Measurement of the fatigue crack propagation threshold of fretting induced cracks in Ti-6Al-4V

International Journal of Fatigue

Volumn 26, Issue 3, 2004, Pages 281-288

  Golden, P J ^a   Bartha, B B ^a   Grandt Jr, A F ^b   Nicholas, T ^a  

^a AIR FORCE RESEARCH LABORATORY   (United States)

^b Purdue University   (United States)

Author keywords

Fatigue; Fretting; Threshold; Ti 6Al 4V

Indexed keywords

CRACK PROPAGATION; LOADS (FORCES); SCANNING ELECTRON MICROSCOPY; STRESS ANALYSIS; STRESS RELIEF; TITANIUM ALLOYS;

FRETTING CRACKS; HEAT TINTING; THRESHOLD STRESSES;

FATIGUE TESTING;

EID: 0344513105     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(03)00166-X     Document Type: Article

References (18)

1. Johnson K.L. Contact mechanics. 1985;Cambridge University Press, Cambridge.
2. Hills D.A., Nowell D. Mechanics of fretting fatigue. 1994;Kluwer, Dordrecht.
3. Farris T.N., Szolwinski M.P., Harish G. Fretting in aerospace structures and materials. Hoeppner D.W., Chandrasekaran V., Elliott C.B. Fretting fatigue: current technologies and practices, ASTM STP 1367. 1999;267-281 American Society for Testing and Materials, Philadelphia, PA.
4. Nicholas T. Critical issues in high cycle fatigue. Int J Fatigue. 21:1999;S221-S231.
5. Szolwinski M.P., Farris T.N. Observation, analysis and prediction of fretting fatigue in 2024-T351 aluminum alloy. Wear. 221:1998;24-36.
6. Murthy H, Rajeev PT, Farris TN, Slavik DC. Fretting fatigue of Ti-6Al-4V subjected to blade/disk contact loading. In: Developments in Fracture Mechanics for the New Century, 50th Anniversary of Japan Society of Materials Science, Osaka, Japan, 2001. p. 41-8.
7. McVeigh P.A., Harish G., Farris T.N., Szolwinski M.P. Modeling interfacial conditions in nominally flat contacts for application to fretting fatigue of turbine engine components. Int J Fatigue. 21:1999;S157-S165.
8. Golden PJ. High cycle fatigue of fretting induced cracks. Ph.D. thesis, Purdue University, 2001.
9. Shen G., Glinka G. Weight functions for a surface semi-elliptical crack in a finite thickness plate. Theor Appl Fract Mech. 15:1991;247-255.
10. Standard test method for measurement of fatigue crack growth rates, annual book of ASTM standards, E 647-95, 1998. p. 562-98.
11. Maxwell D.C., Nicholas T. A rapid method for generation of a haigh diagram for high cycle fatigue. Panontin T.L., Sheppard S.D. Fatigue and fracture mechanics: 29th volume, ASTM STP 1321. 1999;626-641 American Society for Testing and Materials, West Conshohocken, PA.
12. Nicholas T. Step loading, coaxing and small crack thresholds in Ti-6Al-4V under high cycle fatigue. Chan K.S., Liaw P.K., Bellows R.S., Zogas T.C., Soboyejo W.O. Fatigue - David L Davidson Symposium. 2002;91-106 TMS (The Minerals, Metals & Materials Society), Cleveland, OH.
13. Moshier M.A., Hillberry B.M., Nicholas T. The effect of low-cycle fatigue cracks and loading history on the high cycle fatigue threshold. Halford G.R., Gallagher J.P. Fatigue and fracture mechanics: 31st volume, ASTM STP 1389. 2000;427-444 American Society for Testing and Materials, West Conshohocken, PA.
14. Garcia DB. Fractographic analysis of fatigue failures with fretting induced damage. Masters thesis, Purdue University, 2002.
15. Garcia DB, Grandt Jr AF. Fractographic characteristics associated with fretting cracks in turbomachinery alloys. 44th AIAA/ASME/ASCE/AHS Structures, Structural Dynamics, and Materials Conference, 2003, Proceedings CD.
16. Moshier M.A., Nicholas T., Hillberry B.M. High cycle fatigue threshold in the presence of naturally initiated small surface cracks. Reuter W.G., Piascik R.S. Fatigue and fracture mechanics: 33rd volume, ASTM STP 1417. 2002;129-146 American Society for Testing and Materials, West Conshohocken, PA.
17. El Haddad M.H., Smith K.N., Topper T.H. Fatigue crack propagation of short cracks. ASME J Eng Mater Tech. 101:1979;42-46.
18. Hartman GA. Infrared damage detection system (IDDS) for real-time, small-scale damage monitoring. In: Proc. SEM Ann. Conf. on Exptl Mech., Charlotte, North Carolina 2003, in press.