using the crack opening displacement and fracture mechanical weight function approach J. Am. Ceram. Soc. 79 1996 1189-1196
3. F. Meschke O. Raddatz A. Kolleck G.A. Schneider R-curve behaviour and crack-closure stresses in Barium Titanate and (Mg,Y)-PSZ ceramics J. Am. Ceram. Soc. 83 2000 353-361
4. G. Pezzotti N. Muraki N. Maeda K. Satou T. Nishida In situ measurement of bridging stresses in toughened silicon nitride using Raman microprobe spectroscopy J. Am. Ceram. Soc. 82 1999 1249-1256
5. J. Seidel J. Rödel Measurement of crack tip toughness in alumina as a function of grain size J. Am. Ceram. Soc. 80 1997 433-438
6. J.J. Kruzic Robert O. Ritchie Determining the toughness of ceramics from Vickers indentations using the crack-opening displacements: An experimental study J. Am. Ceram. Soc. 86 2003 1433-1436
7. Z. Burghard A. Zimmermann J. Rödel F. Aldinger B.R. Lawn Crack opening profiles in normal and anomalous glasses Acta Mater. 52 2004 293-297
8. Rödel J. Rissüberbrückung in keramischen Werkstoffen, VDI-Verlag, Reihe 5: Grund- und Werkstoffe, Nr. 331, Düsseldorf, 1993
9. Fett T. Computation of crack opening displacements for Vickers indentation cracks, Report FZKA 6757, Forschungszentrum Karlsruhe, Karlsruhe, 2002
10. T. Fett A.B. Kounga J. Rödel Stresses and stress intensity factor from COD of Vickers indentation cracks J. Mater. Sci. Lett. 39 2004 2219-2221
11. A.G. Evans E.A. Charles Fracture toughness determinations by indentation J. Am. Ceram. Soc. 59 1976 371-372
12. B.R. Lawn D.B. Marshall Hardness, toughness, and brittleness: An indentation analysis J. Am. Ceram. Soc. 62 1979 347-350
13. B.R. Lawn A.G. Evans A model for crack initiation in elastic/plastic indentation fields J. Mater. Sci. 12 1977 2195-2199
14. D.B. Marshall B.R. Lawn P. Chantikul Residual stress effects in sharp contact cracking. Part 2: Strength degradation J. Mater. Sci. 14 1979 2225-2235
15. B.R. Lawn A.G. Evans D.B. Marshall Elastic/plastic indentation damage in ceramics: The median/radial crack system J. Am. Ceram. Soc. 63 1980 574-581
16. J.G.P. Binner R. Stevens The measurement of toughness by indentation Brit. Ceram. 83 1984 168-172
17. G.R. Anstis P. Chantikul B.R. Lawn D.B. Marshall A critical evaluation of indentation techniques for measuring fracture toughness: I. Direct crack measurements J. Am. Ceram. Soc. 64 1981 533-538
18. D.B. Marshall B.R. Lawn P. Chantikul Residual stress effects in sharp contact cracking. Part 1: Indentation fracture mechanics J. Mater. Sci. 14 1979 2001-2012
19. S.E. Molis D.R. Clarke Measurement of stresses using fluorescence in an optical microprobe: Stresses around indentations in a chromium-doped sapphire J. Am. Ceram. Soc. 73 1990 3189-3194
20. C.P. Ostertag L.H. Robins L.P. Cook Catholuminescence measurements of strained alumina single crystals J. Euro. Ceram. Soc. 7 1991 109-116
21. S. Lathabai J. Rödel T. Dabbs B.R. Lawn Fracture mechanics model for subthreshold indentation flaws. Part I: Equilibrium fracture J. Mater. Sci. 26 1991 2157-2168
22. S. Lathabai J. Rödel T. Dabbs B.R. Lawn Fracture mechanics model for subthreshold indentation flaws. Part II: Non-equilibrium fracture J. Mater. Sci. 26 1991 2313-2321
23. R. Hill Mathematical theory of plasticity 1950 Oxford University Press Oxford
24. S.S. Chiang D.B. Marshall A.G. Evans The response of solids to elastic/plastic indentation. II. Crack initiation J. Appl. Phys. 53 1982 312-317
25. V.M. Sglavo D.J. Green Influence of indentation crack configuration on strength and fatigue behaviour of soda-lime silicate glass Acta Metall. Mater. 43 3 1995 965-972
26. W. Gröbner N. Hofreiter Integraltafeln I 1975 Springer Verlag Heidelberg
27. C. Kocer R.E. Collins Measurement of very slow crack growth in glass J. Am. Ceram. Soc. 84 2001 2585-2593