Double cantilever beam testing of multidirectional laminates

Author keywords

A. Laminates; A. Polymer matrix composites (PMCs); B. Delamination; B. Fracture toughness

Indexed keywords

CANTILEVER BEAMS; DELAMINATION; FINITE ELEMENT METHOD; FRACTURE TOUGHNESS; RESIDUAL STRESSES; STRAIN;

EID: 0242335641     PISSN: 1359835X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compositesa.2003.08.008     Document Type: Article
Times cited : (54)

References (21)
  • 1
    • 0032194941 scopus 로고    scopus 로고
    • Standard test methods for delamination resistance of composite materials: Current status
    • Davies P., Blackman B.R.K., Brunner A.J. Standard test methods for delamination resistance of composite materials: current status. Appl Compos Mater. 5:1998;345-364.
    • (1998) Appl Compos Mater , vol.5 , pp. 345-364
    • Davies, P.1    Blackman, B.R.K.2    Brunner, A.J.3
  • 3
    • 0020300644 scopus 로고
    • Factors affecting the interlaminar fracture energy of graphite/epoxy laminates
    • Tokyo
    • Russell A.J., Street K.N. Factors affecting the interlaminar fracture energy of graphite/epoxy laminates. Proc ICCM IV, Tokyo. 1982;279-286.
    • (1982) Proc ICCM IV , pp. 279-286
    • Russell, A.J.1    Street, K.N.2
  • 4
  • 5
    • 0021505859 scopus 로고
    • The characterization of mode I delamination failure in non-woven multidirectional laminates
    • Chai H. The characterization of mode I delamination failure in non-woven multidirectional laminates. Composites. 15:1984;277-290.
    • (1984) Composites , vol.15 , pp. 277-290
    • Chai, H.1
  • 6
    • 0008797907 scopus 로고
    • Delamination analysis of composites with distributed damage using a J integral
    • Beijing
    • Schapery R.A., Goetz D.P., Jordan W.M. Delamination analysis of composites with distributed damage using a J integral. Proc Int Symp Compos Mater Struct, Beijing. 1986;543-549.
    • (1986) Proc Int Symp Compos Mater Struct , pp. 543-549
    • Schapery, R.A.1    Goetz, D.P.2    Jordan, W.M.3
  • 8
    • 0026626271 scopus 로고
    • A modified DCB specimen for mode I testing of multidirectional laminates
    • Robinson P., Song D.Q. A modified DCB specimen for mode I testing of multidirectional laminates. J Compos Mater. 26:1992;1554-1577.
    • (1992) J Compos Mater , vol.26 , pp. 1554-1577
    • Robinson, P.1    Song, D.Q.2
  • 9
    • 0032629812 scopus 로고    scopus 로고
    • Delamination fracture of multidirectional carbon-fibre/epoxy composites under mode I, mode II and mixed-mode I/II loading
    • Choi N.S., Kinloch A.J., Williams J.G. Delamination fracture of multidirectional carbon-fibre/epoxy composites under mode I, mode II and mixed-mode I/II loading. J Compos Mater. 33:1999;73-100.
    • (1999) J Compos Mater , vol.33 , pp. 73-100
    • Choi, N.S.1    Kinloch, A.J.2    Williams, J.G.3
  • 10
    • 0033906781 scopus 로고    scopus 로고
    • Initiation and bifurcation mechanisms of cracks in multidirectional laminates
    • Benyahia A.A., Benzeggagh M.L., Gong X.L. Initiation and bifurcation mechanisms of cracks in multidirectional laminates. Compos Sci Technol. 60:2000;597-604.
    • (2000) Compos Sci Technol , vol.60 , pp. 597-604
    • Benyahia, A.A.1    Benzeggagh, M.L.2    Gong, X.L.3
  • 11
    • 0033901143 scopus 로고    scopus 로고
    • Mode I fracture resistance characteristics of graphite/epoxy laminated composites
    • Rhee K.Y., Koh S.K., Lee J.H. Mode I fracture resistance characteristics of graphite/epoxy laminated composites. Polym Compos. 21:2000;155-164.
    • (2000) Polym Compos , vol.21 , pp. 155-164
    • Rhee, K.Y.1    Koh, S.K.2    Lee, J.H.3
  • 12
  • 13
    • 84970692230 scopus 로고
    • An analytical investigation of delamination front curvature in double cantilever beam specimens
    • Davidson B.D. An analytical investigation of delamination front curvature in double cantilever beam specimens. J Compos Mater. 24:1990;1124-1137.
    • (1990) J Compos Mater , vol.24 , pp. 1124-1137
    • Davidson, B.D.1
  • 14
    • 0030286964 scopus 로고    scopus 로고
    • Effect of stacking sequence on energy release rate distributions in multidirectional DCB and ENF specimens
    • Davidson B.D., Krüger R., König M. Effect of stacking sequence on energy release rate distributions in multidirectional DCB and ENF specimens. Engng Fract Mech. 55:1996;557-569.
    • (1996) Engng Fract Mech , vol.55 , pp. 557-569
    • Davidson, B.D.1    Krüger, R.2    König, M.3
  • 15
    • 0033899229 scopus 로고    scopus 로고
    • Energy release rate analysis for adhesive and laminate double cantilever beam specimens emphasizing the effect of residual stresses
    • Nairn J.A. Energy release rate analysis for adhesive and laminate double cantilever beam specimens emphasizing the effect of residual stresses. Int J Adhes Adhes. 20:2000;59-70.
    • (2000) Int J Adhes Adhes , vol.20 , pp. 59-70
    • Nairn, J.A.1
  • 17
    • 0023847596 scopus 로고
    • Convergence of strain energy release rate components for edge-delaminated composite laminates
    • Raju I.S., Crews J.H., Aminpour M.A. Convergence of strain energy release rate components for edge-delaminated composite laminates. Engng Fract Mech. 30:1988;383-396.
    • (1988) Engng Fract Mech , vol.30 , pp. 383-396
    • Raju, I.S.1    Crews, J.H.2    Aminpour, M.A.3
  • 18
    • 0031152267 scopus 로고    scopus 로고
    • Calculation of stress intensity factors for interlaminar cracks in composite laminates
    • Qian W., Sun C.T. Calculation of stress intensity factors for interlaminar cracks in composite laminates. Compos Sci Technol. 57:1997;637-650.
    • (1997) Compos Sci Technol , vol.57 , pp. 637-650
    • Qian, W.1    Sun, C.T.2
  • 19
    • 0032280622 scopus 로고    scopus 로고
    • Designation of mode mix in orthotropic composite delamination problems
    • Narayan S.H., Beuth J.L. Designation of mode mix in orthotropic composite delamination problems. Int J Fract. 90:1998;383-400.
    • (1998) Int J Fract , vol.90 , pp. 383-400
    • Narayan, S.H.1    Beuth, J.L.2
  • 20
    • 0030658440 scopus 로고    scopus 로고
    • Stress intensity factors as the fracture parameters for delamination crack growth in composite laminates
    • Chow W.T., Atluri S.N. Stress intensity factors as the fracture parameters for delamination crack growth in composite laminates. Composites. 28B:1997;375-384.
    • (1997) Composites , vol.28 B , pp. 375-384
    • Chow, W.T.1    Atluri, S.N.2
  • 21
    • 0028992545 scopus 로고
    • Finite element modelling of delamination growth in the DCB and edge delaminated DCB specimens
    • Robinson P., Javidrad F., Hitchings D. Finite element modelling of delamination growth in the DCB and edge delaminated DCB specimens. Compos Struct. 32:1995;275-285.
    • (1995) Compos Struct , vol.32 , pp. 275-285
    • Robinson, P.1    Javidrad, F.2    Hitchings, D.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.